A kind of ND-sensitized environment-friendly germanium tellurate luminescent glass and preparation method thereof

A luminescent glass, environmentally friendly technology, applied in the field of material science, can solve problems such as unavailability and no absorption band, and achieve the effects of improved thermal properties, easy pouring, and lower melting temperature

Active Publication Date: 2019-10-25
CHINA JILIANG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some rare earth luminescent ions such as Ho, Dy and Pr have no obvious absorption band near 808nm, and cannot be pumped by common 808nm semiconductor lasers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ND-sensitized environment-friendly germanium tellurate luminescent glass and preparation method thereof
  • A kind of ND-sensitized environment-friendly germanium tellurate luminescent glass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: a kind of traditional germanate glass

[0028] A kind of traditional germanate glass, raw material composition is as shown in 1# in table 1;

[0029] Concrete preparation process is as follows:

[0030] According to the mass percent of 1# glass composition in Table 1, calculate the corresponding weight of each composition, and take by weighing each raw material component;

[0031] Pour the uniformly mixed raw materials into a platinum crucible, and move it into a constant temperature and humidity furnace with a relative humidity of less than 2%. First, heat up to 500°C at a rate of 10°C / min, and then continue to heat up at a rate of 5°C / min. to 1000°C, during which they were respectively kept at 800°C, 900°C, and 1000°C for 20 minutes respectively, and then melted in a silicon carbide rod electric furnace at 1400°C for 20 minutes. Inject high-purity oxygen with a purity greater than 99.95%, homogenize and clarify to obtain a uniform glass liquid without ...

Embodiment 2

[0036] Embodiment 2: a kind of traditional germanium tellurite glass

[0037] A kind of traditional germanate glass, raw material composition is as shown in 2# in table 1;

[0038] Concrete preparation process is as follows:

[0039] According to the mass percentage that 2# glass forms among the table 1, calculate the corresponding weight of each composition, and take each raw material component;

[0040]Pour the raw materials into a platinum crucible and move it into a constant temperature and humidity furnace with a relative humidity of less than 2%. First, heat up to 500°C at a rate of 10°C / min, and then continue to heat up to 1000°C at a rate of 5°C / min. During the period, they were respectively kept at 800°C, 900°C, and 1000°C for 20 minutes respectively, and then melted in a silicon carbide rod electric furnace at 1300°C for 20 minutes. 99.95% high-purity oxygen, homogenized and clarified to obtain a uniform glass liquid without bubbles; pour the glass liquid into a pr...

Embodiment 3

[0046] Embodiment 3: a kind of environment-friendly germanium tellurate glass

[0047] An environment-friendly germanium tellurate glass, the raw material composition is as shown in 3# in Table 1;

[0048] Concrete preparation process is as follows:

[0049] Mo-V-Te-Nb-O catalyst uses ammonium molybdate, ammonium metavanadate, telluric acid and niobium oxalate as raw materials, and the molar ratio of its active components is Mo:V:Te:Nb=1:0.3: 0.23:0.12. The raw materials were weighed according to the molar ratio of the active components, and the niobium oxalate was configured into an 8mg / mL aqueous solution for use. The volume is 110 times of the total mass of ammonium molybdate, ammonium metavanadate, and telluric acid. Rotate and heat to 80°C to completely dissolve it, and obtain a clear and transparent orange-yellow solution. After 0.5 hours, lower the temperature to 30°C, add niobium oxalate solution, and the solution gradually becomes cloudy. After rotating for 2 hour...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Vickers hardnessaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of material science and in particular relates to Nd-sensitized environmental-friendly germanium tellurite luminescent glass and a preparation method thereof. The glass is prepared from the following raw material components: GeO2, Mo-V-Te-Nb-O catalyst waste, Na2O, BaF2, NdF3 or Nd2O3, and MF3 or M2O3, wherein M refers to a rare earth luminescent ion. The tellurium oxide is replaced with the Mo-V-Te-Nb-O catalyst waste, and the problem that the mechanical property of germanium tellurite is reduced by tellurium oxide can be effectively improved when the melting temperature is reduced, so that the obtained rare-earth doped environmental-friendly germanium tellurite glass can obtain good visible, near-infrared and mid-infrared fluorescence under laser diode pumping with the wavelength of 808nm. Meanwhile, the physical and chemical properties are excellent, the thermal stability is high, the parameter Delta T is more than or equal to 170 DEG C, and the Vickers hardness of the glass is more than 680 kgf / mm<2>.

Description

Technical field: [0001] The invention belongs to the technical field of material science, and in particular relates to an Nd-sensitized environment-friendly germanium tellurate luminescent glass and a preparation method thereof. Background technique: [0002] Germanate glass has good thermal stability and chemical durability, and has the advantages of wide fluorescent linewidth, high solubility of rare earth ions, wide infrared transmission range (6 μm), and good glass-forming performance. However, its forming temperature is high, and a large amount of germanium oxide precious metal raw materials is used, which greatly increases the production cost and limits its commercialization process. Adding an appropriate amount of tellurium oxide compound to the germanate glass system can reduce the phonon energy and melting temperature of the germanate glass matrix, while retaining the good mid-infrared luminescence characteristics and glass-forming properties of germanate, but the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C6/06C03C4/12C03C1/02C03C3/253
CPCC03C1/00C03C1/002C03C1/02C03C3/253C03C4/12
Inventor 张军杰田颖卢玉蔡沐之黄飞飞徐时清
Owner CHINA JILIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap