Dispersible papermaking lubricant and preparation method thereof
A dispersive and lubricant technology, which is applied in papermaking, textiles, papermaking, paper coatings, etc., can solve the problems of poor storage stability, long storage time, easy layering, etc., and achieves improved storage stability, simple preparation process, solid The effect of a wide content range
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] Add 74 grams of calcium hydroxide and 1000 grams of water to a four-necked flask with a thermometer, disperse and heat up to 80°C, add 284 grams of stearic acid in a molten state, and the addition time is 0.5 hours. Material, dehydration (the same below) in the SB / SS type three-legged type upper discharge centrifuge, obtains the calcium stearate that weight solid content is 60%, this calcium stearate 505 grams and 2.47 grams of water disperse, add 2.22 grams of sodium lauryl sulfate, 1.48 grams of emulsifier MOA-3 (Jiangsu Haian Petrochemical Plant) (fatty alcohol polyoxyethylene condensate, n=3), after dispersion, grind in a grinder to obtain A dispersive lubricant with a solids content of 60% by weight.
[0022] The obtained product has an average particle size of 0.05 μm and a viscosity of 800 cps. Viscosity test uses NDJ-1 rotational viscometer 2# rotor; particle size test uses JL-1155 laser particle size distribution analyzer. The equipment used in the following ...
Embodiment 2
[0024] Add 58 grams of magnesium hydroxide and 1,000 grams of water to a four-necked flask with a thermometer, disperse and heat up to 70° C., add 100 grams of molten lauric acid, the addition time is 2 hours, react for 3.5 hours, and the product is cooled and discharged. Dehydration obtains the magnesium laurate that weight solid content is 50%, this magnesium laurate 213.4 grams and 338.7 grams of water disperse, add polyethylene glycol stearic acid monoester 2.9 grams, triethylhexyl phosphate (Jiande City Xinde Chemical Industry) 1.74 grams, uniformly dispersed, and then ground to obtain a dispersive lubricant with a solid content of 20%. The obtained product has an average particle diameter of 0.5 μm and a viscosity of 250 cps.
Embodiment 3
[0026] Add 171.3 grams of barium hydroxide and 1000 grams of water to a four-necked flask with a thermometer, disperse and heat up to 100°C, add 452 grams of triacic acid in a molten state, add the addition time for 1.5 hours, react for 5 hours, and cool the product out. Material, dehydration, obtain the barium triacionate that solid content is 85%, 567.4 grams and 37.26 grams of water dispersions of this barium trianoate, add sorbitan polyoxyethylene stearate monoester 0.34 gram, hydroxypropyl methyl 6.85 grams of cellulose, evenly dispersed and then ground to obtain a dispersive lubricant with a solid content of 80%. The average particle size of the product is 0.1μm, and the viscosity is 530cps.
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com