A method for improving biomimetic mineralization ability of titanium alloy implant surface

A biomimetic mineralization, titanium alloy technology, applied in prostheses, drug delivery, pharmaceutical formulations, etc., can solve the problem of not obtaining a nanometer surface layer, and achieve the effect of easily controlling repeatability, maintaining dimensional accuracy and surface roughness

Active Publication Date: 2021-03-05
ANHUI UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Huang Run et al. published the article "The Effect of Surface Mechanical Grinding on the Bioactivity of Medical Titanium Alloys" on pages 522-529, Vol. The TLM alloy was treated with SMAT for 30 minutes. The treated TLM alloy significantly changed the surface roughness, topological structure, hydrophilicity and the content of oxygen elements in different chemical states on the surface of the alloy, showing stronger biological activity, but the TLM titanium alloy The phase composition and grain size have not changed, and a nano-sized surface layer with good osteogenic effect has not been obtained

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for improving biomimetic mineralization ability of titanium alloy implant surface
  • A method for improving biomimetic mineralization ability of titanium alloy implant surface
  • A method for improving biomimetic mineralization ability of titanium alloy implant surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] This embodiment provides a method for improving the biomimetic mineralization ability of the titanium alloy implant surface, the specific steps are:

[0039] The sample is the TLM titanium alloy hot-rolled plate after vacuum smelting. The hot-rolled plate is cut into discs with a diameter of 100 mm and a thickness of 5 mm. #, 1200# water sandpaper grinding, surface polishing, ultrasonic cleaning with acetone and deionized water, drying, using the SNC-I type metal material surface nanometer test jointly manufactured by the Institute of Metal Research, Chinese Academy of Sciences and Chengdu New Crystal Technology Co., Ltd. The above-mentioned polished TLM wafers were SMAT treated by the machine. The treatment process was carried out under normal temperature and pressure. The impact balls used 50 GCr15 steel balls with a diameter of 5mm, the working frequency was 200Hz, and the vacuum was pumped to 3 As the ion source, the P ions used are selected by a symmetrical double-f...

Embodiment 2

[0052] This embodiment provides a method for improving the biomimetic mineralization ability of the titanium alloy implant surface, the specific steps are:

[0053] The sample is the TLM titanium alloy hot-rolled plate after vacuum smelting. The hot-rolled plate is cut into discs with a diameter of 100 mm and a thickness of 5 mm. #, 1200# water sandpaper grinding, surface polishing, ultrasonic cleaning with acetone and deionized water, drying, using the SNC-I type metal material surface nanometer test jointly manufactured by the Institute of Metal Research, Chinese Academy of Sciences and Chengdu New Crystal Technology Co., Ltd. The above-mentioned polished TLM wafers were SMAT treated by the machine. The treatment process was carried out under normal temperature and pressure. The impact balls used 50 GCr15 steel balls with a diameter of 2mm, the working frequency was 500Hz, and the vacuum was pumped to 3 As the ion source, the P ions used are selected by a symmetrical double-f...

Embodiment 3

[0055] This embodiment provides a method for improving the biomimetic mineralization ability of the titanium alloy implant surface, the specific steps are:

[0056] The sample is the TLM titanium alloy hot-rolled plate after vacuum smelting. The hot-rolled plate is cut into discs with a diameter of 100 mm and a thickness of 5 mm. #, 1200# water sandpaper grinding, surface polishing, ultrasonic cleaning with acetone and deionized water, drying, using the SNC-I type metal material surface nanometer test jointly manufactured by the Institute of Metal Research, Chinese Academy of Sciences and Chengdu New Crystal Technology Co., Ltd. The above-mentioned polished TLM wafers were SMAT treated by the machine. The treatment process was carried out under normal temperature and pressure. The impact balls used 50 GCr15 steel balls with a diameter of 8mm, the working frequency was 100Hz, and the vacuum was pumped to 17 ions / cm 2 , the injection beam density is 55μA / cm 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for improving the biomimetic mineralization ability of the surface of a titanium alloy implant. The method is to mechanically grind the surface of the titanium alloy implant to generate a nano-sized surface layer, and then use ion implantation technology to inject the nano-sized surface layer into the nano-sized surface layer. After implanting P ions, because the surface of the nano-sized implant has more defects such as dislocations, the injection effect is strengthened, and the implanted atomic concentration is more than three times higher than that of the non-nano-sized implant; after 28 days of immersion in simulated body fluid The surface of the implant is covered with spherical apatite, which significantly improves the biological activity of the titanium alloy implant.

Description

technical field [0001] The invention belongs to a method for modifying the surface of a titanium alloy implant, in particular to a method for improving the bionic mineralization ability of the surface of a titanium alloy implant. Background technique [0002] Titanium alloy has ideal physical and chemical properties and good biocompatibility. It is a clinical artificial implant material with good application prospects. Since it has no osteoinductive activity, it cannot form sufficient chemical combination with surrounding bone tissue. make clinical application limited. The chemical composition and structure of hydroxyapatite is similar to that of bone tissue, and it can combine with bone tissue through chemical bonds and induce new bone formation. Therefore, the use of hydroxyapatite coating method has become one of the commonly used modification methods for the surface of titanium alloys. [0003] At present, the methods for preparing HA thin films from titanium alloys ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/06A61L27/32A61L27/50C23C14/48C23C14/02
CPCA61L27/06A61L27/32A61L27/50A61L2400/12A61L2400/18A61L2420/02C23C14/021C23C14/028C23C14/48
Inventor 黄润秦亮黄雷黄明策
Owner ANHUI UNIV OF SCI & TECH