Flame retardant micro-foamed all plastic wood-like material and its preparation method

A wood-like material and micro-foaming technology, which is applied in the field of all-plastic wood-like materials and their preparation, can solve the problems of limited research reports, poor impact resistance, and easy burning of full-plastic wood-like materials, and reduce the difficulty of preparation technology , The flame retardant mechanism is simple, and the imitation wood effect is realistic

Inactive Publication Date: 2012-04-11
XIAMEN UNIV +1
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Song Yongming et al. (CN101153098A) disclosed a micro-foamed polystyrene-based wood-plastic composite material and its preparation method, which solved the problems of poor impact resistance and easy combustion of wood-plastic composite materials
At present, there are many researches and developments on traditional wood-plastic composite wood-like materials in China, and the research reports on all-plastic wood-like materials are relatively limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame retardant micro-foamed all plastic wood-like material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Mix 1 part of nano-silicon carbide, 1 part of nano-calcium carbonate, and 10 parts of ABS resin, dry in a dryer at 80°C for 2 hours, and simultaneously add 0.5 parts of CF-210 / AC composite foaming agent (1:1) to 0.5 parts, 0.5 parts of ACR cell regulator, 15 parts of flame retardant HBCD / antimony trioxide / magnesium hydroxide (6:4:5), smoke suppressant zinc molybdate / iron oxide / zinc borate (2:1:2) 5 parts, 0.2 parts of UV-531 (ultraviolet absorber), 0.2 parts of polyethylene wax / lithium complex soap base (1:1), 0.4 parts of sandalwood oil, 0.7 parts of polybutyl acrylate, zinc oxide / iron oxide red / 0.5 parts of carbon black were mixed, and then the two groups of mixtures were mixed with 100 parts of PS and 25 parts of HIPS, and the final mixture was extruded and granulated in a twin-screw extruder (granulation extrusion temperature 160° C.), and finally the obtained granules The material is extruded and processed in an extruder (180°C, screw speed 6-10r / min).

[0025] T...

Embodiment 2

[0030] Mix 1 part of nano-barium sulfate, 2 parts of nano-calcium carbonate, and 13 parts of AS / PMMA resin (8:5), and dry in a dryer at 80° C. for 2 hours. At the same time, 1 part of CF-420 / AP composite blowing agent (4:5), 1 part of ACR cell regulator, 20 parts of flame retardant TBBPA / antimony trioxide / aluminum hydroxide (8:7:5), Smoke suppressant zinc molybdate / zinc oxide / aluminum hydroxide (5:3:2) 10 parts, UV-531 (ultraviolet absorber) 0.3 parts, calcium stearate / zinc stearate / amino silicone oil (1:1 : 0.3 part of 1), 0.4 part of cloudwood oil, 1 part of butyl polyacrylate, 1 part of benzidine yellow / quinacridone purple / permanent yellow HR (4:2:4), and then mix the two Mix the group mixture with 100 parts of PS and 30 parts of HIPS, extrude and granulate the final mixture in a twin-screw extruder (granulation extrusion temperature 170°C), and finally put the obtained pellets in the extruder (200°C, screw speed 6~10r / min) for extrusion processing.

[0031] The product w...

Embodiment 3

[0033] Mix 1.5 parts of nano-silica, 1.5 parts of nano-barium sulfate, 3 parts of nano-calcium carbonate, and 15 parts of ABS / AS / PMMA resin (6:6:3), and dry in a dryer at 80°C for 2 hours. At the same time blowing agent AP / AC / NaHCO 3 Composite (7:3:5) 1.5 parts, cell regulator PA-530 / K-400 composite (1:1) 2 parts, flame retardant DBDPO / decabromodiphenylethane / antimony trioxide / hydroxide Magnesium / aluminum hydroxide (5:6:4:5:5) 25 parts, zinc molybdate fume / iron oxide / cuprous oxide, zinc borate (5:3:3:4) 15 parts, UV-531 ( UV absorber) 0.5 parts, polyethylene wax / amino silicone oil (2:3) 0.5 parts, camphor wood sesame oil 0.7 parts, polybutyl acrylate 1.3 parts, zinc oxide / iron oxide red / carbon black, benzidine yellow, quinine Mix 1.5 parts of acridone purple and permanent yellow HR (2:3:1:4:2:3), then mix the two groups of mixtures with 100 parts of PS and 35 parts of HIPS, and put the final mixture in a twin-screw extruder (Pelleting extrusion temperature: 160°C) to extrude...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Relating to an all plastic wood-like material and its preparation method, the invention provides a flame retardant micro-foamed all plastic wood-like material and its preparation method. The all plastic wood-like material comprises: 100 of polystyrene, 20-40 of high impact polystyrene, 10-15 of resin, 2-5 of an inorganic filling material, 15-25 of fire retardants, 5-15 of a smoke suppressant, 0.5-1.5 of foaming agents, 0.5-2 of a cell regulator, 0.5-2 of a colouring agent and 1.5-3 of auxiliary agents. The method consists of: mixing the auxiliary agents, the colouring agent, the fire retardants, the smoke suppressant, the foaming agents and the cell regulator according to the ratio so as to obtain a mixture A; drying the resin and the inorganic filling material; mixing polystyrene, high impact polystyrene, resin and the inorganic filling material, as well as the mixture A, thus obtaining a mixture B; subjecting the mixture B to granulation, and molding the obtained particles, thus obtaining the halogen-free and flame retardant micro-foamed all plastic wood-like material.

Description

technical field [0001] The invention relates to an all-plastic imitation wood material and a preparation method thereof, in particular to a micro-foaming all-plastic imitation wood material with a flame-retardant function and a preparation method thereof. Background technique [0002] Micro-foamed all-plastic wood-like material is a new type of energy-saving and environmentally friendly wood replacement product. It is made of pure polymer material foam and can be 100% recycled and reused. Since wood, plastic-wood composite materials and all-plastic imitation wood materials are combustible substances, once burned, the fire will spread rapidly and form a fire, which will inevitably cause irreparable casualties and property losses. As a new type of wood-replacing product, all-plastic imitation wood material has been widely valued by industries such as construction and home decoration for its flame retardant performance. Wang Mei et al. (Research Progress on Flame Retardancy of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/06C08L51/00C08L55/02C08L25/12C08L33/12C08K13/02C08K3/26C08K3/36C08K3/34C08K3/30C08K5/02C08K5/136C08K5/06C08K5/03C08K3/22C08J9/08C08J9/10
Inventor 曾碧榕许延利许一婷吴卫明戴李宗
Owner XIAMEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap