A kind of mof-5 non-destructive modified carbon fiber reinforced resin-based wet friction material and preparation method thereof

A fiber-reinforced resin and wet friction material technology, which is applied in chemical instruments and methods, other chemical processes, bulk chemical production, etc., can solve the problems of fiber inherent strength damage, low interface bonding strength, and complicated experimental process, etc., and achieve improvement Holes, solve the effect of low interface strength and increase roughness

Active Publication Date: 2021-06-29
SHAANXI UNIV OF SCI & TECH
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The Chinese patent with the application number CN201610554989.X "A Method for Grafting Triazine Dendritic Molecules on the Surface of Carbon Fibers" removes the epoxy coating on the surface of carbon fibers, oxidizes carbon fibers, reduces carbon fibers, and grafts triazines on the surface of carbon fibers. Dendritic molecules and other processes have been used to obtain modified carbon fibers, which effectively solve the problems of less grafting of groups to carbon fibers and large loss of carbon fiber body strength, but the experimental process is cumbersome and the test period is long
The Chinese patent with application number CN201710056932.1 "A method of grafting and modifying carbon fiber surface sizing agent with acrylamide aqueous solution" solves the technology of low interfacial bonding strength of carbon fiber reinforced vinyl ester resin or unsaturated polyester resin composite materials problem, but will cause damage to the inherent strength of the fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mof-5 non-destructive modified carbon fiber reinforced resin-based wet friction material and preparation method thereof
  • A kind of mof-5 non-destructive modified carbon fiber reinforced resin-based wet friction material and preparation method thereof
  • A kind of mof-5 non-destructive modified carbon fiber reinforced resin-based wet friction material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] A method for preparing MOF-5 nondestructively modified carbon fiber reinforced resin-based wet friction material, comprising the following steps:

[0029] Step 1: Firstly, acetone is used in a Soxhlet extractor under oil bath conditions, and a mixture of acetone and water is used to treat carbon fibers in a supercritical state to remove surface sizing agents and other pollutants. It was washed and dried repeatedly with deionized water. Wherein, the temperature and time of the oil bath used were 110° C. and 2 h, respectively, and a mixed solution of acetone and water with a volume ratio of 5:1 was used to treat the carbon fibers in a Soxhlet extractor.

[0030]Step 2: The above-mentioned carbon fibers were treated with nitric acid at 130° C. for 2 hours, filtered and recovered, washed with deionized water, and placed in an oven at 70° C. for drying to obtain functionalized carbon fibers.

[0031] Step 3: Dissolve a certain amount of zinc nitrate hexahydrate and terephth...

Embodiment 1

[0037] Step 1: Firstly, acetone and a mixture of acetone and water are used to treat the carbon fiber at a supercritical state of 110°C in a Soxhlet extractor under oil bath conditions, so as to remove surface sizing agents and other pollutants. It was washed and dried repeatedly with deionized water. The above-mentioned carbon fibers were treated with nitric acid at 130°C for 2 hours, recovered by filtration, washed with deionized water, and placed in an oven at 70°C to dry for later use to obtain functionalized carbon fibers.

[0038] Step 2: Dissolve 0.1g polyacrylonitrile-based carbon fiber, 0.714g zinc nitrate hexahydrate and 0.133g terephthalic acid in 50mL N,N-dimethylformamide, magnetically stir for 1 hour, and perform a homogeneous reaction at 130°C React in the container for 24 hours, cool with the furnace, take out the carbon fiber after the reaction is completed, wash the carbon fiber with DMF and chloroform repeatedly for 3 times, age for 12 hours, and then dry it...

Embodiment 2

[0042] Step 1: Firstly, acetone and a mixture of acetone and water are used to treat the carbon fiber at a supercritical state of 110°C in a Soxhlet extractor under oil bath conditions, so as to remove surface sizing agents and other pollutants. It was washed and dried repeatedly with deionized water. The above-mentioned carbon fibers were treated with nitric acid at 130°C for 2 hours, recovered by filtration, washed with deionized water, and placed in an oven at 70°C to dry for later use to obtain functionalized carbon fibers.

[0043] Step 2: Dissolve 0.01g polyacrylonitrile-based carbon fiber, 0.714g zinc nitrate hexahydrate and 0.133g terephthalic acid in 50mL N,N-dimethylformamide, magnetically stir for 1 hour, and perform a homogeneous reaction at 130°C React in the container for 24 hours, cool with the furnace, take out the carbon fiber after the reaction is completed, wash the carbon fiber with DMF and chloroform repeatedly for 3 times, age for 12 hours, and then dry i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a MOF-5 nondestructively modified carbon fiber reinforced resin-based wet friction material and a preparation method thereof. First, carbon fibers are treated to remove surface sizing agents and other pollutants, and then the carbon fibers are treated with nitric acid at a certain temperature to obtain functional The carbon fiber is synthesized to provide active sites for subsequent growth. The carbon fiber, zinc nitrate hexahydrate and terephthalic acid are dissolved in N,N-dimethylformamide, and the carbon fiber is modified by a solvothermal reaction after uniform magnetic stirring. The carbon fiber modified by MOF-5 is obtained. Finally, the modified carbon fiber is mixed with aramid fiber, paper fiber and resin to prepare the base paper for friction material. After the hot pressing curing process, the MOF-5 modified carbon fiber reinforced resin matrix is ​​obtained. Wet friction material. The invention can avoid the loss caused by the traditional treatment process to the carbon fiber, improve the surface activity of the fiber without damaging the strength of the fiber.

Description

technical field [0001] The invention relates to the field of wet friction materials, in particular to a MOF-5 non-destructive modified carbon fiber reinforced resin-based wet friction material and a preparation method thereof, which are suitable for aviation, automobiles, trains, airplanes, ships, oil drilling rigs, mining machinery, energy sources , ships, construction and other traffic engineering machinery fields. Background technique [0002] Friction materials are widely used in various transportation vehicles (such as automobiles, trains, airplanes, ships, etc.) and transmission materials in brakes, clutches and friction transmission devices of various machinery and equipment, and are very important security parts. Resin-based friction material has the advantages of high friction coefficient, smooth and soft joint, low noise, less damage to the paired disc, and low cost. It is an indispensable friction material for power transmission or braking deceleration in various ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/14C08L1/02C08L77/10C08K9/04C08K7/06C08J5/24C09K3/14
CPCC08J5/24C08J2361/14C08J2401/02C08K7/06C08K9/04C09K3/14Y02P20/54
Inventor 费杰周曼段笑屈蒙张立洁谷岳峰黄剑锋曹丽云
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com