Graphene and nonmetallic tailing based foamed lightweight wallboard and preparation method thereof

A lightweight wallboard and non-metal technology, which is applied in the field of foamed lightweight wallboard based on graphene and non-metal tailings and its preparation, and can solve the problems of wear resistance, weather resistance, high temperature resistance, heat insulation, sound insulation , The waterproof and impermeability has not been better improved, the operation process is complicated, the raw material price is expensive, etc., to overcome the fear of open fire, improve the comprehensive utilization of resources, and be conducive to the effect of ecological environmental protection

Inactive Publication Date: 2018-03-02
GUANGXI XUTENG INDUSTRIAL GROUP CO LTD
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. The invention with the Chinese patent application number 201610090524.3 discloses a cement-based foamed lightweight composite material and its preparation method. The structure is regulated, and the pore structure, cement hydration products and structure are effectively regulated by using modified starch foam stabilizer and graphene oxide nanomaterials, so that the pore structure formed has a fine particle size and uniform distribution, and the cement hydration products The shape is regular and the arrangement is orderly, so that the cement-based foam composite material has a cross-network structure, so as to improve the strength and toughness of the cement-based lightweight composite material, but the raw materials used need to be pre-treated, and the operation process is complicated. It is recorded that the density in the strength is 0.6~0.7g / cm 3 , the compressive strength is greater than 2.5MPa, and the wear resistance, weather resistance, high temperature resistance, heat insulation, sound insulation, waterproof and impermeability have not been better improved, and need to be improved
[0005] 2. The invention of Chinese patent application number 201610258377.6 discloses a lightweight partition wall board with loofah fibers added. In this application, a large number of chemical additives and conventional raw materials are used. The raw materials are expensive and complicated. The prepared wall board, It has a good heat insulation effect, and is not prone to gaps, moisture absorption, and bubbling, which improves the quality of the partition wall. However, the water absorption rate still reaches 21.4%, and the compressive strength is 5.5MPa. There is still room for further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene and nonmetallic tailing based foamed lightweight wallboard and preparation method thereof
  • Graphene and nonmetallic tailing based foamed lightweight wallboard and preparation method thereof
  • Graphene and nonmetallic tailing based foamed lightweight wallboard and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] 1. The ratio of raw materials is shown in Table 1;

[0034] The non-metallic tailings are shown in Table 2;

[0035] Described clay is see table 3;

[0036] The high-temperature flux is shown in Table 4;

[0037] Described whipping agent is see table 5;

[0038] The stabilizers are yttrium oxide and cerium oxide.

[0039] 2. Preparation:

[0040] The specific method of preparing the foamed lightweight wallboard from the above-mentioned proportioning raw materials includes the following steps:

[0041] S1. Ore washing: crush the non-metallic tailings and pass through 1 mesh, then send the crushed non-metallic tailings into the immersion pool, the immersion pool is a cone cylinder, and the diameter of the inlet is 1 / 5 of the bottom diameter The high-pressure water pipeline set above the inner side of the feed inlet is sending the non-metallic tailings into the ammonium oxalate solution with a high-pressure spray mass concentration of 1.5% to spray and wet until the v...

Embodiment 2

[0046] 1. The ratio of raw materials is shown in Table 1;

[0047] The non-metallic tailings are shown in Table 2;

[0048] Described clay is see table 3;

[0049] The high-temperature flux is shown in Table 4;

[0050] Described whipping agent is see table 5;

[0051] The stabilizers are yttrium oxide and cerium oxide.

[0052] 2. Preparation:

[0053] The specific method of preparing the foamed lightweight wallboard from the above-mentioned proportioning raw materials includes the following steps:

[0054] S1. Ore washing: crush the non-metallic tailings and pass through 10 meshes, then send the crushed non-metallic tailings into the immersion pool. The high-pressure water pipeline arranged above the inner side of the feed inlet is sending in the non-metallic tailings while high-pressure spraying the ammonium oxalate solution with a mass concentration of 5.5% for spraying and wetting until the volume of the sprayed ammonium oxalate solution is equal to the non-metallic ...

Embodiment 3

[0059] 1. The ratio of raw materials is shown in Table 1;

[0060] The non-metallic tailings are shown in Table 2;

[0061] Described clay is see table 3;

[0062] The high-temperature flux is shown in Table 4;

[0063] Described whipping agent is see table 5;

[0064] The stabilizers are yttrium oxide and cerium oxide.

[0065] 2. Preparation:

[0066] The specific method of preparing the foamed lightweight wallboard from the above-mentioned proportioning raw materials includes the following steps:

[0067] S1. Ore washing: crush the non-metallic tailings and pass through 5 meshes, then send the crushed non-metallic tailings into the immersion pool. The high-pressure water pipeline set above the inner side of the feed inlet is sending the non-metallic tailings into the ammonium oxalate solution with a high-pressure spray mass concentration of 3.5% to spray and wet until the volume of the sprayed ammonium oxalate solution is equal to the non-metallic tailings. After the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of building enclosure wall materials, and particularly relates to a graphene and nonmetallic tailing based foamed lightweight wallboard and a preparation method thereof. The graphene and nonmetallic tailing based foamed lightweight wallboard comprises the following components in percentage by weight: 55-75% of nonmetallic tailings, 0.05-15% of graphene, 1-15% ofvermiculite, 0.05-15% of a high-temperature cosolvent, 5-20% of high-temperature-resistant fiber, 0.05-5% of a foaming agent, 1-20% of zirconia, 1-10% of clay, 0.05-5% of a stabilizing agent and 0.05-5% of a peptizing agent. The invention has the advantages that the graphene and nonmetallic tailing based foamed lightweight wallboard has the comprehensive properties of obvious aging resistance, corrosion resistance, heat insulation, sound insulation, water resistance, permeation resistance, fire resistance, light weight, high strength, no cracking, environmental protection and the like, and isprepared by adopting a production preparation method which is green and low-carbon, high in efficiency, energy-saving, consumption-reducing, and simple and convenient in operation.

Description

【Technical field】 [0001] The invention relates to the field of building enclosure wall materials, in particular to a foamed lightweight wallboard based on graphene and non-metallic tailings and a preparation method thereof. 【Background technique】 [0002] The existing concrete aerated blocks, shale hollow bricks, lightweight ceramsite concrete wall panels, and lightweight polyethylene concrete wall panels are of poor quality for the interior and exterior walls of the same volume, low compressive and flexural strength, and sound and heat insulation. Poor performance, poor waterproof and impermeable performance, high water absorption, easy cracking at the interface, easy cracking and falling off of the cement mortar batch layer, easy aging, unsafe and environmentally friendly, when making partition walls with aerated concrete and hollow brick wall panels, there is volume It is large, takes up a lot of building space, is heavy, and requires sporadic masonry. The surface of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/36C04B38/06
CPCC04B33/131C04B33/1324C04B38/068C04B2235/3225C04B2235/3229C04B2235/3244C04B2235/3826C04B2235/422C04B2235/425C04B2235/445C04B2235/5216C04B2235/5228C04B2235/5236C04B2235/77C04B2235/95C04B2235/96C04B2235/9607Y02P40/60
Inventor 黄聿新黄昭烨
Owner GUANGXI XUTENG INDUSTRIAL GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap