Catalyst for C5 petroleum resin hydrogenation and preparation method thereof

A C5 petroleum resin and catalyst technology, applied in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., can solve the problems of low activity, poor activity stability, poor resistance to impurities, etc., and achieve a large ratio Surface area, reduced olefin polymerization, low carbon deposition rate

Inactive Publication Date: 2017-06-20
QINZHOU UNIV
View PDF10 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The existing catalysts for the hydrogenation of C5 petroleum resins have the problems of low activity of nickel-based hydrogenation catalysts, poor resistance to impurities, and poor activity stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for C5 petroleum resin hydrogenation and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Dissolve 1.2kg of zinc nitrate in 6L of water to make a solution containing zinc, and dissolve 0.24kg of sodium metaaluminate and 0.30kg of sodium carbonate in 4L of water to make a solution containing aluminum. Divide the zinc-containing solution into 3 equal parts, each 2L. Take 2L of zinc-containing solution, keep the temperature at 80°C, add aluminum-containing mixed solution dropwise to it until the pH value reaches 9.0; stop dropping the aluminum-containing mixed solution, then add 2L of zinc-containing solution dropwise to the mixing system, and continue to drop aluminum-containing solution Mix the solution until the pH value reaches 9.0; titrate the aluminum-containing mixed solution and the zinc-containing solution alternately until all the zinc-containing solutions are added, and add the aluminum-containing mixed solution dropwise until the pH reaches 9.0. The total titration time is 3 hours. The obtained mixture was aged at 80°C for 4h, cooled and washed unti...

Embodiment 2

[0038] The preparation method and steps of the composite carrier containing zinc oxide-alumina are the same as in Example 1, and the zinc oxide containing zinc-aluminum spinel is prepared, and the pH value is adjusted to 8.7. In terms of oxides, the content of zinc oxide is 70%; the specific surface area is 191m 2 / g.

[0039] The composite carrier includes 32wt% of zinc oxide containing zinc-aluminum spinel, 67wt% of alumina, and the contents of phosphorus, potassium and magnesium in the auxiliary components are P 2 o 5 0.6wt%, K 2 O 1.0 wt%, MgO 1.0 wt%. Composite carrier specific surface area 279m 2 / g.

[0040] The difference is that after the composite carrier is obtained, the composite carrier containing zinc oxide-alumina is modified by using potassium and magnesium. , magnesium nitrate, completely dissolved in 30ml of distilled water, and then diluted with deionized water to prepare a solution and spray the composite carrier of zinc oxide-alumina, so that the co...

Embodiment 3

[0043] The preparation method and steps of the composite carrier containing zinc oxide-alumina are the same as in Example 1. Zinc oxide containing zinc aluminum spinel was prepared, and the pH value was adjusted to 9.3. Zinc oxide containing zinc aluminum spinel, calculated as oxide, the content of zinc oxide is 63%; the specific surface area is 214m 2 / g.

[0044] The composite carrier includes 18.3wt% of zinc oxide containing zinc-aluminum spinel, 79wt% of alumina, and the contents of phosphorus, potassium and magnesium in the auxiliary components are P 2 o 5 0.9wt%, K 2 O 2.0wt%, MgO 1.6wt%. Composite carrier specific surface area 242m 2 / g.

[0045] Get palladium chloride, nickel phosphide and lanthanum nitrate and join in 30ml of distilled water, add ammonia water to adjust the pH value at 3.0, then dilute with deionized water, make a solution and impregnate 100g of spherical composite carriers containing zinc oxide-alumina, specifically The steps are the same as ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a catalyst for C5 petroleum resin hydrogenation and a preparation method thereof. The catalyst comprises the following components by mass: 78.0-96.0wt% of a composite carrier containing zinc oxide-alumina, 1.0-8.0wt% of an active component, 1.0-15.0wt% of nickel phosphide, and 0.1-2.5wt% of lanthanum oxide. C5 petroleum resin has high hydrogenation activity and good activity stability, the catalyst active center loss rate is low, and the operation period is long.

Description

technical field [0001] The invention belongs to the technical field of hydrogenation catalysts, in particular to a catalyst and preparation method for hydrogenation of C5 petroleum resins, more specifically a C5 petroleum resin with zinc oxide-alumina composite material as a carrier Hydrogenation catalyst and preparation method. Background technique [0002] Thermoplastic resins produced by polymerization of C5 and C9 fractions in ethylene cracking by-products can generally be divided into: aliphatic hydrocarbon resins (C5), aliphatic hydrocarbon-aromatic resins (C5 / C9), aromatic hydrocarbon resins (C9) and dicyclopentadiene resins Diene resin (DCPD). Because petroleum resin has good water resistance, acid and alkali resistance, weather resistance and light aging resistance, it is widely used in the fields of paint, coating, adhesive and rubber. At present, domestic petroleum resin is affected by the composition of raw materials, and its products are generally light yellow...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/185B01J35/10
CPCB01J27/1856B01J35/615
Inventor 晁会霞尹继蕊张海燕
Owner QINZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com