High polymer water stopping material for crack repair and preparation method thereof

A crack repairing and water-stopping material technology, which is applied in the field of high polymer water-repellent water-stopping materials and their preparation, as well as in the field of crack repair engineering. Good, good water absorption, fast setting effect

Inactive Publication Date: 2019-03-01
西安长大公路养护技术有限公司
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the prior art, Chinese patent CN108424087A mentions a geopolymer-based cement pavement crack rapid repair material. The most prominent advantage is high strength, but its raw material process is complex and difficult to operate, and the main raw material is an inorganic binder. It does not have flexibility; and the production of powder generally requires simple process, easy to obtain raw materials, and crack glue has a certain degree of flexibility
[0007] Acrylic repair materials have the advantages of low viscosity and fast curing time, but they are generally polymerized organic polymer materials, suitable for asphalt pavement, not conducive to environmental protection and cracks in cement pavement, and have the problems of large volume shrinkage and short aging time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A high-polymer water-blocking material for crack repairing includes the following raw materials in parts by weight: vinyl monomer: 10 parts, cement substrate: 20 parts, humectant: 10 parts, initiator: 1 part, and initiator agent: 1 part, crosslinking agent: 1 part, water reducing agent: 1 part.

[0027] The above-mentioned vinyl monomer is one or more of acrylic acid, acrylamide, butyl acrylate, ethyl acrylate, vinyl acetate, methyl acrylate, styrene or methyl methacrylate.

[0028] The cement base material is one or more of Portland cement, aluminate cement, sulphoaluminate cement, iron-aluminate cement, fluoroaluminate cement or phosphate cement.

[0029] The above moisturizing agent is calcium sulfate, barium oxide, phosphorus pentoxide, calcium chloride, magnesium perchlorate, potassium hydroxide, aluminum oxide, concentrated sulfuric acid, silica gel, sodium hydroxide, calcium oxide, active anhydrous copper sulfate , magnesium sulfate, sodium sulfate, potassium su...

Embodiment 2

[0039] A high-polymer water-blocking material for repairing cracks includes the following raw materials in parts by weight: vinyl monomer: 30 parts, cement substrate: 60 parts, humectant: 30 parts, initiator: 2 parts, and initiator agent: 2 parts, cross-linking agent: 10 parts, water reducer: 2 parts.

[0040] The above-mentioned vinyl monomer is one or more of acrylic acid, acrylamide, butyl acrylate, ethyl acrylate, vinyl acetate, methyl acrylate, styrene or methyl methacrylate.

[0041] The cement base material is one or more of Portland cement, aluminate cement, sulphoaluminate cement, iron-aluminate cement, fluoroaluminate cement or phosphate cement.

[0042] The above moisturizing agent is calcium sulfate, barium oxide, phosphorus pentoxide, calcium chloride, magnesium perchlorate, potassium hydroxide, aluminum oxide, concentrated sulfuric acid, silica gel, sodium hydroxide, calcium oxide, active anhydrous copper sulfate , magnesium sulfate, sodium sulfate, potassium su...

Embodiment 3

[0049] A high-polymer water-blocking material for crack repairing includes the following raw materials in parts by weight: vinyl monomer: 20 parts, cement substrate: 45 parts, humectant: 20 parts, initiator: 1.5 parts, and initiator Agent: 1.5 parts, crosslinking agent: 5 parts, water reducing agent: 1.5 parts.

[0050] The above-mentioned vinyl monomer is one or more of acrylic acid, acrylamide, butyl acrylate, ethyl acrylate, vinyl acetate, methyl acrylate, styrene or methyl methacrylate.

[0051] The cement base material is one or more of Portland cement, aluminate cement, sulphoaluminate cement, iron-aluminate cement, fluoroaluminate cement or phosphate cement.

[0052] The above moisturizing agent is calcium sulfate, barium oxide, phosphorus pentoxide, calcium chloride, magnesium perchlorate, potassium hydroxide, aluminum oxide, concentrated sulfuric acid, silica gel, sodium hydroxide, calcium oxide, active anhydrous copper sulfate , magnesium sulfate, sodium sulfate, po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of road maintenance materials, and particularly relates to a high polymer water stopping material for crack repair and a preparation method thereof. The high polymer water stopping material has excellent characteristics like good bonding performance, high water absorbability, high fluidity, short coagulation time, high impermeability, high seasonal adjustability, high durability and simplicity and convenience in construction operation. The high polymer water stopping material comprises, by weight, 10-30 parts of vinyl monomer, 20-60 parts of cementbase material, 10-30 parts of moisturizing agent, 1-2 parts of initiator, 1-2 parts of co-initiator, 1-10 parts of crosslinking agent and 1-2 parts of water reducer. The high polymer water stopping material is prepared through a certain preparation method.

Description

technical field [0001] The invention belongs to the technical field of road maintenance materials, and in particular relates to a high-polymer water-resisting water-stopping material for repairing cracks and a preparation method thereof, in particular to cracks, kerfs, asphalt concrete pavements, and road bridges used in cement concrete pavements crack repair works. Background technique [0002] Cement concrete pavement is one of the most widely used pavement in highway engineering. In actual use, due to reasons such as poor concrete quality, improper construction, climate, hydration reaction of cement, dry shrinkage of cement concrete, and temperature stress, the diseases caused by cracks and slits on the cement concrete pavement affect the service life of the pavement. main reason. [0003] Asphalt concrete pavement is another pavement most widely used in highway engineering. In actual use, transverse cracks are caused by foundation and foundation settlement differences...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/06C04B28/34C08F220/06C08F220/56C08F220/18C08F220/14C08F212/08C08F220/20C08F222/38C08F212/36C08F220/58C04B111/72
CPCC04B28/04C04B28/06C04B28/34C04B2111/72C08F212/08C08F212/36C08F220/06C08F220/14C08F220/18C08F220/20C08F220/56C08F220/58C08F222/385C04B24/00C04B2103/465C04B2103/302C04B22/14C04B24/02C04B24/2652C04B24/2641C04B24/06C04B24/124C08F220/1804
Inventor 吴超凡吴莉亢小红凌俊丽吴世伟王炳林彭荣贵
Owner 西安长大公路养护技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka