Preparation method of nano titanic oxide film for photochemical catalyst

A nano-titanium dioxide, titanium dioxide technology, applied in the direction of titanium dioxide, chemical instruments and methods, titanium oxide/hydroxide, etc., can solve the problems of poor bonding strength, the sol cannot be stored for a long time, the film is easy to fall off, etc. Specific surface area, the effect of improving the utilization rate of light energy

Inactive Publication Date: 2009-03-18
ZHANGJIAGANG PUSHENG OPTOELECTRONICS
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in the preparation method of photocatalytic nano-titanium dioxide film, the basic steps mainly adopt the sol-gel method to form the film, that is, the titanium dioxide precursor is hydrolyzed to obtain a titanium dioxide ultrafine colloidal solution, and then the brushing method and the pulling method are used to prepare the film. Transfer the titanium dioxide ultrafine particle sol to the metal mesh, and prepare nano-titanium dioxide film after drying and sintering. The bonding strength between this film and the carrier is poor, and the film is easy to fall off.
At the same time, it is also a technical defect that the sol cannot be stored for a long time in the traditional method.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] 1) Using butyl titanate as the precursor of titanium dioxide, using ethanol as the solvent, the volume ratio of the two is 1 to 5.5, adding diethanolamine as an inhibitor, and then adding an appropriate amount of polyethylene glycol as a pore-forming agent, at room temperature Stir at a low speed for 1.5 hours, then add a certain ratio of double distilled water and ethanol, and stir evenly to obtain a light yellow transparent sol, namely A glue;

[0009] 2) Use tetraisopropyl titanate or tetrabutyl titanate as the main raw material, mix it with isopropanol in a certain proportion, and slowly drop it into the dilute nitric acid solution prepared with deionized water to make B glue;

[0010] 3) Mix glue A and glue B evenly, add absolute ethanol and alcoholyze it into titanium dioxide colloid;

[0011] 4) At the same time, the stainless steel wire mesh is pretreated by pickling, alkali washing, pure water and ethanol cleaning, and through the processes of dipping, drying, ...

Embodiment 2

[0014] 1) Using butyl titanate as the precursor of titanium dioxide, using ethanol as the solvent, the volume ratio of the two is 1 to 6.5, adding diethanolamine as an inhibitor, and then adding an appropriate amount of polyethylene glycol as a pore-forming agent, at room temperature Stir at a low speed for 2.5 hours, then add a certain ratio of double distilled water and ethanol, and stir evenly to obtain a light yellow transparent sol, namely glue A;

[0015] 2) Use tetraisopropyl titanate or tetrabutyl titanate as the main raw material, mix it with isopropanol in a certain proportion, and slowly drop it into the dilute nitric acid solution prepared with deionized water to make B glue;

[0016] 3) Mix glue A and glue B evenly, add absolute ethanol and alcoholyze it into titanium dioxide colloid;

[0017] 4) At the same time, the stainless steel wire mesh is pretreated by pickling, alkali washing, pure water and ethanol cleaning, and through the processes of dipping, drying, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method used for a photocatalytic nano-TiO2 film; firstly, butyl titanate is taken as TiO2 former body; ethanol is taken as solvent; ethylene glycol used as inhibitor and polyethylene glycol used as pore-forming agent are added and mixed under room temperature at low speed; subsequently, secondary distilled water and ethanol with a certain proportion are added and uniformly mixed to gain glue A; secondly, titanium tetra-isopropoxide or tetrabutyl titanate is used as main raw material and mixed with isopropyl alcohol and dripped into compounded dilute nitric acid solution so as to gain glue B; glue A and glue B are uniformly mixed and anhydrous alcohol is added to be alcoholysed as TiO2 colloid; meanwhile, stainless steel wire net is pre-disposed by acid-washing and the like and working procedures such as glue-sticking and the like are carried out so as to gain the product. The preparation method has the advantages that the reaction efficiency of the catalyst and the utilization ratio of the light energy can be effectively improved, the film and the carrier form firm combination and keep best crystal form proportion.

Description

technical field [0001] The invention belongs to the field of preparation of titanium dioxide thin films, and relates to a preparation method of nano titanium dioxide thin films for photocatalysis. Background technique [0002] At present, the most studied and most promising solution to the purification of indoor air pollution is the nano-titanium dioxide technology for photocatalysis. It is characterized by being non-toxic to the human body, harmless to the environment, and can efficiently purify chemical pollution and biological pollution. It can kill bacteria and germs while decomposing organic matter and degrading toxic gases. At present, in the preparation method of photocatalytic nano-titanium dioxide film, the basic steps mainly adopt the sol-gel method to form the film, that is, the titanium dioxide precursor is hydrolyzed to obtain a titanium dioxide ultrafine colloidal solution, and then the brushing method and the pulling method are used to prepare the film. The t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J21/06B01J35/02A61L9/22C01G23/053B01J35/00
Inventor 李东
Owner ZHANGJIAGANG PUSHENG OPTOELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com