Piston rubber material for mud pumps and preparation method thereof

A technology for mud pumps and pistons, which is applied in the field of piston rubber for mud pumps and its preparation. It can solve problems such as uneven dispersion of processing aids, unfavorable occupational safety for workers, poor tearing and oil resistance, etc., and achieve good mechanical properties and improve comprehensive performance. Performance, improve the effect of high and low temperature resistance

Active Publication Date: 2013-04-17
平湖市泓博科技有限公司
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Through the improvement of the process, it overcomes the slow "eating" of fluorosilicone rubber in the open mill, easy sticking to the roller, high dust, high labor intensity, uneven dispersion of processing aids, low production efficiency, poor tear and oil resistance in the prior art, Detrimental to workers' occupational safety and other disadvantages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Piston rubber material for mud pumps and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A kind of preparation of piston rubber compound for mud pump,

[0021] Weigh 28kg of fluorosilicone rubber, 22kg of EPDM rubber 9650 (Germany LANXESS), 24kg of chlorosulfonated polyethylene rubber, 26kg of hydrogenated nitrile rubber, 11kg of modified tree ash, 3kg of ferrocene, and diisopropyl peroxide Benzene DCP0.4kg, carbon black N220 25kg, fumed white carbon black 14kg, hexamethyldisilazane 0.3kg, light calcium carbonate 6kg, zinc oxide 2kg, wollastonite powder 8kg, magnesium oxide 3kg, modified iron tail Mine 13kg, vulcanization accelerator M0.6kg, antioxidant RD 1.5kg, antioxidant TPPD 1.4kg, 2-mercaptobenzimidazole 1.6kg, vinyltriethoxysilane 2.5kg, dimethyl silicone oil 1.8kg,

[0022] The preparation method comprises the following steps:

[0023] (1) Preparation method of modified tree ash:

[0024] Add triphenyl phosphate with 1-2% weight of tree ash to the tree ash and mix, soak with 15-20% hydrochloric acid for 1-2 hours, wash with water until neutral, af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a piston rubber material for mud pumps. The piston rubber material is made from the following raw materials in parts by weight: 20-30 parts of fluorosilicone rubber, 50-60 parts of hydrogenated nitrile rubber, 15-25 parts of chlorosulfonated polyethylene rubber TS-320 (Tosoh), 2-3 parts of gamma-methacryloxypropyl trimethoxy silane, 1-2 parts of diphenyl silanediol, 14-16 parts of modified tree ashes, 2-3 parts of ferrocene, 0.2-0.6 part of dicumyl peroxide (DCP), 20-30 parts of high abrasion furnace (HAF) black N330, 20-25 parts of precipitated silica, 5-7 parts of light calcium carbonate, 2-4 parts of zinc oxide, 1-3 parts of calcium stearate, 1-3 parts of aluminum oxide, 5-8 parts of dolomite, 13-15 parts of modified iron ore tailing powder, 0.1-0.3 part of accelerant MBTS, 1-2 parts of sulfur, 1-2 parts of anti-aging agent RD, 1-2 parts of anti-aging agent MB, 1-2 parts of 2-mercaptobenzimidazole, 1-3 parts of methyl trimethoxysilane and 2-3 parts of paraffin wax. The rubber material disclosed by the invention has excellent resistance to high / low temperature, oil, solvents and chemicals; and meanwhile, the mechanical property is good, and the cost is low.

Description

technical field [0001] The invention relates to the field of synthetic rubber, in particular to a piston rubber for a mud pump and a preparation method thereof. Background technique [0002] Fluorosilicone rubber has excellent high and low temperature resistance, oil resistance, solvent resistance and chemical resistance. A new type of low temperature sealing material and fuel oil hose. [0003] In the prior art, a basic fluorosilicone raw rubber is used to prepare fluorosilicone compounded rubber through mixing. Due to the different molecular weight distribution and average molecular weight of different fluorosilicone raw rubber, the properties of fluorosilicone rubber compounded by mixing a single raw rubber are different. The high molecular weight of raw rubber has good tensile strength and tear strength. Good oil resistance, but poor processability and difficult mixing. The low molecular weight of raw rubber makes it difficult to have good tensile strength and tear st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/08C08L23/16C08L23/34C08L15/00C08K13/06C08K9/04C08K9/02C08K3/04C08K3/36C08K3/26C08K3/22C08K3/34C08K5/37
Inventor 王立新
Owner 平湖市泓博科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com