Environment-friendly compound material prepared from waste plastics and application thereof

A technology for waste plastics and composite materials, applied in the direction of additive processing, etc., to achieve the effect of broadening the selection range, low price and wide source

Inactive Publication Date: 2017-05-31
广西丰达三维科技有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides an environmentally friendly composite material made o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0049] The preparation method of the environmentally friendly composite material made of waste plastics comprises the following steps:

[0050] S1: Wash and dry the waste plastics until the water content is ≤0.8%, then mix and pulverize the dried plastics and EPDM grafted with maleic anhydride, and pass through a 200-300 mesh sieve to obtain plastic powder;

[0051] S2: adding a surfactant to the plastic powder prepared in step S1, and activating it for 1.2-1.8 hours at a temperature of 70-74° C. and a rotation speed of 150-180 r / min to obtain an activated plastic powder;

[0052] S3: Under nitrogen protection, add polylactic acid, sodium tripolyphosphate, 2-hydroxy-4-octyloxybenzobutanone, butenyl bisstearamide, ethylene glycol to the activated plastic powder prepared in step S2 Alcohol monostearate, tributoxyethyl phosphate, tris(2,4-di-tert-butylphenyl) phosphite, regulator, generating agent, crosslinking agent, compatibilizer, bridging agent, Catalyst, plasticizer, dispersa...

Embodiment 1

[0064] An environment-friendly composite material made of waste plastics, including the following raw materials in parts by weight: 90 parts of waste plastics, 60 parts of maleic anhydride grafted EPDM rubber, 45 parts of polylactic acid, and 26 parts of sodium tripolyphosphate Parts, 22 parts of 2-hydroxy-4-octyloxybenzobutanone, 26 parts of butenyl bisstearamide, 13 parts of ethylene glycol monostearate, 18 parts of tributoxyethyl phosphate, three 15 parts of (2,4-di-tert-butylphenyl) phosphite, 1.5 parts of surfactant, 0.8 parts of regulator, 0.5 parts of generator, 0.6 parts of crosslinking agent, 1 part of compatibilizer, and 1 part of bridging agent 0.5 parts of catalyst, 0.6 parts of plasticizer, 0.4 parts of dispersant, 0.5 parts of tackifier, 1.8 parts of curing agent, 0.4 parts of antioxidant, 0.3 parts of stabilizer, 1.5 parts of anti-aging agent, 1.8 parts of flame retardant , 3 parts of smoke suppressant;

[0065] The surfactant is polyoxyethylene-polyoxypropylen...

Embodiment 2

[0095] An environment-friendly composite material made of waste plastics, including the following raw materials in parts by weight: 62 parts of waste plastics, 35 parts of maleic anhydride grafted EPDM rubber, 36 parts of polylactic acid, and 22 parts of sodium tripolyphosphate Parts, 20 parts of 2-hydroxy-4-octyloxybenzobutanone, 20 parts of butenyl bisstearamide, 11 parts of ethylene glycol monostearate, 16 parts of tributoxyethyl phosphate, three 12 parts of (2,4-di-tert-butylphenyl) phosphite, 1.3 parts of surfactant, 0.6 parts of regulator, 0.4 parts of generating agent, 0.4 parts of crosslinking agent, 0.6 parts of compatibilizer, and 0.6 parts of bridging agent 0.3 parts of catalyst, 0.4 parts of plasticizer, 0.3 parts of dispersant, 0.3 parts of tackifier, 1.2 parts of curing agent, 0.0 parts of antioxidant, 0.2 parts of stabilizer, 1 part of anti-aging agent, 1.5 parts of flame retardant 2 parts, 2 parts of smoke suppressant;

[0096] The surfactant is polyoxyethylen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly compound material prepared from waste plastics and application thereof. The environment-friendly compound material prepared from the waste plastics comprises the following raw materials: waste plastics, maleic anhydride grafted ethylene propylene terpolymer, polylactic acid, sodium tripolyphosphate, 2-hydroxy-4-zinc-oxo-diphenyl butanone, butenyl stearamide, glycol monostearate, phosphoric tri-butoxy ethyl ester, tri(2,4-tertiary butyl phenyl) phosphite ester, a surface active agent, a modifier, a generating agent, a cross-linking agent, a compatilizer, a bridging agent, a catalyst, a plasticizer, a dispersing agent, a tackifier, a curing agent, an antioxidant, a stabilizer, an anti-aging agent, a fire retardant and a smoke suppressor. The environment-friendly compound material prepared from the waste plastics is prepared according to the steps of cleaning, drying, crushing, activating, mixing, extruding and the like. The abrasive resistance and the tensile strength of the environment-friendly compound material prepared from the waste plastics provided by the invention are obviously better than those of a plastic material in the prior art.

Description

[0001] 【Technical field】 [0002] The invention belongs to the technical field of material preparation for 3D printing, and in particular relates to an environmentally friendly composite material made of waste plastics and its application. [0003] 【Background technique】 [0004] 3D printing, also known as rapid prototyping technology, is also called additive manufacturing technology. It does not require traditional tools, fixtures and machine tools, but is based on digital model files, using adhesive materials such as metal powder or plastic Layer printing technology to manufacture objects of any shape. 3D printers can manufacture many items, such as airplanes, pistols, food, human organs, children's toys, etc. 3D printing technology is a major breakthrough in the world's manufacturing technology field in the past 20 years. It is the integration of multidisciplinary technologies such as mechanical engineering, computer technology, numerical control technology, and material s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L101/00C08L51/04C08L67/04C08L33/04C08K13/06C08K3/32C08K5/07C08K5/11C08K3/22C08J3/28B33Y70/00
CPCC08L101/00B33Y70/00C08J3/28C08J2300/00C08J2433/04C08J2451/04C08J2467/04C08L2201/02C08L2205/035C08L51/04C08L67/04C08L33/04C08K13/06C08K2003/324C08K5/07C08K5/11C08K2003/2227
Inventor 冯可发
Owner 广西丰达三维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap