High-flash-point safe alkyd anticorrosive coating and preparation process thereof

A technology of anti-corrosion coating and preparation process, applied in anti-corrosion coatings, polyester coatings, coatings and other directions, can solve the problems of poor salt spray resistance, harmful to human health, low safety, etc. Chemical resistance, effect of increasing crosslink density

Inactive Publication Date: 2021-12-07
无锡市造漆厂有限公司
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Because alkyd resin has excellent durability, flexibility, and good brushability, it is widely prepared as anti-corrosion coating resin, which is used in vehicles, railways, large pipelines, construction and other fields; Medium, there are defects such as slow drying and easy yellowing, and the salt spray resistance of the coating is poor;
[0003] The flash point is an important basis for classifying the fire hazard of flammable liquids. Most of the solvents used in the existing alkyd resins are volatile flammable solvents, and the flash point is generally low, and it is easy to release a large amount of aromatic hydrocarbons, esters, and ketones after construction. Organic volatiles such as methionine pollute the environment and are also harmful to human health;
[0004] Existing alkyd resin coatings are mainly composed of long-oil semi-dry soy-acid alkyd resin, combined with 200# solvent oil, pigments and fillers, and drier; there are the following deficiencies: the product has a low flash point; Low safety; in the process of production, operation, transportation, storage and use, there are strict requirements on related production facilities, transportation vehicles, warehouse storage facilities and construction management; traditional alkyd resin coatings need to be used in large quantities in order to meet the construction conditions Organic solvents are used for dilution, so the VOC content is high, polluting the environment, requiring post-environmental protection treatment, and increasing costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-flash-point safe alkyd anticorrosive coating and preparation process thereof
  • High-flash-point safe alkyd anticorrosive coating and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Mix high iodine value oleic acid alkyd resin, titanium dioxide, nano-barium sulfate and ultrasonically disperse, grind, add high flash point solvent under stirring condition, then add emulsified water at 60°C, emulsify for 40min, then add high-efficiency drying agent agent to obtain a high flash point safe alkyd anti-corrosion coating;

[0043] The high flash point solvent is dipropylene glycol methyl ether;

[0044] In parts by weight, the emulsified water consists of: 10 parts of water-based epoxy emulsifier, 60 parts of deionized water; the preparation method of the water-based epoxy emulsifier is as follows: epoxy resin, polyetheramine, Water ethanol was stirred at 60°C for 5 hours under the protection of argon; after vacuum distillation at 60°C, acetic acid was added, ultrasonically dispersed, and reacted at 55°C for 1 hour to obtain a water-based epoxy emulsifier;

[0045] In terms of parts by weight, the content of each component in the anti-corrosion coating is...

Embodiment 2

[0055] Mix high iodine value oleic acid alkyd resin, titanium dioxide, nano-barium sulfate and ultrasonically disperse, grind, add high flash point solvent under stirring condition, then add emulsified water at 70°C, emulsify for 30 minutes, then add high-efficiency drying agent agent to obtain a high flash point safe alkyd anti-corrosion coating;

[0056] The high flash point solvent is diethylene glycol ether;

[0057] In parts by weight, the composition of the emulsified water is: 15 parts of water-based epoxy emulsifier, 65 parts of deionized water; the preparation method of the water-based epoxy emulsifier is as follows: epoxy resin, polyether amine, Water ethanol was stirred at 70°C for 4 hours under the protection of argon; after vacuum distillation at 80°C, acetic acid was added, ultrasonically dispersed, and reacted at 75°C for 0.8h to obtain a water-based epoxy emulsifier;

[0058] In terms of parts by weight, the content of each component in the anti-corrosion coat...

Embodiment 3

[0068] Mix high iodine value oleic acid alkyd resin, titanium dioxide, nano-barium sulfate and ultrasonically disperse, grind, add high flash point solvent under stirring condition, then add emulsified water at 80°C, emulsify for 20min, then add high-efficiency drying agent agent to obtain a high flash point safe alkyd anti-corrosion coating;

[0069] The high flash point solvent is ethylene glycol diacetate;

[0070] In parts by weight, the emulsified water consists of: 20 parts of water-based epoxy emulsifier, 70 parts of deionized water; the preparation method of the water-based epoxy emulsifier is as follows: epoxy resin, polyether amine, Water ethanol was stirred at 80°C for 3 hours under the protection of argon; after vacuum distillation at 90°C, acetic acid was added, ultrasonically dispersed, and reacted at 80°C for 0.5h to obtain a water-based epoxy emulsifier;

[0071] In terms of parts by weight, the content of each component in the anti-corrosion coating is: 40 pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-flash-point safe alkyd anticorrosive coating and a preparation process thereof. The anticorrosive coating prepared by the invention is compounded by taking renewable high-iodine-value oleic acid alkyd resin as an adhesive and taking a high-flash-point solvent, emulsified water, a high-efficiency drier, titanium dioxide, nano barium sulfate and the like as pigments and fillers; linseed oil with a high iodine value and basic alkyd resin are used for preparing the oleic acid alkyd resin with a high iodine value, so that the compactness, dryness and water resistance of the coating are synchronously improved; the linseed oil with a high iodine value is prepared by limiting the content ratio of maleic anhydride, linseed oil and azodiisobutyronitrile, so that the hydrolytic stability of the resin is improved; the basic alkyd resin with stable gloss, gloss retention, water resistance and outdoor durability is prepared by limiting the contents of maleic anhydride, linoleic acid, benzoic acid, tung linoleic acid, pentaerythritol and isophthalic acid; and the high-iodine-value oleic acid alkyd resin is modified by hollow titanium dioxide microspheres with the particle size of 250-300nm, so that the compactness of the coating is improved, and the corrosion resistance is greatly enhanced.

Description

technical field [0001] The invention relates to the field of anticorrosion paint preparation, in particular to a high-flash point safe alkyd anticorrosion paint and a preparation process thereof. Background technique [0002] Because alkyd resin has excellent durability, flexibility, and good brushability, it is widely prepared as anti-corrosion coating resin, which is used in vehicles, railways, large pipelines, construction and other fields; Medium, there are defects such as slow drying and easy yellowing, and the salt spray resistance of the coating is poor; [0003] The flash point is an important basis for classifying the fire hazard of flammable liquids. Most of the solvents used in the existing alkyd resins are volatile flammable solvents, and the flash point is generally low, and it is easy to release a large amount of aromatic hydrocarbons, esters, and ketones after construction. Organic volatiles such as methionine pollute the environment and are also harmful to h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D5/08C09D7/61C09F9/00
CPCC09D167/08C09D5/08C09D7/61C09D7/70C09F9/00C08K2003/2241C08K2003/3045C08K3/22C08K3/30C08K7/24
Inventor 顾贵荣顾柳燕
Owner 无锡市造漆厂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products