Adhesive with anti-corrosion function

An adhesive and anti-corrosion technology, applied in the direction of adhesives, non-polymer organic compound adhesives, non-polymer adhesive additives, etc., can solve problems such as affecting product use, decreasing adhesive adhesion, and electrochemical corrosion, etc. To achieve the effect of excellent corrosion resistance

Active Publication Date: 2020-11-10
湖南创瑾科技有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] When the adhesive is connected to a metal surface that is easily oxidized or corroded, under high temperature and high humidity, electrochemical corrosion often occurs at the interface between the adhesive and the metal, resulting in the formation of metal oxides at the adhesive / metal interface, and the generation of interface oxides leads to the adhesion of the adhesive. The relay drops, affecting the use of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] 1. Preparation of polyurethane prepolymer: dehydrate polyethylene glycol 3000 (10 parts by weight of raw materials) at 110°C for 2 hours under a vacuum of 0.1MPa, and then mix with the prepared amount at 80°C Good diphenylmethane diisocyanate (20 parts by weight of raw materials) was reacted to form a low molecular weight prepolymer, and the reaction time was 2 hours to obtain a polyurethane prepolymer, which was stored under anhydrous conditions for use.

[0029] 2. Preparation of mixed epoxy resin: mix 40 parts of bisphenol A epoxy resin and 60 parts of 4-vinylcyclohexene (in parts by weight of raw materials), and mix them uniformly for later use.

[0030] 3. Other raw material components are commercially purchased. The main raw materials used in the examples of the present invention and comparative examples are as follows: bisphenol A epoxy resin: E-44; curing agent: N-aminoethylpiperazine; Accelerator: calcium carboxylate; filler: microsilica; oxygen scavenger: dihydr...

Embodiment 1

[0032] A kind of adhesive with anticorrosion function, its raw material composition is as shown in table 1 below:

[0033] Table 1. Adhesive preparation raw materials

[0034] components parts by mass Hybrid Epoxy 100 Polyurethane prepolymer 30 Hardener 20 Accelerator 3 filler 15 Oxygen scavenger 2 preservative 6

[0035] A method for preparing and using an adhesive with anti-corrosion function, comprising the steps of:

[0036] S1. Add the mixed epoxy resin, accelerator, filler, oxygen scavenger and preservative into the stirring tank in order, and mix the raw materials evenly through the mixer;

[0037] S2. Add polyurethane prepolymer and curing agent sequentially to the above raw materials, stir for 10 minutes and heat to 80°C to prepare an adhesive;

[0038] S3. Coating the adhesive between the two layers of galvanized sheets and curing it for 1 hour to obtain a galvanized sheet product bonded by the adhesive.

Embodiment 2

[0040] A kind of adhesive with anticorrosion function, its raw material composition is as shown in table 2 below:

[0041] Table 2. Adhesive preparation raw materials

[0042] components parts by mass Hybrid Epoxy 80 Polyurethane prepolymer 30 Hardener 20 Accelerator 3 filler 15 Oxygen scavenger 2 preservative 6

[0043] Compared with Example 1, the amount of mixed epoxy resin in this example is 80 parts, and the ratio of mixed epoxy resin to polyurethane prepolymer is 8:3. The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an adhesive with an anti-corrosion function, which is characterized by comprising the following raw materials in parts by weight: 80-150 parts of mixed epoxy resins, 20-40 parts of polyurethane prepolymers, 10-25 parts of curing agents, 2-5 parts of accelerants, 10-20 parts of fillers, 1-3 parts of deoxidants and 4-8 parts of preservatives, wherein the mixed epoxy resin comprises at least two of glycidyl ethers, glycidyl esters and alicyclic epoxy resin; the polyurethane prepolymer is prepared by carrying out a prepolymerization reaction on oligomer polyol and isocyanate, and the mass ratio of the oligomer polyol to the isocyanate is 1: (1-3). The adhesive has strong adhesiveness and corrosion resistance, and is especially suitable for metal surfaces which are easyto oxidize and corrode.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an adhesive with anti-corrosion function. Background technique [0002] Adhesive is a substance with good adhesive properties, which acts to connect objects by bonding surfaces through adhesion and cohesion. Adhesives are divided into natural polymer compounds (such as starch, animal skin glue, bone glue and natural rubber, etc.), synthetic polymer compounds (such as epoxy resin, phenolic resin, urea-formaldehyde resin, polyurethane and other thermosetting resins and polyvinyl acetal, superglue, etc.) thermoplastic resins such as vinyl chloride resin or synthetic rubber, etc.), or inorganic compounds (such as silicates, phosphates, etc.). Among them, in industrial production, synthetic polymer adhesives are more commonly used. [0003] Epoxy resin adhesives have a series of excellent properties, such as: good adhesion, wide bonding range, excellent mechanical properties, smal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/06C09J11/06C08F283/10C08F236/20C08F283/00
CPCC09J4/06C09J11/06C08F283/10C08F283/006C08F236/20
Inventor 岳利俞国金周佩先
Owner 湖南创瑾科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com