Noise reduction and heat-insulation cement mortar and method for preparing same

A cement mortar, noise reduction and heat preservation technology, which is applied in the field of cement mortar, can solve the problems of increasing the difficulty of building construction, not obvious sound insulation effect, poor heat preservation effect, etc., and achieve good noise reduction and heat preservation effect, good sound insulation effect, and low void ratio Effect

Inactive Publication Date: 2018-08-17
HEFEI WANZHIJING DOORS & WINDOWS CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]Existing building materials such as cement mortar are widely used due to their easy construction and high strength. Higher and higher, sound insulation materials generally require high density and large thickness, etc. At present, the density of composite building materials on the market is small, and the sound insulation effect is not obvious after the construction is completed. In order to achieve the purpose of sound insulation, sound insulation is often added to the building wall. Cotton or sound insulation layer is realized, the cost is high, and it increases the difficulty of building construction
With the increasing awareness of environmental protection, the thermal insulation performance of building materials has been paid more and more attention. At this stage, ordinary cement mortar has poor thermal insulation effect, and there is an urgent need for a building material with significant thermal insulation effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A noise-reducing and heat-retaining cement mortar, comprising the following raw materials:

[0030] 75 parts of ordinary Portland cement, 45 parts of carbon fiber-graphene reinforcing agent, 25 parts of redispersible latex powder, 25 parts of ethyl acetate, 25 parts of phosphogypsum, 20 parts of fly ash, 20 parts of reinforced particle composition, polyurethane 15 parts, 15 parts of gelatin, 5 parts of modified rubber powder, 5 parts of fatty amine, 5 parts of N-acyl sarcosinate, 5 parts of aluminum sulfate, 5 parts of water repellent, 2 parts of triethanolamine and 100 parts of water;

[0031] Reinforcing particle composition: 10 parts of polypropylene fiber, 8 parts of silica sol, 4 parts of expanded perlite, 4 parts of calcium fluoride, 2 parts of polyvinyl alcohol, 2 parts of sodium silicate, 0.5 part of sodium gluconate and 0.5 part of cellulose ether share.

[0032] in,

[0033] The modified rubber powder includes the following raw materials in parts: 21 parts o...

Embodiment 2

[0050] A noise-reducing and heat-retaining cement mortar, comprising the following raw materials:

[0051] 95 parts of ordinary Portland cement, 55 parts of carbon fiber-graphene reinforcing agent, 35 parts of redispersible latex powder, 35 parts of ethyl acetate, 35 parts of phosphogypsum, 25 parts of fly ash, 25 parts of reinforced particle composition, polyurethane 20 parts, 20 parts of gelatin, 10 parts of modified rubber powder, 10 parts of fatty amine, 10 parts of N-acyl sarcosinate, 10 parts of aluminum sulfate, 10 parts of water repellent, 6 parts of triethanolamine and 120 parts of water;

[0052] Reinforcing particle composition: 15 parts of polypropylene fiber, 11 parts of silica sol, 7 parts of expanded perlite, 7 parts of calcium fluoride, 5 parts of polyvinyl alcohol, 5 parts of sodium silicate, 1.5 parts of sodium gluconate and 1.5 parts of cellulose ether share.

[0053] in,

[0054] The modified rubber powder includes the following raw materials in parts: 23...

Embodiment 3

[0071] A noise-reducing and heat-retaining cement mortar, comprising the following raw materials:

[0072] 85 parts of ordinary Portland cement, 50 parts of carbon fiber-graphene reinforcing agent, 30 parts of redispersible latex powder, 30 parts of ethyl acetate, 30 parts of phosphogypsum, 22.5 parts of fly ash, 22.5 parts of reinforcing particle composition, polyurethane 17.5 parts, 17.5 parts of gelatin, 7.5 parts of modified rubber powder, 7.5 parts of fatty amine, 7.5 parts of N-acyl sarcosinate, 7.5 parts of aluminum sulfate, 7.5 parts of water repellent, 4 parts of triethanolamine and 110 parts of water;

[0073] Reinforcing particle composition: 12.5 parts of polypropylene fiber, 10 parts of silica sol, 5.5 parts of expanded perlite, 5.5 parts of calcium fluoride, 3.5 parts of polyvinyl alcohol, 3.5 parts of sodium silicate, 1 part of sodium gluconate and 1 part of cellulose ether share.

[0074] in,

[0075] The modified rubber powder includes the following raw mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses noise reduction and heat-insulation cement mortar and a method for preparing the same, and relates to the technical field of cement mortar. The noise reduction and heat-insulation cement mortar comprises, by weight, 75-95 parts of ordinary silicate cement, 45-55 parts of carbon fiber-graphene reinforcing agents, 25-35 parts of redispersible latex powder, 25-35 parts of ethyl acetate, 25-35 parts of ardealite, 20-25 parts of fly ash, 20-25 parts of reinforced particle compositions, 15-20 parts of polyurethane, 15-20 parts of gelatin, 5-10 parts of modified rubber powder,5-10 parts of aliphatic amine, 5-10 parts of N-sodium cocoyl sarcosinate, 5-10 parts of aluminum sulfate, 5-10 parts of water repellents, 2-6 parts of triethanolamine and 100-120 parts of water. Thenoise reduction and heat-insulation cement mortar and the method have the advantages that excellent noise reduction and heat-insulation effects can be realized by the noise reduction and heat-insulation cement mortar, the noise reduction and heat-insulation cement mortar is high in abrasion resistance, chemical corrosion resistance, strength and impact strength, good in toughness and convenient toconstruct, and the like.

Description

technical field [0001] The invention relates to the technical field of cement mortar, in particular to a noise-reducing and heat-retaining cement mortar and a preparation method thereof. Background technique [0002] Existing building materials such as cement mortar are widely used due to their easy construction and high strength. However, with the improvement of user needs, the requirements for sound insulation performance of building materials are getting higher and higher. Sound insulation materials generally require high density and large thickness. At present, the density of composite building materials on the market is small, and the sound insulation effect is not obvious after the construction is completed. In order to achieve the purpose of sound insulation, it is often achieved by adding sound insulation cotton or sound insulation layer to the wall of the building, which is expensive and increases the difficulty of construction. . As people's awareness of environme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B111/20C04B111/34C04B111/52
CPCC04B28/04C04B2111/20C04B2111/343C04B2111/52C04B14/386C04B14/024C04B24/045C04B18/0445C04B18/08C04B24/282C04B24/38C04B24/121C04B24/124C04B22/148C04B24/122C04B16/0633C04B14/062C04B14/185C04B22/126C04B22/00C04B24/2623C04B24/10C04B24/383C04B18/22C04B24/42C04B22/14C04B24/085C04B24/281C04B2103/0057
Inventor 武娟
Owner HEFEI WANZHIJING DOORS & WINDOWS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products