Composite material and preparation method thereof
A composite material and mixed solution technology, applied in chemical instruments and methods, water treatment of special compounds, water/sludge/sewage treatment, etc., can solve problems such as low catalytic efficiency, achieve simple preparation method, increase degradation rate, improve The effect of mass transfer and conduction capacity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment
[0029] a CuFeO 2 -TiO 2 The preparation method of composite material comprises the following steps:
[0030] (1) Weigh 2.0g of ferric nitrate and an appropriate amount of copper nitrate and tetrabutyl titanate, and add ferric nitrate, copper nitrate and tetrabutyl titanate to 200ml of absolute ethanol and acetic acid in a molar ratio of 1:1:1 In the mixed solution, the volume ratio of absolute ethanol and acetic acid is 1:1, the pH of the mixed solution is adjusted to 10 with sodium hydroxide solution, and ultrasonically dispersed for 30 minutes;
[0031] (2) Add 1.5ml of reducing agent propionaldehyde dropwise to the above mixed solution, and continue to stir vigorously for 30min;
[0032] (3) After the reaction kettle containing the mixed solution was subjected to hydrothermal reaction at 120° C. for 6 hours, it was naturally cooled and filtered;
[0033] (4) After filtering and washing, the filter cake is alternately washed with deionized water and absolute ethanol for 3...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com