Extinction casting PE (polyethylene) film and preparation method thereof

A casting and matting technology, applied in the field of polymer chemistry, can solve the problems of limiting the application range of polyethylene, low strength, easy deformation, etc., and achieve good uniformity, enhanced strength and flame retardancy, and good strength.

Active Publication Date: 2018-07-24
四川厚诚新材料有限公司
View PDF9 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the shortcomings of polyethylene, such as low strength, easy deformation, and flammability, the application range of polyethylene is greatly limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Extinction casting PE (polyethylene) film and preparation method thereof
  • Extinction casting PE (polyethylene) film and preparation method thereof
  • Extinction casting PE (polyethylene) film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Embodiment 1 A kind of matting casting PE film

[0052] Formula is as follows by weight:

[0053]

[0054]

[0055] Among them: the average particle size of nano-silica is 100nm; the average particle size of nano-calcium carbonate is 100nm; titanate coupling agent and silane coupling agent in the blend of titanate coupling agent and silane coupling agent The weight ratio of aluminum atoms is 2:1; the silicon-aluminum molecular sieve is a Y-type molecular sieve, and the molar ratio of silicon atoms to aluminum atoms is 1.5:1.

[0056] The preparation method comprises the following steps:

[0057] (1) Get 2 parts by weight of nano silicon dioxide, 20 parts of nano calcium carbonate, 0.5 part of antioxidant 1098, 0.5 part of light stabilizer UV-419, 12 parts of polyvinyl alcohol, 8 parts of sodium stearate , 0.5 parts of sodium carboxymethyl cellulose, 2 parts of oleic acid amide, 1 part of a blend of titanate coupling agent and silicic acid coupling agent, 20 part...

Embodiment 2

[0061] Embodiment 2 A kind of matting casting PE film

[0062] Formula is as follows by weight:

[0063] Example 2

Inner layer / part

middle / part

outer layer / part

Nano silica

8

8

8

Nano calcium carbonate

10

10

10

Antioxidant 1010

2

2

2

Light stabilizer GW-4611

2

2

2

Polyvinylpyrrolidone

5

5

5

Glyceryl monostearate

3

3

3

Sodium carboxymethyl cellulose

2

2

2

Erucamide

0.5

0.5

0.5

Blend of titanate coupling agent and silicic acid coupling agent

2.5

2.5

2.5

LLDPE

10

10

10

Si-alumina molecular sieve

5

0

0

Aluminum phosphate

2

0

0

PA

0

9

0

Cobalt trioxide

0

0

1

scandium trioxide

0

0

0.5

zirconium dioxide

0

0

2

HDPE

60

60

60

[0064] Among them: the average particle size of nano-silica is 400nm...

Embodiment 3

[0066] Embodiment 3 A kind of matting casting PE film

[0067] Formula is as follows by weight:

[0068] Example 3

Inner layer / part

middle / part

outer layer / part

Nano silica

3

3

3

Nano calcium carbonate

17

17

17

Blend of Antioxidants 1098 and 1010

1

1

1

Light stabilizer UV-419

1.5

1.5

1.5

Dispersant polyvinylpyrrolidone

10

10

10

Glyceryl monostearate and or sodium stearate

4

4

4

Sodium carboxymethyl cellulose

1

1

1

Blend of Oleamide and Erucamide

1.5

1.5

1.5

Blend of titanate coupling agent and silicic acid coupling agent

1.5

1.5

1.5

LLDPE

19

19

19

Si-alumina molecular sieve

4

0

0

Aluminum phosphate

6

0

0

PA

0

4

0

Cobalt trioxide

0

0

0.4

scandium trioxide

0

0

1.2

zirconium dioxide

0

0

1.3

HDPE

55 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Puncture strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an extinction casting PE (polyethylene) film and a preparation method thereof. The extinction casting PE film has a three-layer structure of an inner layer, a middle layer andan outer layer; the PE film comprises the following preparation raw materials: nanometer silicon dioxide, nanometer calcium carbonate, an antioxidant, a light stabilizer, a dispersing agent, a lubricating agent, a tackifier, a slipping agent, a coupling agent, LLDPE, a silicon aluminum molecular sieve, aluminum phosphate, PA, cobalt oxide, scandium oxide, zirconium dioxide and HDPE; and the PE film is prepared by the steps of preparing an inner-layer film-forming material, a middle-layer film-forming material and an out-layer film-forming material by selecting different raw materials, and adding the above three layers of film-forming materials into a co-extrusion casting stretcher to prepare the PE film. The casting PE film prepared by the method has extinction property and has high tensile strength, anti-puncture strength and flame resistance.

Description

technical field [0001] The invention belongs to the field of macromolecule chemistry, and in particular relates to a polyethylene film and a preparation method thereof, more specifically to a matting cast PE film and a preparation method thereof. Background technique [0002] Polyethylene (PE) is a thermoplastic resin obtained by polymerization of ethylene. In industry, it also includes copolymers of ethylene and a small amount of α-olefin. Polyethylene is odorless and non-toxic, has excellent low temperature resistance, good chemical stability, insoluble in common solvents at room temperature, good water absorption, and excellent electrical insulation, so it is widely used in various industries. Polyethylene is divided into high-density polyethylene, medium-density polyethylene and low-density polyethylene according to different densities. PE film, which can withstand most acid and alkali erosion, has the advantages of light weight, non-toxic, moisture-proof, and superior h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L23/08C08L29/04C08L39/06C08L1/28C08L77/00C08K13/02C08K13/04C08K7/26C08K3/22C08K3/36C08K3/26C08K5/20C08K5/098B32B27/06B32B27/18B32B27/20B32B27/32B65D65/40B29C47/06
CPCB29C48/18B32B27/08B32B27/18B32B27/20B32B27/32B32B2250/24B32B2270/00B32B2307/3065B32B2307/40B32B2553/00B65D65/40C08K2003/2244C08K2003/2289C08K2003/265C08K2201/011C08L23/06C08L2201/02C08L2203/16C08L2205/035C08L2207/062C08L23/0815C08L29/04C08L1/286C08K13/04C08K7/26C08K3/36C08K3/26C08K5/20C08K5/098C08L77/00C08K13/02C08K3/22C08L39/06
Inventor 李健王广陈渊
Owner 四川厚诚新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products