Anti-corrosion paint for guardrail surface layer and preparation method thereof

An anti-corrosion coating and surface layer technology, applied in the field of coatings, can solve the problems of increasing the overall cost of handrails, not having bacteriostatic properties, poor anti-aging properties, etc. Effect

Inactive Publication Date: 2018-07-20
HEFEI YIZHI DOORS & WINDOWS CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using aluminum alloy material for plugging, the price is relatively expensive, which increases the overall cost of the handrail
Although the spray paint film is cheap, the existing paint materials have poor aging resistance, are easy to powder and fall off, and do not have antibacterial properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of anticorrosion coating for handrail surface, comprises following raw material by weight:

[0028] 30 parts of epoxy resin, 25 parts of silicone resin, 10 parts of polyvinyl acetate, 5 parts of mica powder, 6 parts of attapulgite, 4 parts of silicon dioxide, 3 parts of ceramic fiber, 3 parts of nano titanium dioxide, nano magnesium hydroxide 3 parts, 3 parts of sodium antimony trioxide, 2 parts of negative ion powder, 3 parts of tea meal powder, 4 parts of bamboo charcoal powder, 2 parts of zirconia, 1.8 parts of pigment, 2.5 parts of silane coupling agent, 2.2 parts of antiaging agent, fluid 1.4 parts of leveling agent and 2.5 parts of tackifier.

[0029] The silane coupling agent is N-(β-aminoethyl)-γ-aminopropyltriethoxysilane.

[0030] Antiaging agent is 4,4-bis(dimethylbenzyl)diphenylamine.

[0031] The leveling agent is polyethyl acrylate.

[0032] The tackifier is composed of water glass and alkanolamide in a mass ratio of 2:1.

[0033] The pigment is...

Embodiment 2

[0041] A kind of anticorrosion coating for handrail surface, comprises following raw material by weight:

[0042] 40 parts of epoxy resin, 30 parts of silicone resin, 20 parts of polyvinyl acetate, 10 parts of mica powder, 12 parts of attapulgite, 10 parts of silicon dioxide, 8 parts of ceramic fiber, 6 parts of nano titanium dioxide, nano magnesium hydroxide 6 parts, 6 parts of sodium antimony trioxide, 5 parts of negative ion powder, 6 parts of tea meal powder, 7 parts of bamboo charcoal powder, 5 parts of zirconia, 3.6 parts of pigment, 4.5 parts of silane coupling agent, 3.8 parts of antiaging agent, fluid 3.1 parts of leveling agent and 4.8 parts of tackifier.

[0043] The silane coupling agent is N-β-(aminoethyl)-γ-aminopropyltrimethoxysilane.

[0044] Anti-aging agent is 4-methyl-6 tert-butylphenol.

[0045] The leveling agent is composed of polybutyl acrylate and ethyl acrylate in a mass ratio of 1:1.

[0046] The tackifier is composed of water glass and polyethylen...

Embodiment 3

[0055] A kind of anticorrosion coating for handrail surface, comprises following raw material by weight:

[0056] 37 parts of epoxy resin, 26 parts of silicone resin, 17 parts of polyvinyl acetate, 7 parts of mica powder, 10 parts of attapulgite, 8 parts of silicon dioxide, 6 parts of ceramic fiber, 4 parts of nano titanium dioxide, nano magnesium hydroxide 4 parts, 4 parts of sodium antimony trioxide, 3.5 parts of negative ion powder, 4.5 parts of tea meal powder, 6 parts of bamboo charcoal powder, 2.8 parts of zirconia, 2.5 parts of pigment, 3.8 parts of silane coupling agent, 3.2 parts of antiaging agent, fluid 2.3 parts of leveling agent and 3.8 parts of tackifier.

[0057] The silane coupling agent is composed of N-(β-aminoethyl)-γ-aminopropyltriethoxysilane and γ-aminopropylmethyldiethoxysilane in a mass ratio of 2:1.

[0058] Antiaging agent is 2-mercaptobenzimidazole.

[0059] The leveling agent is ethyl acrylate and butyl acrylate copolymer.

[0060] The tackifier ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses anti-corrosion paint for a guardrail surface layer and a preparation method thereof, and relates to the field of paint. The paint is prepared from the following raw materials in parts by weight: 30 to 40 parts of epoxy resin, 25 to 30 parts of organic silicon resin, 10 to 20 parts of polyvinyl acetate, 5 to 10 parts of mica powder, 6 to 12 parts of attapulgite, 4 to 10 parts of silicon dioxide, 3 to 8 parts of ceramic fiber, 3 to 6 parts of nanometer titanium dioxide, 3 to 6 parts of nanometer magnesium hydroxide, 3 to 6 parts of nanometer antimonous oxide, 2 to 5 partsof nanometer iron powder, 3 to 6 parts of tea meal powder, 4 to 7 parts of bamboo charcoal powder, 2 to 5 parts of zirconium oxide, 1.8 to 3.6 parts of pigments, 2.5 to 4.5 parts of silane coupling agents, 2.2 to 3.8 parts of anti-aging agents, 1.4 to 3.1 parts of leveling agents and 2.5 to 4.8 parts of tackifiers. The anti-corrosion paint has the advantages of high bonding performance, stable physicochemical property, high anti-corrosion performance, difficult pulverization falling, high anti-mechanical-impact performance, bacteriostatic effect and air purification effect.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an anti-corrosion coating for the surface layer of a handrail and a preparation method thereof. Background technique [0002] Handrails are mainly used for the protection and protection of personal safety and equipment and facilities in residences, highways, commercial areas, public places and other occasions, which can be seen everywhere in our lives. Handrails are often made of steel, such as: stainless steel, round steel pipe, square steel pipe or profiled steel plate, iron wire, etc. In order to improve the service life of the handrail and reduce the corrosion of the handrail, in recent years, the plugging of aluminum alloy material has been popular, or a layer of paint film has been sprayed on the surface of the handrail. The use of aluminum alloy material for plugging is relatively expensive, which increases the overall cost of the handrail. Although the spray paint film is cheap,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D183/04C09D131/04C09D5/08C09D5/14C09D5/18C09D7/61
CPCC09D163/00C08L2205/03C09D5/08C09D5/14C09D5/18C08L83/04C08L31/04C08K13/04C08K7/04C08K7/14C08K3/34C08K3/04
Inventor 汪中奇
Owner HEFEI YIZHI DOORS & WINDOWS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap