Treatment method of high-palladium high-tin high-copper regenerated tin anode slime

A technology of tin anode slime and treatment method, which is applied to the improvement of process efficiency, photography process, instruments, etc., can solve the problems of low comprehensive recovery rate, low recovery rate of precious metal gold, high process operation intensity, etc., and achieve labor intensity of workers Low, easy automatic control, good environmental effect
CN109971964AInactive Publication Date: 2019-07-05江西自立环保科技有限公司
14 Cites 4 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
江西自立环保科技有限公司
Publication Date
2019-07-05
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
Patent Text Reader

Abstract

The invention relates to a treatment method of high-palladium high-tin high-copper regenerated tin anode slime. The method comprises the following steps of (1) pre-leaching; (2) pressurized oxidationleaching; (3) precipitating silver; (4) separating gold; (5) separating silver; and (6) smelting in a tin-lead antimony-fire method. According to the treatment method, the copper and nickel in the high-palladium high-tin high-copper tin anode slime are effectively and selectively leached into the copper removal liquid, so that a cathode copper and nickel sulfate product can be obtained, the loss of silver in the pressurized oxidation leaching working sequence is effectively reduced through the silver precipitation operation, gold, silver and platinum and palladium are separated can be realizedthrough 'gold separation-silver separation' process, and tin and lead-antimony alloy products can be obtained by smelting through the tin-lead antimony-fire method. According to the treatment method,automatic control is easy to realize, effective separation and recovery of copper-nickel, tin-lead and antimony and noble metals can be realized, the whole process can realize closed-loop circulationof the smelting system, without emission of three wastes, and has the characteristics of good environmental effect, good economical efficiency and the like.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the technical field of nonferrous metallurgy, in particular to a method for treating regenerated tin anode slime with high palladium, high tin and high copper. Background technique

[0002] When crude tin is electrolytically refined, tin is reduced and precipitated at the cathode to become a product, and elements with a positive potential than tin remain at the anode and sink to the bottom of the electrolytic cell to become anode slime, which mainly contains Cu, Ni, Pb, Sn, Sb, Au, Ag , Pd and other metal elements.

[0003] The existing tin anode slime treatment methods mainly include:

[0004] One: reduction smelting - electrolysis process. The principle of this method is that the tin anode slime is mixed with sodium carbonate and reducing agent coal powder, etc., and sent to the reverberatory furnace or electric furnace for reduction smelting. The smelting temperature is 1200~1300°C, and the smelting time is 12h, and finall...