Diatom ooze coating with purification effect
A technology of diatom mud coating and action, applied in the direction of coating, etc., to achieve the effect of good grain crystallinity, increased degradation rate, and low preparation temperature
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0036] Example 1
[0037] A diatom mud coating with purification effect, the weight percentage of each raw material is: 10% of diatomite, 5% of shell powder, 25% of light calcium carbonate, 12% of ethylene-vinyl acetate copolymer, 5% of cellulose ether %, composite photocatalyst 5%, guar gum 6%, surfactant 0.5%, dispersant 1%, the balance is deionized water;
[0038] The composite photocatalyst is Zr-BiNbO 4 Photocatalyst, Zr-BiNbO 4 The preparation method of photocatalyst is as follows:
[0039] (1) dissolve 10mol bismuth nitrate in 50% concentrated nitric acid, add water to be diluted to 5mol / L while stirring, obtain bismuth nitrate acid solution after stirring;
[0040] (2) 11mol potassium niobate is dissolved in 5-7mol / L potassium hydroxide solution, and after stirring, potassium niobate solution is obtained;
[0041] (3) while stirring the bismuth nitrate acid solution, the potassium niobate solution is dropped into it, after the dropwise addition, stirring is perform...
Example Embodiment
[0050] Example 2
[0051] A diatom mud coating with purification effect, the weight percentage of each raw material is: 15% of diatomite, 3% of shell powder, 30% of light calcium carbonate, 10% of ethylene-vinyl acetate copolymer, 7% of cellulose ether %, composite photocatalyst 8%, guar gum 9%, surfactant 1, dispersant 2%, the balance is deionized water;
[0052] The composite photocatalyst is Zr-BiNbO 4 Photocatalyst, Zr-BiNbO 4 The preparation method of the photocatalyst is the same as in Example 1;
[0053] Described surfactant is fatty alcohol polyoxyethylene ether ammonium sulfate;
[0054] Described dispersant is calcium stearate;
[0055] A preparation method of a diatom mud coating with purifying effect is:
[0056] S1. Activation of diatomite: 1kg of diatomite was added to a ball mill for grinding and pulverization, soaked in 10% nitric acid for 5 hours, filtered, washed to neutrality, dried, and then put into a muffle furnace for gradient calcination. The calc...
Example Embodiment
[0059] Example 3
[0060] A diatom mud coating with purification effect, the weight percentage of each raw material is: diatomite 5%, shell powder 6%, light calcium carbonate 25%, ethylene-vinyl acetate copolymer 12%, cellulose ether 6% %, composite photocatalyst 7%, guar gum 8%, surfactant 0.5%, dispersant 3%, the balance is deionized water;
[0061] The composite photocatalyst is Zr-BiNbO 4 Photocatalyst, Zr-BiNbO 4 The preparation method of the photocatalyst is the same as in Example 1;
[0062] Described surfactant is fatty alcohol polyoxyethylene ether ammonium sulfate;
[0063] Described dispersant is calcium stearate;
[0064] A preparation method of a diatom mud coating with purifying effect is:
[0065] S1. Activation of diatomite: 1kg of diatomite was added to a ball mill for grinding and pulverization, soaked in 10% nitric acid for 4 hours, filtered, washed to neutrality, dried, and then put into a muffle furnace for gradient calcination. The calcination steps...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap