Water-based all-purpose adhesive and method for preparing same

An all-purpose glue, water-based technology, applied in the application, coating, ink and other directions, can solve the problems of human body injury, environmental pollution, smelly working environment, etc., to achieve a wide range of applications, good stability, solve flammable Effect

Inactive Publication Date: 2008-07-23
唐浩
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to meet the needs of interior decoration, environmentally friendly all-purpose adhesives with styrene-butadiene rubber (SBS glue) and triphenyl solvents have appeared on the market, as disclosed in Chinese patent ZL 02115077.X (publication date 2003.10.29, publication number CN1451709A) "Multipurpose Universal Decorative Adhesive", Chinese Patent ZL02115167.9 (publication date 2003.11.05, publication number CN1453325A) disclosed "high-viscosity SBS non-toxic universal decorative glue" and Chinese patent ZL200410037322.X (publication date 2005.01. 26. The "Environmentally Friendly Universal Adhesive and Its Production Method" disclosed by Publication No. CN1570006A) is a product made of SBS as the main component and processed with various mixed solvents such as ethyl acetate and solvent naphtha. Although it does not contain Triphenyl is relatively harmful, but the inherent flammability and explosiveness of solvent-based glue has not been really solved. The volatilization of organic solvents in glue will also cause environmental pollution, and the working environment has a strong smell, and organic solvents are also harmful to the human body. Harmful, easy to form occupational diseases, not conducive to the health of workers
[0004] There are also various water-based adhesives in the prior art, such as water-based adhesives such as vinyl acetate homopolymer emulsions and acrylate copolymer emulsions, but all of them can only meet part of the use requirements, and there are deficiencies in one way or another. There is also a lack of a water-based universal adhesive that is widely applicable and easy to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based all-purpose adhesive and method for preparing same
  • Water-based all-purpose adhesive and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] (1) Put 50kg of dibutyl phthalate into a 100L enamel reaction kettle, heat to 80°C, then add 10kg of rosin resin and 10kg of rosin glycerin resin, stir and dissolve evenly for later use.

[0017] (2) Put 500kg of deionized water in a 1500L enamel reaction kettle, add 25kg of polyvinyl alcohol, stir and heat to 90°C to dissolve the polyvinyl alcohol, then cool down to 75-85°C to keep warm.

[0018] (3) Put 150kg of vinyl acetate, 30kg of methyl vinyl chlorosilane, 80kg of tertiary vinyl carbonate, 100kg of butyl acrylate, 100kg of isooctyl acrylate and 10kg of acrylic acid into the dropping tank and mix well .

[0019] (4) Add 5kg of γ-aminopropyltriethoxysilane, 8kg of sodium dodecylbenzenesulfonate, 8kg of OP-10, 5kg of sodium hexametaphosphate, and 3kg of defoamer in the reactor and 8kg of hydrochloric acid.

[0020] (5) Start to add the mixed monomers dropwise, and simultaneously add the initiator ammonium persulfate aqueous solution of 0.15% of the total weight of...

Embodiment 2

[0027] (1) Put 60kg of dibutyl phthalate in a 100L enamel reaction kettle, heat to 80°C, then add 15kg of rosin resin and 15kg of rosin glycerin resin, stir and dissolve evenly for later use.

[0028] (2) Put 500kg of deionized water in a 1500L enamel reaction kettle, add 30kg of polyvinyl alcohol, stir and heat to 90°C to completely dissolve the polyvinyl alcohol, then cool down to 75-85°C and keep warm.

[0029] (3) 120kg of vinyl acetate, 15kg of vinyltrichlorosilane, 150kg of tertiary vinyl carbonate, 80kg of butyl acrylate, 150kg of isooctyl acrylate and 5kg of acrylic acid were drawn into the dropping tank and mixed evenly.

[0030] (4) Add 2kg of vinyltrimethoxysilane, 5kg of nonylphenol polyoxyethylene alcohol sodium sulfate, 12kg of OP-10, 3kg of ethylenediaminetetraacetic acid disodium salt, 31kg of ethylenediaminetetraacetic acid disodium salt in the reaction kettle foaming agent and 10kg of hydrochloric acid.

[0031] (5) Start to add the mixed monomers dropwise, ...

Embodiment 3

[0038] (1) Put 80kg of dioctyl phthalate into a 100L enamel reaction kettle, heat to 80°C, then add 15kg of rosin resin and 15kg of rosin glycerin resin, stir and dissolve evenly for later use.

[0039] (2) Put 500kg of deionized water in a 1500L enamel reaction kettle, add 20kg of polyvinyl alcohol, stir and heat to 90°C to dissolve the polyvinyl alcohol, then cool down to 75-85°C to keep warm.

[0040] (3) 300kg of vinyl acetate, 15kg of vinyltrichlorosilane, 60kg of tertiary vinyl carbonate, 80kg of butyl acrylate, 100kg of isooctyl acrylate and 10kg of acrylic acid were drawn into the dropping tank and mixed evenly.

[0041] (4) Add 2kg of vinyltrimethoxysilane, 10kg of nonylphenol polyoxyethylene alcohol sodium sulfate, 5kg of OP-10, 3kg of sodium hexametaphosphate, 3kg of defoamer and 8kg in the reactor of hydrochloric acid.

[0042] (5) Start to add the mixed monomers dropwise, and simultaneously add 0.1% initiator ammonium persulfate aqueous solution with the total we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based all purpose adhesive and the preparation method, which belongs to the field of water-based adhesive, the technical proposal is a copolymer emulsion of 120 to 300 portions of vinyl acetate, 15 to 50 portions of organic silicon monomer with unsaturated double bond, 60 to 150 portions of ethylene tertiary carbonate, 80 to 120 portions of butyl acrylate, 90 to 150 portions of iso-octyl acrylate, 5 to 15 portions of acrylic acid; the emulsion also comprises 20 to 80 portions of tackifying resin, 3 to 8 portions of sodium salt decocting mixture, 50 to 150 portions of plasticizer, 15 to 50 portions of polyvinyl alcohol, 2 to 8 portions of silane coupling agent, 8 to 12 portions of hydrochloric acid, 3 to 15 portions of anionic emulsifier and 3 to 12 portions of nonionic emulsifier. The preparation method is that the mixed monomer is dropped by the manner of emulsion polymerization, and should be completed in three to five hours; warming up to 85 to 95 DEG C to cure for 40 to 60 minutes; then discharging and filtering and packaging after cooling down to 45 to 35 DEG C. The water-based all purpose adhesive has the advantages of convenient use, wide applicability, and can be used for the manufacturing of furniture, luggage and construction decoration.

Description

technical field [0001] The present invention relates to a kind of water-based adhesive, more specifically, it relates to a kind of water-based all-purpose adhesive used in furniture, bag manufacturing, building decoration, and the invention also relates to the preparation method of this all-purpose adhesive. Background technique [0002] The universal adhesive we usually refer to refers to a type of solvent-based adhesive commonly used in the architectural decoration and hardware maintenance industries. It is named for its wide bonding range and ease of use. The main component of early universal glue is neoprene, which generally uses benzene, toluene, and xylene as solvents. It is yellow liquid and viscous (commonly known as yellow glue). Bonding of hard and soft materials such as metals. Because benzene, toluene, and xylene are harmful to the body, their use has been banned abroad, but they will not withdraw from the domestic interior decoration market in the short term. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D131/04C09D11/06
Inventor 唐浩
Owner 唐浩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com