Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for preparing environment-friendly type organosilicon modified acrylic ester binding agent

A technology of acrylate and silicone, which is applied in the field of preparation of silicone-modified acrylate adhesives and silicone-modified acrylate adhesives, can solve the problems of poor rubbing fastness of fabrics, and achieve good environmental protection, Improvement of solvent resistance and functionality, effect of small domain size

Inactive Publication Date: 2011-02-09
WUHAN TEXTILE UNIV
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] Environmentally friendly acrylate adhesive, because the cross-linking monomer is glycidyl methacrylate, its environmental protection is good, but after use, the rubbing fastness of the fabric is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] The raw material of this preparation method comprises:

[0065] 1. Basic monomer

[0066] Hard monomer: methyl acrylate 15g, acrylonitrile 10g, styrene 10g, acrylic acid 2g;

[0067] Soft monomer: butyl acrylate 60g;

[0068] Cross-linking monomer: 3 g of glycidyl acrylate.

[0069] 2. Modified monomer

[0070] Silane monomer: organosiloxane mixed ring 2g;

[0071] Coupling agent: 0.02g of trimethoxyvinylsiloxane;

[0072] Inorganic nanopowder: 0.3 g of nano titanium dioxide with an average particle diameter of 50 nanometers.

[0073] 3 auxiliary monomers

[0074] Modified monomer catalyst: 0.2 g of dodecylbenzenesulfonic acid;

[0075] Basic monomer catalyst: ammonium persulfate 0.3g;

[0076] Emulsifier: compounded AEO 3.5g, sodium lauryl sulfate 2g;

[0077] Nano powder modifier: sodium silicate 0.3g;

[0078] Deionized water: 250g.

[0079] Preparation conditions and equipment of the preparation method:

[0080] Reaction pressure: one atmosphere;

[008...

Embodiment 2

[0106] The raw material of this preparation method comprises:

[0107] 1. Basic monomer

[0108] Hard monomer: methyl methacrylate 15g, styrene 20g, methacrylic acid 3g;

[0109] Soft monomer: 40g butyl acrylate, 16g ethyl acrylate;

[0110] Cross-linking monomer: 6 g of glycidyl methacrylate.

[0111] 2 modified monomer

[0112] Silane monomer: octamethylcyclotetrasiloxane 8g;

[0113] Coupling agent: 0.3 g of triethoxy vinyl siloxane;

[0114] Inorganic nanopowder: 2.0 g of nano silicon dioxide with an average particle diameter of 20 nanometers.

[0115] 3 auxiliary monomers

[0116] Modified monomer catalyst: sulfonic acid 0.8g;

[0117] Basic monomer catalyst: ammonium persulfate 0.6g;

[0118] Emulsifier: compounded AEO 3.5g, sodium lauryl sulfate 2g;

[0119] Nano powder modifier: 1.2g tetraethyl orthosilicate, 5g ethanol;

[0120] Deionized water: 220g.

[0121] Preparation conditions and equipment of the preparation method:

[0122] Reaction pressure: one a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing an environment-friendly silicone-modified acrylate adhesive. Raw materials of the preparation method comprise a basic monomer, a modified monomer and an auxiliary agent, wherein the basic monomer comprises a hard monomer, a soft monomer and a crosslinking monomer; the modified monomer comprises a silane monomer, a coupling agent and inorganic nano-powder; the crosslinking monomer is glycidyl acrylate or glycidyl methacrylate; and the grain diameter of the inorganic nano-powder is less than 80 nanometers. In the preparation method, the crosslinking monomer adopts the glycidyl acrylate or the glycidyl methacrylate so as to be environment-friendly. The product prepared by the method is a nanometer / silicone double-modified molecular composite polymer material. The molecular composite material is combined with the advantages of two polymer materials, namely silicone and polyacrylic ester and an inorganic nanometer material, and has better performance and broad application.

Description

technical field [0001] The invention relates to acrylate adhesives used in textile paint printing, paint dyeing, electrostatic flocking and finishing, and in particular to organosilicon-modified acrylate adhesives, especially organosilicon-modified acrylate adhesives method of preparation. Background technique [0002] Acrylate adhesives are widely used in paint printing, paint dyeing, electrostatic flocking, stiffening and finishing of various textiles. Acrylate adhesives are generally prepared by emulsion polymerization of acrylic acid (ester) raw materials. [0003] The above-mentioned raw materials include basic monomers, modified monomers and auxiliary agents, wherein: basic monomers include hard monomers, soft monomers, and crosslinking monomers; modified monomers are silane monomers or coupling agents; auxiliary agents It is modified monomer catalyst, basic monomer catalyst, emulsifier, deionized water, etc. [0004] The preparation method of present acrylate adhes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/04C08F220/10C08F230/08C08F2/44C08K9/04D06P1/52D06M15/356D06M11/00
Inventor 权衡杨振朱虹
Owner WUHAN TEXTILE UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com