Environment-friendly weather-resistant wood-plastic floor tile and preparation method thereof

A floor tile and weather-resistant technology, which is applied in the direction of floors, buildings, and building structures, can solve the problems of waste plastics and waste cardboard polluting the environment, and achieve the effects of benefiting human health, enhancing resilience, and rationally recycling waste resources.

Inactive Publication Date: 2018-09-18
合肥慧林建材有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems existing in the prior art, the present invention provides an environment-friendly weather-resistant wood-plastic floor tile and a preparation method thereof. The floor tile of the present invention has stable properties, good corrosion resistance, compression resistance and weather resistance, and can be used with waste plastic and waste cardboard as the main raw materials, which solves the environmental pollution problem of waste plastics and waste cardboard, and at the same time rationally recycles waste resources, saves energy consumption, and is green and environmentally friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 20 parts of polyvinyl chloride, 35 parts of waste plastic, 30 parts of waste cardboard, 15 parts of bamboo powder, 8 parts of glass fiber, 8 parts of attapulgite, 10 parts of light calcium carbonate, 3 parts of tourmaline powder, 5 parts of nano-titanium dioxide, 2 parts of methyl acrylate, 1.8 parts of silane coupling agent, and 2.4 parts of antibacterial agent.

[0029] The silane coupling agent is vinyltriethoxysilane.

[0030] The antibacterial agent is composed of zinc borate, carboxymethyl chitosan and eugenol in a mass ratio of 3:1:1.

[0031] This embodiment also discloses a method for preparing the above-mentioned environmentally friendly weather-resistant wood-plastic floor tiles, specifically, including the following steps:

[0032] (1) Disposal of waste cardboard:

[0033] (a) Putting waste cardboard into a pulverizer for pulverization, crossing a 50-mesh sieve, adding the pulverized cardboard powder into a 10% sodium hydroxide solution by mass, raising th...

Embodiment 2

[0042] 30 parts of polyvinyl chloride, 50 parts of waste plastic, 40 parts of waste cardboard, 25 parts of bamboo powder, 15 parts of glass fiber, 15 parts of attapulgite, 20 parts of light calcium carbonate, 6 parts of tourmaline powder, 10 parts of nano-titanium dioxide, 4 parts of methyl acrylate, 3.2 parts of silane coupling agent, and 3.5 parts of antibacterial agent.

[0043] The silane coupling agent is vinyltrimethoxysilane.

[0044]The antibacterial agent is composed of zinc borate, carboxymethyl chitosan and eugenol in a mass ratio of 3:1:1.

[0045] This embodiment also discloses a method for preparing the above-mentioned environmentally friendly weather-resistant wood-plastic floor tiles, specifically, including the following steps:

[0046] (1) Disposal of waste cardboard:

[0047] (a) put waste cardboard into a pulverizer for pulverization, cross a 100-mesh sieve, add the pulverized cardboard powder into a 10% sodium hydroxide solution by mass, raise the temper...

Embodiment 3

[0056] 24 parts of polyvinyl chloride, 40 parts of waste plastic, 34 parts of waste cardboard, 19 parts of bamboo powder, 10 parts of glass fiber, 10 parts of attapulgite, 14 parts of light calcium carbonate, 4 parts of tourmaline powder, 7 parts of nano-titanium dioxide, 2.5 parts of methyl acrylate, 2.3 parts of silane coupling agent, and 2.8 parts of antibacterial agent.

[0057] The silane coupling agent is 3-aminopropyltrimethoxysilane.

[0058] The antibacterial agent is composed of zinc borate, carboxymethyl chitosan and eugenol in a mass ratio of 3:1:1.

[0059] This embodiment also discloses a method for preparing the above-mentioned environmentally friendly weather-resistant wood-plastic floor tiles, specifically, including the following steps:

[0060] (1) Disposal of waste cardboard:

[0061] (a) Putting waste cardboard into a pulverizer for pulverization, crossing an 80-mesh sieve, adding the pulverized cardboard powder into a 10% sodium hydroxide solution by ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly weather-resistant wood-plastic floor tile and a preparation method thereof, and relates to the field of floor tiles. The environment-friendly weather-resistant wood-plastic floor tile comprises the following raw materials of, by parts, 20-30 parts of polyvinyl chloride, 35-50 parts of waste plastic, 30-40 parts of scrap cardboard, 15-25 parts of bamboo powder, 8-15 parts of glass fiber, 8-15 parts of attapulgite, 10-20 parts of light calcium carbonate, 3-6 parts of tourmaline powder, 5-10 parts of nano titanium dioxide, 2-4 parts of methyl methacrylate, 1.8-3.2 parts of silane coupling agents and 2.4-3.5 parts of antibacterial agents. The environment-friendly weather-resistant wood-plastic floor tile is stable in properties, has good corrosion resistance, pressure resistance and weather resistance. The environment-friendly weather-resistant wood-plastic floor tile adopts the waste plastics and the scrap cardboard as the main raw materials, the problem of environmental pollution caused by the waste plastics and the scrap cardboard is solved, meanwhile, waste resources are rationally recycled, energy consumption is saved, and environmental protection is realized.

Description

technical field [0001] The invention relates to the field of floor tiles, in particular to an environment-friendly weather-resistant wood-plastic floor tile and a preparation method thereof. Background technique [0002] Green environmental protection, low-carbon energy saving has always been the direction of my country's economic development. It has driven all walks of life in our country to increase the meaning of environmental protection, and set up measures for energy conservation and emission reduction. The same is true for the floor tile industry. New types of floor tiles are used in construction projects. It can effectively improve the environmental protection function of construction projects and save energy consumption. [0003] With the vigorous development of national online shopping and the increase of waste cartons for express delivery, the problem of recycling cartons is also becoming more and more serious. Similarly, the application of plastics as chemical raw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/02C08L101/00C08L1/02C08L27/06C08L97/02C08L5/08C08L89/04C08K13/04C08K7/14C08K3/34C08K3/38C08K3/22
CPCE04F15/02C08K2003/2241C08K2003/387C08K2201/011C08K2201/014C08L101/00C08L2205/035C08L1/02C08L27/06C08L97/02C08L5/08C08L89/04C08K13/04C08K7/14C08K3/346C08K3/38C08K3/22C08K7/12
Inventor 刘伍
Owner 合肥慧林建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products