Method for making high performance cement mixed material from flyash

A fly ash, high-performance technology, used in high-performance concrete, masonry mortar. It can solve problems such as unsatisfactory effect, complicated process and poor stability.

Inactive Publication Date: 2003-03-12
李国栋
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, a lot of compound excitation is used, that is, dry grinding of lime, gypsum, sodium sulfate and fly ash mixed. Although the early strength has been improved, the activity is not high, and the dosage is low, not higher t...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] According to the percentage by weight of the formula: 15% quicklime; 3% quick gypsum; 76% wet discharge fly ash (calculated as solid); 1.0% sodium sulfate; 1.7% calcium carbonate; 0.05% triethanolamine; 1% calcium chloride; lignin Calcium sulfonate 0.45%; Sodium nitrite 1.0%; Ferrous sulfate 0.8%. Add water and grind in a ball mill until the sieve of 45 μm is 15%, release the slurry, and spray dry to a moisture content of less than 1%, which is a high-performance multifunctional cement mixture with early strength, high strength, frost resistance, and impermeability. Replace 52.5R Portland cement with 40% and 50% high-performance fly ash equivalent, according to GB / T1767T1-1999 "Cement Mortar Strength Test Method Test", its strength indicators reach 42.5, 32.5 grades, and other indicators Both meet the national standard GB12958-1999 "Composite Portland Cement". It has early strength, frost resistance, impermeability, low heat of hydration, and good workability. Used in...

Embodiment 2

[0019] Same as Example 1, except that acetylene gas slag or milk of lime is used to replace quicklime on a dry basis; phosphogypsum is used to replace quicklime on a dry basis, and third-grade fly ash with a carbon content of 12% is used. The result is the same.

Embodiment 3

[0021] Same as Example 1, the difference is that the fineness of the slurry is 45 μm and the sieve residue is 9%, and 525R Portland cement is replaced with 55%, 70% equivalent, according to GB / T1767T1-1999 "Cement Mortar Strength Test Method" Test", its strength indicators reach 42.5 and 32.5 respectively, and other indicators reach the national standard GB12958-1999 "Composite Portland Cement". Good workability and high water reducing rate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A flyash mixture used for preparing high-performance cement is prepared from 11 raw materials including alkaline lime material, gypsum, flyash, sodium sulfate, calcium carbonate, etc through mixing them with water, grinding, sieving, and spray drying or baking. Its advantages are high activity, multiple functions, low cost and high performance.

Description

technical field [0001] The present invention relates to a method for producing high-performance cement admixture with fly ash. The cement admixture produced by this method has characteristics such as high activity, containing a large amount of ultrafine powder, and multi-function, and can be used for fly ash Portland cement, Composite Portland cement, ordinary Portland cement, and high-performance Portland cement are mixed materials and ground for the preparation of concrete, high-performance concrete, and masonry mortar. It belongs to the technical field of building materials and the technical field of environmental protection. Background technique [0002] Fly ash is a large amount of industrial waste, and its treatment and comprehensive utilization have attracted much attention from all over the world. The commonly used method in our country is to use undisturbed fly ash or finely ground fly ash as cement admixture and concrete admixture, brick and block. The use of fly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B7/24C04B28/02
CPCC04B28/02C04B7/243Y02P40/10Y02W30/91C04B12/04C04B18/08C04B22/064C04B22/085C04B22/10C04B22/124C04B22/143C04B22/147C04B22/149C04B24/122C04B24/18
Inventor 李国栋
Owner 李国栋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap