Ultraviolet LED with polarized doped composite polar surface electron blocking layer

Abstract

The invention discloses an ultraviolet LED with a polarized doped composite polar surface electron blocking layer. The device comprises a substrate arranged in sequence from bottom to top, the devicecomprises a low-temperature AIN nucleating layer, a high-temperature AlN intermediate layer, a non-doped AlGaN buffer layer, an n-type AlGaN layer, an Alx1Ga (1-x) 1N/Alx2Ga (1-x) 2N multi-quantum well active region, a polarization doped composite polar surface electron blocking layer and a p-type Alx5Ga (1-x) 5N layer, an n-type ohmic electrode is arranged on the n-type AlGaN layer; wherein a p-type ohmic electrode is arranged on the p-type Alx5Ga1-x5N layer, and the polarization doped composite polar surface electron barrier layer comprises a nitrogen polar surface p-type Alx3Ga1-x3N electron barrier layer and a metal polar surface p-type Alx4Ga1-x4N electron barrier layer which are arranged from bottom to top. The polarized doped composite polar surface electron barrier layer has higherelectron barrier layer hole concentration, and hole injection of the p-type Alx5Ga1-x5N layer is facilitated; lattice mismatch between the active region and the electron blocking layer is reduced, and the crystal quality of the epitaxial layer is improved; the radiation recombination efficiency of electron holes in an active region is improved, and the light-emitting efficiency of the ultravioletlight-emitting diode is improved.

Description

technical field [0001] The invention relates to the manufacturing field of semiconductor optoelectronic materials and devices, in particular to an ultraviolet LED with a polarization-doped composite polar surface electron blocking layer. Background technique [0002] Ultraviolet light-emitting diodes (UV-LEDs) based on III-nitride wide bandgap semiconductor materials have broad application prospects in the fields of sterilization, polymer curing, biochemical detection, non-line-of-sight communication, and special lighting. The light source mercury lamp, UV-LED has the advantages of mercury-free environmental protection, small and portable, low power consumption, low voltage and so on. For AlGaN-based UV-LEDs, the hole concentration is very low, coupled with the low mobility of holes, resulting in low efficiency of hole injection into the quantum well active region; while electrons have higher mobility and smaller Especially in the case of high current injection, it is easy ...

AI Technical Summary

Problems solved by technology

For AlGaN-based UV-LEDs, the hole concentration is very low, coupled with the low mobility of holes, resulting in low efficiency of hole injection into the quantum well active region; while electrons have higher mobility and smaller The effective mass, especially in the case of large current injection, is easy to overcome the limitation of the quantum well and reach the p-type region for non-radiative recombination with holes, so it will cause serious current leakage

[0003] like figure 2 As shown, the AlGaN-based UV-LED prepared in the prior art includes a substrate 201, a low-temperature AlN nucleation layer 202, a high-temperature AlN intermediate layer 203, an undoped AlGaN buffer layer 204, and an n-type AlGaN Layer 205, Al x1 Ga 1- x1 N/Al x2 Ga 1-x2 N multi-quantum well active region 206, metal polar surface Al x3 Ga 1-x3 N electron blocking layer 207 and p-type AlGaN layer 208, n-type ohmic electrode 209 and p-type ohmic electrode 210 respectively arranged on n-type AlGaN layer 205 and p-type AlGaN layer 208, wherein the metal polar surface p-type AlGaN electron blocking Layer 208 has a higher valence band barrier to prevent holes from being injected into the multi-quantum well active region; due to the larger voltage generated by the larger lattice mismatch between the last quantum well barrier and the electron blocking la

Images