3D printing foaming shoe material and preparation method thereof

A technology for 3D printing and shoe materials, applied in the field of 3D printing materials, it can solve the problems of limited materials, achieve uniform cell size, enhance bonding strength, and reduce dosage.

Inactive Publication Date: 2018-04-13
广西景康商贸有限公司
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, 3D printing technology has been applied to the production of sports shoes, which can not only greatly improve the efficiency of production, but also can be tailored according to each user's feet, which has a good market prospect. However, due to the lag in research on 3D printing materials, The available materials on the market are limited, and the soles printed by 3D printing materials still need to be improved in terms of additional functions such as wear resistance, flame retardancy, soft and hard comfort, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 3D printing foaming shoe material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A 3D printing foam shoe material is made of the following raw materials in parts by weight: 80 parts of ethylene-vinyl acetate copolymer, 30 parts of EPDM rubber, 40 parts of glass fiber, 5 parts of wear-resistant agent, foam 6 parts of p-azodicarbonamide, 4 parts of γ-chloropropyl triethoxysilane, 15 parts of magnesium aluminum layered double hydroxide, 3 parts of flame retardant synergist, 3 parts of lubricant, foaming aid 3 parts of agent, 1 part of 2,6-di-tert-butyl-p-cresol; wherein, the flame retardant synergist is graphene and isopropyl tri(dioctyl pyrophosphate amidooxy) in a weight ratio of 3:1 Titanate. The foaming aid is composed of 3 parts of corn flour, 6 parts of acetylated monoglyceride fatty acid ester and 1 part of sodium alginate sulfate in parts by weight.

[0025] The anti-wear agent is prepared by the following method: the temperature of the internal mixer is raised to 330 ° C, and then 3 parts by weight of carbonyl iron, 6 parts by weight of wear-...

Embodiment 2

[0032]A 3D printing foam shoe material is made of the following raw materials in parts by weight: 90 parts of ethylene-vinyl acetate copolymer, 35 parts of EPDM rubber, 45 parts of glass fiber, 6 parts of wear-resistant agent, foam 8 parts of p-azodicarbonamide, 5 parts of γ-chloropropyl triethoxysilane, 18 parts of magnesium aluminum layered double hydroxide, 4 parts of flame retardant synergist, 4 parts of lubricant, foaming aid 4 parts of agent, 1 part of 2,6-di-tert-butyl-p-cresol; wherein, the flame retardant synergist is graphene and isopropyl tri(dioctyl pyrophosphate amidooxy) in a weight ratio of 3.5:1 Titanate. The foaming assistant is composed of 4 parts of corn flour, 7 parts of acetylated monoglyceride fatty acid ester and 1.5 parts of sodium alginate sulfate in parts by weight.

[0033] The anti-wear agent is prepared by the following method: the temperature of the internal mixer is raised to 340 ° C, and then 5 parts by weight of carbonyl iron, 8 parts by weigh...

Embodiment 3

[0040] A 3D printing foam shoe material is made of the following raw materials in parts by weight: 100 parts of ethylene-vinyl acetate copolymer, 40 parts of EPDM rubber, 50 parts of glass fiber, 8 parts of wear-resistant agent, foam 10 parts of p-azodicarbonamide, 6 parts of γ-chloropropyl triethoxysilane, 20 parts of magnesium aluminum layered double hydroxide, 5 parts of flame retardant synergist, 5 parts of lubricant, foaming aid 5 parts of agent and 2 parts of thiolauric anhydride; wherein, the flame retardant synergist is graphene and isopropyl tris (dioctyl pyrophosphate amidooxy) titanate in a weight ratio of 4:1. The foaming aid is composed of 5 parts of corn flour, 9 parts of acetylated monoglyceride fatty acid ester and 2 parts of sodium alginate sulfate in parts by weight.

[0041] The anti-wear agent is prepared by the following method: the temperature of the internal mixer is raised to 350 ° C, and then 8 parts by weight of carbonyl iron, 9 parts by weight of wea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention provides a 3D printing foaming shoe material and a preparation method thereof, and belongs to the technical field of 3D printing materials. The foaming shoe material is prepared from thefollowing raw materials in parts by weight: 80-100 parts of ethylene-vinyl acetate copolymer, 30-40 parts of ethylene-propylene-diene monomer rubber, 40-50 parts of glass fibres, 5-8 parts of a wear-resistant agent, 6-10 parts of a foaming agent, 4-6 parts of gamma-chloropropyl triethoxysilane, 15-20 parts of a flame retardant, 3-5 parts of a flame retardant synergist, 3-5 parts of a lubricatingagent, 3-5 parts of a foaming auxiliary agent and 1-2 parts of an antioxidant; the flame retardant is a layered double hydroxide; the flame retardant synergist is prepared from graphene and isopropyltris(dioctyl pyrophosphate) titanate which are in the weight ratio of (3-4):1. The 3D printing foaming shoe material prepared with the preparation method has relatively high wear resistance, flame resistance, good elasticity and moderate hardness.

Description

【Technical field】 [0001] The invention relates to the technical field of 3D printing materials, in particular to a 3D printing foamed shoe material and a preparation method thereof. 【Background technique】 [0002] 3D printing, also known as rapid prototyping technology, is also called additive manufacturing technology. It does not require traditional tools, fixtures and machine tools, but is based on digital model files, using adhesive materials such as metal powder or plastic Layer printing technology to manufacture objects of any shape. 3D printers can manufacture many items, such as airplanes, pistols, food, human organs, children's toys, etc. 3D printing technology is a major breakthrough in the world's manufacturing technology field in the past 20 years. [0003] At present, 3D printing mainly includes Fused Deposition Modeling (Fused Deposition Modeling, FDM), Selective Laser Sintering (Selective Laser Sintering, SLS), Stereo Lithography Apparatus (SLA), Laminated Ob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/16C08L27/18C08K13/04C08K7/14C08K7/00C08K3/22C08K3/04C08K5/5399C08J9/10C08J9/00A43B13/04
Inventor 覃晓捷
Owner 广西景康商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap