Method for recovering valuable metal from electroplating sludge

A technology of electroplating sludge and valuable metals, applied in the direction of improving process efficiency, etc., can solve problems such as poor economic benefits, environmental pollution, loss of metal resources, etc., achieve significant economic and social benefits, easy control of process conditions, The effect of high purity of recycled products

Inactive Publication Date: 2012-04-18
朱小红
View PDF8 Cites 47 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. Sintering method: Mix electroplating sludge and clay at a ratio of 1:20 or more, and burn it to 1000 degrees or more to make red bricks or gray bricks. However, due to the small sales volume and economic losses, it is difficult to form a production scale. The brick process still pollutes the environment and at the same time causes a large amount of precious metal resources to be lost;
[0004] 2. Acid-soluble-sulfurization method: It is a process of recovering nickel and copper by sulfide precipitation step by step. The nickel and copper products recovered by this process a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for recovering valuable metal from electroplating sludge
  • Method for recovering valuable metal from electroplating sludge

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] see figure 1 , the present embodiment production method is as follows:

[0036] Step 1: Put 500 grams of electroplating sludge raw materials (Ni5.6%, Cu7.8%, Cr3.88%, Zn3.12%, Fe1.29%) in a 3000ml beaker, with a 2:1 liquid-solid Then, slowly add concentrated sulfuric acid while stirring, and stop adding acid when the pH is stable at 1.5; then turn on the electric furnace to raise the temperature to 75°C, and under the condition of about 75°C, properly replenish acid to maintain pH = 1.5 remains the same, continue to decompose for 60 minutes; then carry out pressure filtration, the pressure filtration filtrate enters the next process to continue processing, the pressure filtration filter residue is washed, the washing water is returned to the previous process for pulping water, and the residue after washing is solidified.

[0037] Step 2: Put 1600ml of the solution prepared in step 1 into a 3000ml beaker, start stirring, and heat to 85°C. 2+ : NaClO 3 = Add sodium chl...

Embodiment 2

[0044] see figure 1 , the present embodiment production method is as follows:

[0045] Step 1: Put 500 grams of electroplating sludge raw materials (Ni3.5%, Cu1.2%, Cr6.43%, Zn1.12%, Fe2.01%) in a 3000ml beaker, with 3:1 liquid-solid Then, slowly add concentrated sulfuric acid while stirring. When the pH is stable at 1.5, stop adding acid; turn on the electric furnace and raise the temperature to 80°C. Change, continue to decompose for 1 hour; press filtration, the filtrate enters the next process to continue processing, the filter residue is washed, the washing water is returned to the previous process for pulping water, and the washed residue is solidified;

[0046] Step 2: Put 1600ml of the solution prepared in step 1 into a 3000ml beaker, start stirring, and heat to 90°C. 2+ : NaClO 3 = Add 10ml of sodium chlorate at a ratio of 6:0.5. After reacting for 20 minutes, slowly add 30% sodium carbonate solution while stirring. When the pH=4 or so, stop adding sodium carbonate...

Embodiment 3

[0053] see figure 1 , the present embodiment production method is as follows:

[0054] Step 1: Put 500 grams of electroplating sludge raw materials (Ni 3.45%, Cu 8.7%, Cr 5.69%, Zn 1.5%, Fe 2.31%) into a 3000ml beaker, and make a slurry with a liquid-solid ratio of 4:1 Then, slowly add concentrated sulfuric acid while stirring, when the pH is stable at 1.5, stop adding acid; turn on the electric furnace and heat up to 80°C, and under the condition of 80°C, add acid appropriately to keep pH = 1.5, and continue to decompose 80 minutes; then carry out pressure filtration, the pressure filtration filtrate enters the next process to continue processing, the pressure filtration filter residue is washed, and the washing water is returned as slurry mixing water, and the residue after washing is solidified;

[0055] Step 2: Put 1600ml of the solution prepared in step 1 into a 3000ml beaker, start stirring, and heat to 95°C. 2+ : NaClO 3 Add sodium chlorate in the ratio of =6:0.6 to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for recovering valuable metals from electroplating sludge. Electroplating sludge is used as a raw material; advanced theories and scientific means of leaching principle, redox principle, extraction principle, iron filing displacement principle and evaporation crystallization principle in a wet method metallurgy are integrally utilized; and a technology of ''acid decomposition of electroplating sludge-leachate purification to remove ferrochrome-P204 impurity removal-P507 enrichment-condensation crystallization'' is employed. Meanwhile, calcium and magnesium are removed by an extraction method, which substitutes a traditional sodium fluoride method for removing calcium and magnesium. A recovery rate of nickel reaches 95%, and copper content of recovered copper sponge is larger than 80%. Besides, acid dissolved slag and purifying slag can be solidified to reach requirements of environmental protection and will not cause secondary pollution; waste water can be recycled and has a strong technological versatility. The method is suitable for treating various routine electroplating sludge, has easily controllable technical conditions and low operating cost and is easy for realizing large scale production; therefore, the method is a practical novel technology for treating electroplating sludge in a way of quantitative reduction, harmlessness and resource.

Description

technical field [0001] The invention relates to a method for recovering valuable metals from electroplating sludge, and belongs to the technical field of resource recovery and utilization. technical background [0002] It is well known that there are many studies on the recovery of valuable metals from electroplating sludge, and there are many various process methods. [0003] 1. Sintering method: Mix electroplating sludge and clay at a ratio of 1:20 or more, and burn it to 1000 degrees or more to make red bricks or gray bricks. However, due to the small sales volume and economic losses, it is difficult to form a production scale. The brick process still pollutes the environment and at the same time causes a large amount of precious metal resources to be lost; [0004] 2. Acid-soluble-sulfurization method: It is a process of recovering nickel and copper by sulfide precipitation step by step. The nickel and copper products recovered by this process are only primary products,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B7/00C22B15/00C22B23/00
CPCY02P10/20
Inventor 朱小红
Owner 朱小红
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap