Composite electrolyte for preparing corrosion-resistant surface of petroleum pipeline and preparation method of corrosion-resistant layer of petroleum pipeline through ultrasonic-assisted electrodeposition

A technology of composite electrolyte and oil pipeline, which is applied in the field of preparation of composite electrolyte and ultrasonic-assisted electrodeposition of oil pipeline corrosion resistance, can solve the problem that it is difficult to make regular micro-nano structures, the process is difficult to control, and the service life is short and other problems to achieve the effect of promoting nickel deposition, reducing agglomeration and improving corrosion resistance

Active Publication Date: 2019-11-22
胜利油田金岛实业有限责任公司 +1
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method can theoretically improve the corrosion resistance of stainless steel, the process is not easy to control, and it is difficult to produce regular micro-nano structures, resulting in poor hydrophobicity and short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] The present embodiment makes the stainless steel surface superhydrophobic structure through the following steps:

[0063] (1) Preparation of composite electrolyte: add nickel sulfate, nickel chloride, sodium hydrogen phosphate, sodium sulfate and citric acid to deionized water, stir the solution evenly by magnetic force, mix sodium lauryl sulfate and nano-silicon carbide After mixing, add it to the solution in the magnetic stirring, mix evenly to prepare the electrolyte, the concentration of nickel sulfate in the electrolyte is 150g / L, the concentration of nickel chloride in the electrolyte is 50g / L, sodium hydrogen phosphate in the electrolyte The concentration in the electrolyte is 30g / L, the concentration of sodium lauryl sulfate in the electrolyte is 0.1g / L, the concentration of nano-silicon carbide in the electrolyte is 6g / L, and the concentration of sodium sulfate in the electrolyte is 10g / L, citric acid makes the pH value of the electrolyte solution 4, and the p...

Embodiment 2

[0071] The differences between this embodiment and Embodiment 1 are:

[0072] The concentration of each raw material component in the electrolyte in step (1) is:

[0073] Nickel sulfate 175g / L

[0074] Nickel chloride 65g / L

[0075] Sodium hydrogen phosphate 45g / L

[0076] Sodium Lauryl Sulfate 0.15g / L

[0077] Nano silicon carbide 6g / L

[0078] Sodium sulfate 20g / L

[0079] The consumption of citric acid makes the pH value of composite electrolyte solution be 4,

[0080] In step (3), the concentration of sodium phosphate in the first mixed solution is 50g / L, the concentration of sodium hydroxide in the first mixed solution is 15g / L, and the concentration of sodium carbonate in the first mixed solution is 40g / L L;

[0081] In step (4), the concentration of rhodin in the second mixed solution was 0.75 g / L, and the concentration of hexatropine in the second mixed solution was 0.3 g / L.

[0082] After the modified stainless steel, the static contact angle of deionized wate...

Embodiment 3

[0084] The differences between this embodiment and Embodiment 1 are:

[0085] The concentration of each raw material component in the electrolyte in step (1) is:

[0086] Nickel sulfate 200g / L

[0087] Nickel chloride 80g / L

[0088] Sodium hydrogen phosphate 60g / L

[0089] Sodium Lauryl Sulfate 0.2g / L

[0090] Nano silicon carbide 6g / L

[0091] Sodium sulfate 30g / L

[0092] The consumption of citric acid makes the pH value of composite electrolyte solution be 4,

[0093] In step (3), the concentration of sodium phosphate in the first mixed solution is 70g / L, the concentration of sodium hydroxide in the first mixed solution is 20g / L, and the concentration of sodium carbonate in the first mixed solution is 45g / L L;

[0094] In step (4), the concentration of rhodin in the second mixed solution is 1 g / L, and the concentration of hexatropine in the second mixed solution is 0.5 g / L.

[0095] After the modified stainless steel, the static contact angle of deionized water on t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Corrosion currentaaaaaaaaaa
Corrosion currentaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite electrolyte for preparing a corrosion-resistant surface of a petroleum pipeline and a preparation method of the corrosion-resistant layer of the petroleum pipelinethrough ultrasonic-assisted electrodeposition, and belongs to the technical field of electrolysis or electrophoresis processes. The electrolyte per liter is prepared from solute raw material components of 150-200 g of nickel sulfate, 50-80 g of nickel chloride, 30-60 g of sodium hydrogen phosphate, 0.1-0.2 g of sodium dodecyl sulfate, 6 g of nano silicon carbide, 10-30 g of sodium sulfate and 30-50 g of citric acid, and the solvent is deionized water. In an electrodeposition process, the nickel and phosphorus in the electrolyte are subjected to a reduction reaction on a stainless steel substrate as a negative electrode to be co-deposited on the stainless steel substrate to form a nickel-phosphorus alloy with an amorphous structure and a smooth surface, and therefore the corrosion resistance of the coating is improved; since the nano silicon carbide is inlaid in the nickel-phosphorus alloy, on the one hand, the nano silicon carbide forms a micro-nano double-roughness structure with thenickel-phosphorus alloy, and forms an air layer between the nano silicon carbide and water drops when making contact with the water drops, so that a hydrophobic structure is formed, and the corrosionresistance is improved; and on the other hand, the wear resistance of the coating is improved, and the service life of the coating is prolonged.

Description

technical field [0001] The invention belongs to the technical field of electrolysis or electrophoresis technology, and in particular relates to a method for preparing a composite electrolyte for preparing a corrosion-resistant surface of petroleum pipelines and an ultrasonic-assisted electrodeposition corrosion-resistant layer of petroleum pipelines. Background technique [0002] Metal materials are made into pipe fittings and are widely used in various fields, especially in oil fields, due to their excellent properties such as good electrical conductivity, heat dissipation, and easy processing. However, the chemical properties of metal pipe fittings are relatively active, and they are easily corroded in petroleum, thus shortening the service life of pipe fittings. Therefore, stainless steel pipes with relatively good corrosion resistance are mostly used to reduce the corrosion efficiency of the base material, but they will still be corroded after a long time. [0003] In o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25D3/56C25D15/00C25D5/20C25D5/36C25D5/48
CPCC25D3/562C25D5/20C25D5/36C25D5/48C25D15/00
Inventor 郭卫东刘可峰牛宗伟田佩佩滕云龙李丽
Owner 胜利油田金岛实业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap