Efficient-spraying type dry-mixing and wet-mixing mortar plasticizer composition as well as preparation method and application method thereof

A technology of plasticizer and composition, which is applied in the field of high-efficiency spray dry-wet mortar plasticizer composition, can solve problems such as poor working conditions at the construction site, unfavorable civilized construction, and affecting project quality, and achieve good waterproof and air permeability, Improve workability and water retention, good effect of mortar water retention

Inactive Publication Date: 2017-03-22
四川巨星新型材料有限公司
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the unstable quality of lime, common quality defects such as low strength, easy cracking and hollowing, and uneven thickness of the prepared mortar generally exist, which affect the quality of the project. Serious pollution, not conducive to civilized construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient-spraying type dry-mixing and wet-mixing mortar plasticizer composition as well as preparation method and application method thereof
  • Efficient-spraying type dry-mixing and wet-mixing mortar plasticizer composition as well as preparation method and application method thereof
  • Efficient-spraying type dry-mixing and wet-mixing mortar plasticizer composition as well as preparation method and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Take the preparation of 1000kg product as an example

[0040] Prepare a high-efficiency spray dry-wet mixed mortar plasticizer composition, and its proportion is calculated by weight, and 30 kg of sodium lauryl sulfate, 250 kg of methyl cellulose, 380 kg of sodium gluconate, and 150 kg of polypropylene fiber are successively put into the mixing tank , 50kg of polyacrylamide, 100kg of active calcium formate, and 40kg of polyvinyl alcohol rubber powder are added while stirring for 1 hour to make the mixture even, then stop the machine and pack into bags to obtain a powder product.

[0041]In addition, after the mixture is uniform, take 150kg of powder product, add 850kg of water, and fully stir for 1.5 hours at room temperature to obtain a liquid product.

Embodiment 2

[0043] Take the preparation of 1000kg product as an example

[0044] Prepare high-efficiency spray dry-wet mixed mortar plasticizer composition, its proportioning is by weight, drop into ethoxylated alkyl sulfate sodium 20kg, methyl cellulose 250kg, sodium hexametaphosphate 400kg, poly Add 150kg of acrylic fiber, 50kg of sodium polyacrylate, 100kg of sodium thiosulfate, and 30kg of acrylamide rubber powder, and stir for 1 hour to make the mixture even, then stop the machine and pack it into bags to obtain a powder product.

[0045] In addition, after the mixture is uniform, take 150kg of powder product, add 850kg of water, and fully stir for 1.5 hours at room temperature to obtain a liquid product.

Embodiment 3

[0047] Take the preparation of 1000kg product as an example

[0048] Prepare high-efficiency spray dry-wet mixed mortar plasticizer composition, its proportion is by weight, in the mixing tank, drop into successively 40kg of anionic fluorocarbon surfactant, 250kg of hydroxypropyl methylcellulose, 370kg of sodium tripolyphosphate, Calcium sulfoaluminate expansion agent 150kg, potassium polyacrylate 50kg, sodium chloride 100kg, polymer resin rubber powder 40kg, while adding, stir for 1 hour, make it evenly mixed, stop the machine, pack into bags, and then the powder product is obtained.

[0049] In addition, after the mixture is uniform, take 150kg of powder product, add 850kg of water, and fully stir for 1.5 hours at room temperature to obtain a liquid product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an efficient-spraying type dry-mixing and wet-mixing mortar plasticizer composition as well as a preparation method and an application method thereof. The composition comprises the following components in percentage by weight (100% in total): 1%-5% of a plasticizer, 15%-30% of a thickening agent, 30%-50% of a retarder, 10%-25% of an anti-cracking agent, 1-5% of a water-retaining agent, 5%-10% of an enhancer, and 1%-5% of a binding agent. By utilizing the composition, the workability, water-retaining property, adhesive property and cracking resistance of coating mortar can be remarkably improved, the cracking, hollowing and falling of the mortar are avoided, and various performance indexes such as the strength and permeability resistance of the mortar can be improved; and furthermore, cement can be saved, and the disadvantages of easiness in ash blasting, high shrinkage, low strength and the like of the cement mixed mortar are overcome.

Description

technical field [0001] The invention relates to a high-efficiency spray dry-wet mixing mortar plasticizer composition and a preparation method and an application method thereof. Background technique [0002] Construction mortar is used in a large amount in construction engineering and has a wide range of uses. It is a building material second only to concrete in modern engineering construction. Plastering mortar refers to the mortar that is applied on the surface of buildings or building components, and one or more layers of mortar are applied on the walls, ceilings, and ground planes with a specified thickness, and the final properties are obtained after hardening. The plastering mortar is required to have good workability, easy to spread into a uniform and flat layer, easy to construct, and have high adhesive force. The mortar layer should be firmly bonded to the bottom surface, and it will not crack or crack after long-term use. In general, it should also have the perfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/38
CPCC04B40/0039C04B2103/10C04B2103/465C04B2103/65
Inventor 苏笮斌李立君王世玉
Owner 四川巨星新型材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com