A kind of activated carbon and preparation method thereof

A technology of activated carbon and wood charcoal, applied in the field of activated carbon, can solve the problems of reduced adsorption capacity of activated carbon, excessive VOCs pollution, etc., and achieve the effects of improving processing performance, improving molding effect, and reducing cracks and burrs.

Active Publication Date: 2022-05-06
北京中科恩吉科科技发展有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems of excessive VOCs pollution and reduced adsorption capacity of activated carbon in the existing shaped activated carbon, the present invention provides an activated carbon with excellent performance, no pollution and strong adsorption capacity, and at the same time achieves an abrasion resistance greater than 98% and an iodine value greater than 900mg / g , the ash content is less than 10%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of activated carbon and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 200g of wood activated carbon powder, 5g of yellow dextrin, 5g of polyvinyl alcohol, 35g of high-temperature asphalt, 15g of sodium humate and 10.5g of C5 petroleum resin were pulverized by a pulverizer at a speed of 24000rpm / min, and then sieved with a 200-mesh vibrating sieve. The pass rate requirement is higher than 90%;

[0035] After crushing and screening, woody activated carbon powder larger than 200 meshes, yellow dextrin, polyvinyl alcohol, high-temperature asphalt, sodium humate and C5 petroleum resin powder are put into a kneader for pre-mixing. During the mixing process, the speed of the kneader is 60rpm / min, mixing time 15min;

[0036] Add 2.7g of lactic acid, 1.25g of 3-aminopropyltriethoxysilane and 105g of deionized water to the mixed powder, and then knead it into a billet through a kneader at room temperature. The kneader speed is 60rpm / min, and the kneading time is 2h ;

[0037] After the kneading is completed, the resulting billet is collected in ...

Embodiment 2

[0043] 200g of woody activated carbon powder, 5g of yellow dextrin, 5g of polyvinyl alcohol, 35g of SMP-II sulfonated phenolic resin, 15g of sodium humate and 10.5g of terpene resin were pulverized by a pulverizer at a speed of 24000rpm / min, and then 200-mesh vibrating sieve screening, the pass rate is required to be higher than 90%;

[0044] Put the crushed and screened woody activated carbon powder, yellow dextrin, polyvinyl alcohol, SMP-II sulfonated phenolic resin, sodium humate and terpene resin powder into the kneader for pre-mixing. The mixing process, Kneader speed 60rpm / min, kneading time 15min;

[0045] Add 2.7g of lactic acid, 1.25g of ethylene glycol dimethacrylate and 112g of deionized water to the mixed powder, and then knead it into a billet through a kneader at room temperature. The kneader speed is 60rpm / min, and the kneading time is 2h;

[0046] After the kneading is completed, the resulting blank is collected in a ziplock bag and stale for 12 hours;

[004...

Embodiment 3

[0052] 200g of woody activated carbon powder, 5g of yellow dextrin, 5g of polyvinyl alcohol, 25g of SMP-II sulfonated phenolic resin, 25g of high-temperature asphalt and 10.5g of C5 petroleum resin were pulverized by a pulverizer at a speed of 24000rpm / min, and then 200 mesh Screening by vibrating sieve, the pass rate is required to be higher than 90%;

[0053] Put the crushed and screened wood activated carbon powder, yellow dextrin, polyvinyl alcohol, SMP-II sulfonated phenolic resin, high-temperature asphalt and C5 petroleum resin powder into the kneader for pre-mixing, the mixing process, the kneader Rotation speed 60rpm / min, kneading time 15min;

[0054] Add 2.7g of lactic acid, 1.25g of ethylene glycol dimethacrylate and 110g of deionized water to the mixed powder, and then knead it into a billet through a kneader at room temperature. The kneader speed is 60rpm / min, and the kneading time is 2h;

[0055] After the kneading is completed, the resulting blank is collected i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
abrasion resistanceaaaaaaaaaa
Ash contentaaaaaaaaaa
Login to View More

Abstract

The invention relates to an activated carbon, the raw materials of which include: 70-80 parts of wood charcoal powder, 1-6 parts of normal-temperature binder, 15-20 parts of high-temperature binder, 3-5 parts of tackifier, and 0.5-part of extrusion aid 1 part, 0.1-0.5 part of coupling agent, and water accounting for 35-45% of the total mass of the above components; it also relates to a preparation method of activated carbon, which includes crushing and screening, mixing ingredients, kneading, aging, and extrusion molding , drying, carbonization and activation at the same time. The invention uses high-temperature asphalt, sodium humate and sulfonated phenolic resin instead of dangerous chemical coal tar as an adhesive, which reduces VOCs gas emissions during the preparation process and reduces environmental pollution. The bonding effect of the adhesive can improve the wear resistance and adsorption capacity of activated carbon. The wear resistance of activated carbon can reach 98%, the iodine value can reach 900mg / g, and the ash content is less than 10%. It can be used for some activated carbon wear resistance and adsorption capacity. There are application scenarios with high requirements, such as desulfurization and denitrification catalysts, gold extraction.

Description

technical field [0001] The invention relates to an activated carbon and a preparation method thereof, belonging to the technical field of activated carbon. Background technique [0002] Activated carbon is a carbon material with developed pore structure, large specific surface area, and strong selective adsorption capacity. It has been widely used in toxic and harmful gas purification treatment, water treatment, pharmaceutical industry, food industry, electronics industry and other fields. At present, activated carbon is mainly in the form of powder and amorphous granules. This type of activated carbon has disadvantages such as low bulk density, difficulty in storage and transportation, easy to cause dust pollution, high loss rate during use, and difficulty in recycling. Its application and promotion are limited. The current common way to solve this problem is to mix activated carbon with binder and process it into columnar, honeycomb and other shaped activated carbon. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/318C01B32/336
CPCC01B32/318C01B32/336
Inventor 崔彦斌王瑞强杨运国
Owner 北京中科恩吉科科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com