Heavy arenes lightening catalyst and preparing method thereof

A heavy aromatic hydrocarbon and catalyst technology, which is applied in the field of heavy aromatic hydrocarbon lightening catalyst and its preparation, can solve the problems of technical commercialization limitations, low space velocity, high reaction temperature and pressure, etc., and achieve improved activity stability, strong resistance Coke deposition capacity and the effect of increasing productivity

Inactive Publication Date: 2004-02-04
CHINA PETROLEUM & CHEM CORP +1
View PDF2 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the main method of lightening heavy aromatics is to use pyrolysis and catalytic dealkylation to produce light aromatics. The main disadvantages are high reaction temperature and pressure, and low space velocity, which limits the commercialization of the technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] The preparation method of catalyst of the present invention comprises:

[0020] (1) Mix the sodium type ZSM-5 zeolite, mordenite and alumina hydrate in a weight ratio on a dry basis, and then knead, shape and roast to obtain a composite carrier,

[0021] (2) Carry out ion exchange to composite carrier with ammonium salt aqueous solution, make the exchange capacity of the sodium ion in carrier be at least 90%, then wash,

[0022] (3) Formulating an impregnating solution with a group VIII metal compound, impregnating the ammonium-exchanged support, drying and calcining.

[0023] The (1) step of the above method is the preparation of the composite carrier, which is to mix the sodium-type ZSM-5 zeolite and mordenite with alumina hydrate in a predetermined proportion, and then add 25 to 60% of the weight of the mixed powder, preferably 35 to 45%. %, with a concentration of 1 to 5% by weight, preferably 1.5 to 3.0% by weight, of nitric acid aqueous solution kneading and mold...

example 1～6

[0031] Preparation of the catalyst of the present invention.

[0032] (1) Preparation of composite carrier

[0033] Combine an appropriate amount of sodium-type ZSM-5 zeolite (produced by Shanghai No. Mix alumina powder, add 40% by weight of powder, and 2% nitric acid aqueous solution, knead, extrude, dry at 110-120°C for 2 hours, and roast at 550°C in air for 4 hours to obtain a composite carrier.

[0034] (2) Ammonium exchange

[0035] Take 10 grams of the above-mentioned composite carrier, and use 0.5N NH at 90±10°C 4 20 ml of Cl solution was used to ion-exchange the carrier for 2 hours, filtered, and washed with deionized water until Cl-free - .

[0036] (3) Introduce metal components

[0037] Predetermined amounts of the precursors of each metal component were prepared as an impregnating solution, and the above ammonium ion-exchanged carrier was impregnated at room temperature with a liquid-solid ratio of 2 for 24 hours, filtered, dried at 110-120°C for 2 hours, and ...

example 7～8

[0043] Get the SB aluminum hydroxide powder that German condea company produces, under the condition of room temperature, liquid-solid ratio 2, use the SnCl that concentration is 10 mg / ml 2 After soaking in the solution for 15 hours and drying at 110-120° C. for 2 hours, aluminum oxide containing 0.48% by weight of tin was prepared. This tin-containing alumina is mixed with ZSM-5 zeolite and mordenite according to the dry weight ratio of 25:60:15, and the method of example 1 is used to mix with HNO 3 After peptization and molding, a tin-containing carrier is made, then ammonium exchange is carried out, and chloroplatinic acid and perrhenic acid with a concentration of 2.86 mg / ml and 11.8 mg / ml are used to prepare an impregnating solution, and the liquid / solid volume ratio is The ratio of 2 was impregnated with the carrier at room temperature for 24 hours, dried at 110-120°C for 2 hours, and calcined at 500°C in air for 4 hours to prepare catalysts G and H. See Table 2 for its...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A catalyst for lightening the heavy arylhydrocarbon contains the metal in VIII family and composite carrier including ZSM-5 zeolite, mordenite and alumina. It can increase the transform rate of C9 aryhydrocarbon and output rate of xylene, and decrease the carbon deposit.

Description

technical field [0001] The invention relates to a heavy aromatic hydrocarbon lightening catalyst and a preparation method thereof. Specifically, it is a catalyst containing aluminosilicate zeolite and noble metal components, which is suitable for lightening heavy aromatic hydrocarbons with more than nine carbon atoms to produce benzene, toluene and xylene (BTX) and its preparation method. Background technique [0002] Heavy aromatics generally refer to catalytic reforming, disproportionation and isomerization reactions to generate oil and C contained in ethylene cracking hydrogenated gasoline 9 ~C 16 Mono- and bicycloalkylaromatics. Heavy aromatics resources have not been rationally utilized for a long time, except for a small amount used as solvent and extraction of C 9 or C 10 Except for monomeric aromatics, they are basically blended into fuel for use. With the increasing improvement of environmental regulations, the content of heavy aromatics in fuel oil will be str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J29/068C07C4/18
Inventor 王建伟刘中勋杜晋轩金星花李砚青顾昊辉桂寿喜
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com