Nano composite latex paint and preparing method thereof

A nano-composite, latex paint technology, applied in the direction of latex paint, coating, etc., can solve the problems of scrub resistance, storage stability, etc., to improve color and gloss retention, scrub resistance, and surface active effect

Inactive Publication Date: 2004-04-14
中科纳米涂料技术(苏州)有限公司
View PDF2 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the scrub resistance and storage stability of these two coatings are not very good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025]17.5% water is put into the container of high-speed mixer earlier, add 0.5% microbicide Npcocide N-96 (Henkel Company), 3% alcohol ester-12 film-forming aid (Jilin Chemical Industry Company) successively under low speed (300rpm) Design and Research Institute), 0.5% wetting and dispersing agent Demol EP (Japan Kao Company), 2% defoamer BYK-011 (Germany BYK Chemical Company), 1% anti-sedimentation agent SER-AD BEZ 75 (Shengwo Company) , 8% ethylene glycol antifreeze, 10% nano slurry (containing 3% nano-silicon oxide, 2% nano-titanium oxide, 5% nano-zirconia, 85% water, 5% SN-Dispersant 5034), after mixing evenly , Slowly add 20% titanium dioxide, 10% heavy calcium carbonate and 5% talc into the vortex of the high-speed disperser. After adding the material, increase the impeller speed to make it about 1300rpm. When the fineness reaches 40 μm, gradually add 20% acrylic ester emulsion and 1% ammonia water (pH regulator) at 300rpm to adjust the pH value to 8.5, add 1 % Thicke...

Embodiment 2

[0027] 5% water is put into the container of high-speed mixer earlier, add 1.5% microbiocide BIT (UK ICI company), 1% Texanol ester alcohol film-forming aid (U.S. Eastman company), 1% moistening agent successively under low speed (200rpm). Wet dispersant DP-512 (Taiwan Deqian Trading Co., Ltd.), 0.5% defoamer SN-154 (German Henkel Company), 2% anti-settling agent SER-AD BEZ 75 (Shengwo Company), 4% B Diol antifreeze, 30% nano slurry (containing 1% nano-silicon oxide, 1% nano-titanium oxide, 80% nano-zirconia, 15% water, 3% Disperbyk181), after mixing evenly, 5% titanium dioxide, Add 5% red iron oxide, 5.3% lithopone, 2% light calcium carbonate and 5% wollastonite powder into the vortex of the high-speed disperser slowly. After adding the material, increase the impeller speed to about 1500rpm. When the fineness reaches 40μm, gradually add 30% silicon acrylic emulsion and 0.5% ammonia water (pH adjuster) at 300rpm to adjust the pH value to 8.5 and add 0.2 % Thickener ModicolVD-...

Embodiment 3

[0029] 2% water is first put into the container of high-speed mixer, and 2% microbicide TPN (Lanzhou Chemical Industry Company), 2% Loxasnol 842 DP / 3 film-forming aid (German Henkel Company) are added successively at low speed (200rpm) , 1% wetting and dispersing agent TD-01 (Tianjin Chemical Industry Research Institute), 1% defoamer BYK-074 (Germany BYK Chemical Company), 0.5% anti-settling agent SER-AD BEZ 75 (Shengwo Company), 0.8 % propylene glycol antifreeze agent, 50% nano slurry (containing 70% nano-silicon oxide, 2% nano-titanium oxide, 5% nano-zirconia, 15% water, 8% BEVALOID 211), after mixing evenly, add 5% zinc oxide Slowly add to the vortex of the high-speed disperser. After adding the material, increase the speed of the impeller so that the speed is about 1400rpm. When the fineness reaches 40μm, gradually add 32.7% polyvinyl acetate emulsion at 400rpm, add 2% thickener NATROSOL HH (American AQUALON company) and 1% The leveling agent ACRYSOL RM-4 (Rohm and Haas C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The composition of the invented nano composite latex paint comprises (wt%) 0.3-1% of moistening dipersant, 2-70% of nano pulp, 1-4% of film-forming adjuvant, 0.5-2% of anti-sedimentation agent, 0.8-15% of antifreeze agent, 0.5-3% of defoaming agent, 5-30% of pigment, 0-30% of filling material, 10-45% of emulsion, 0.2-2% of thickening agent, 0.2-2% of leveling agent, 0-2% of pH regulating agent, 0-2% of microbiocide and 2-35% of water. Its preparation method includes two steps: firstly, preparing dispersion stable nano material pulp, then adding said nano material pulp into the latex component according to a certain process so as to obtain the invented high-performance product.

Description

technical field [0001] The invention relates to paint technology, in particular to a nanocomposite latex paint and a preparation method thereof. Background technique [0002] Latex paint is a kind of water-based paint, which contains very low organic volatile matter, meets the requirements of environmental protection, and belongs to "green paint". It has been greatly developed since the latex paint was produced, and people continue to find ways to improve the performance of latex paint from different aspects. The emergence of nanomaterials has brought opportunities for the improvement of the performance of latex paints. For example, Chinese invention patent CN1277234A discloses a kind of architectural paint containing 0.5-1.5% silicon-based oxide. Improve the suspension, bonding strength, aging resistance and pollution resistance of the coating. Chinese invention patent CN1287145A reports a nano-paint for exterior walls prepared with nano-silicon oxides, nano-titanium oxi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/02C09D125/14C09D131/00C09D147/00C09D183/04
Inventor 刘福春韩恩厚柯伟张帆
Owner 中科纳米涂料技术(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap