Water-based metal antirust paint as well as preparation method and construction method thereof

A metal anti-rust, water-based technology, applied in the direction of anti-corrosion coatings, fire-resistant coatings, coatings, etc., can solve the problems of poor performance such as water resistance, salt spray resistance, salt water resistance, acid resistance, poor tightness and sealing of the coating film, The service life is not long, etc., to achieve the effect of low coating cost, increased hardness and improved work efficiency

Inactive Publication Date: 2020-08-07
广州双虹建材有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional metal antirust paint uses organic solvents as the dispersion medium, and is mainly composed of styrene-acrylic emulsion and other additives. When in use, it is directly painted on the base surface to form a dense paint film, which isolates water vapor from contacting the metal surface, thereby preventing rust. However, the traditional metal anti-rust paint has a big smell, serious environmental pollution, poor anti-aging performance, short service life, outdoor rainy season and other climates seriously affect the effect of the coating film, resulting in poor sealing and sealing properties of the coating film, water resistance, salt resistance Fog resistance, salt water resistance (3% sodium chloride solution), acid resistance, etc. are poor, and the service life is not long, and can only last for about 1 year

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Weigh the following raw materials by weight percentage: 54% of acrylic acid copolymerized pure acrylic emulsion, 0.4% of dispersant, 0.15% of wetting agent, 0.15% of defoamer, 10% of iron oxide powder, 2% of film-forming aid, anticorrosion 0.3% agent, 2% mica powder, 6% barium sulfate, 8% zinc phosphate, 3% heavy calcium powder, 0.3% anti-flash rust agent, 0.2% thickener, 0.1% pH regulator, and the balance of deionized water.

[0036] The preparation method of the deionized water-based metal antirust paint provided by the present embodiment may further comprise the steps:

[0037] (1) Add deionized water into the stirring disperser, add the dispersant at a speed of 350r / min, and continue stirring for 5 minutes after feeding;

[0038] (2) Add the defoamer and wetting agent into the stirring disperser at a speed of 350r / min, and stir for 5 minutes;

[0039] (3) Add the pH regulator into the stirring disperser, slowly add iron oxide powder, mica powder, barium sulfate, zi...

Embodiment 2

[0053] Weigh the following raw materials by weight percentage: 60% of acrylic acid copolymerized pure acrylic emulsion, 0.3% of dispersant, 0.1% of wetting agent, 0.2% of defoamer, 5% of iron oxide powder, 2.5% of film-forming aid, anti-corrosion 0.2% agent, 3% mica powder, 5% barium sulfate, 5% zinc phosphate, 5% heavy calcium powder, 0.4% anti-flash rust agent, 0.2% thickener, 0.4% pH regulator, and the balance of deionized water.

[0054] The preparation method of the deionized water-based metal antirust paint provided by the present embodiment may further comprise the steps:

[0055] (1) Add deionized water into the stirring disperser, add the dispersant at a speed of 450r / min, and continue stirring for 3 minutes after feeding;

[0056] (2) Add the defoamer and wetting agent into the stirring disperser at a speed of 450r / min, and stir for 3 minutes;

[0057] (3) Add the pH regulator into the stirring disperser, slowly add iron oxide powder, mica powder, barium sulfate, zi...

Embodiment 3

[0071] Weigh the following raw materials by weight percentage: 50% of acrylic acid copolymerized pure acrylic emulsion, 0.4% of dispersant, 0.15% of wetting agent, 0.2% of defoamer, 8% of iron oxide powder, 3% of film-forming aid, anticorrosion 0.3% agent, 2% mica powder, 10% barium sulfate, 8% zinc phosphate, 4% heavy calcium powder, 0.6% anti-flash rust agent, 0.4% thickener, 0.3% pH regulator, and the balance of deionized water.

[0072] The preparation method of the deionized water-based metal antirust paint provided by the present embodiment may further comprise the steps:

[0073] (1) Add deionized water into the stirring disperser, add the dispersant at a speed of 400r / min, and continue stirring for 5 minutes after adding the material;

[0074] (2) At the speed of 400r / min, add the defoamer and wetting agent into the stirring disperser, and stir for 5 minutes;

[0075] (3) Add the pH regulator into the stirring disperser, slowly add iron oxide powder, mica powder, bari...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses water-based metal antirust paint as well as a preparation method and a construction method thereof. The water-based metal antirust paint is composed of the following raw materials: an acrylic copolymer pure acrylic emulsion, a dispersing agent, a wetting agent, a defoaming agent, iron oxide powder, a coalescing agent, a preservative, mica powder, barium sulfate, zinc phosphate, heavy calcium carbonate powder, an anti-flash-rust agent, a thickening agent, a pH regulator and water. Water is used as a dispersion medium, and the raw material formula is prepared by utilizingmultiple antirust mechanisms such as physics and chemistry, so that the antirust paint has the characteristics of no toxicity, no odor, no pollution, no three wastes, no combustion and no explosion,and is environment-friendly and safe; the water-based metal antirust paint provided by the invention can be directly used, is simple, convenient and rapid, and a paint film formed after construction has excellent properties such as salt spray resistance, saline water resistance, fresh water resistance, gasoline resistance, ultraviolet light resistance, aging resistance, high temperature resistance, low temperature resistance, damp heat resistance, temperature change resistance and the like; the performance effect of a paint film formed after construction can be kept unchanged for at least three years, and the service life is long.

Description

technical field [0001] The invention relates to the technical field of antirust paint, in particular to a water-based metal antirust paint and its preparation and construction method. Background technique [0002] The traditional metal antirust paint uses organic solvents as the dispersion medium, and is mainly composed of styrene-acrylic emulsion and other additives. When in use, it is directly painted on the base surface to form a dense paint film, which isolates water vapor from contacting the metal surface, thereby preventing rust. However, the traditional metal anti-rust paint has a big smell, serious environmental pollution, poor anti-aging performance, short service life, outdoor rainy season and other climates seriously affect the effect of the coating film, resulting in poor sealing and sealing properties of the coating film, water resistance, salt resistance Fog resistance, salt water resistance (3% sodium chloride solution), acid resistance and other properties ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D5/08C09D7/61B05D1/28B05D7/16
CPCB05D1/28B05D7/16C08K2003/2265C08K2003/3045C08L2201/02C08L2205/03C09D5/08C09D5/18C09D133/04C09D7/61C08L83/12C08L83/04C08K5/053C08K5/06C08K3/22C08K3/34C08K3/30C08K13/02
Inventor 罗回新
Owner 广州双虹建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com