Water-based lubricant and preparing method of the same based on nanometer tungsten disulfide

A water-based lubricant and tungsten disulfide technology, which is applied in the direction of lubricating composition, base material, petroleum industry, etc., can solve the problems of high consumption of raw materials and energy, poor working environment, complicated procedures, etc., and achieve environmental protection and simple procedures , cheap effect

Inactive Publication Date: 2014-05-28
HENAN HUIER NANO TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the metal cold plastic forming process, the traditional process adopts surface treatment and lubrication treatment on the surface of the metal workpiece blank through acidification, phosphating, saponification and other processes. However, this method has complicated procedures, large consumption of raw materials and energy, and poor working environment. The cycle is long, and it will also cause serious environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] 1. Prepare a stearic acid aqueous dispersion with a solid content of 30%

[0037] First, add 35kg of water and 15kg of stearic acid granules into the reaction kettle, heat until the stearic acid is completely melted; then, add 200g of stearyl polyoxypropylene ether, 50g of fatty alcohol and Ethylene oxide condensate, after the reaction system is cooled to room temperature, stop stirring, add 50g polyoxypropylene glyceryl ether and 60g isothiazolinone; then, carry out ultrafine grinding for 7 minutes, and obtain stearin with a solid content of 30%. Acidic aqueous dispersion.

[0038] 2. Preparation of water-based lubricant based on nano-tungsten disulfide

[0039]Step 1, add 42g of water to the reaction kettle, slowly add 2.2g of polyvinyl alcohol 1788 powder at a stirring speed of 1000r / min, and mechanically stir for 1.5h, and the polyvinyl alcohol is completely dissolved in water; during the stirring process, add 0.02g Polyoxypropylene glyceryl ether, the obtained co...

Embodiment 2

[0042] 1. Preparation of a stearic acid aqueous dispersion with a solid content of 20%

[0043] First, add 40kg of water and 9.7kg of stearic acid granules into the reaction kettle, heat until the stearic acid is completely melted; then, add 100g of coconut oil fatty acid diethanolamide, 50g of Tween- 80. 50g sodium carboxymethylcellulose, stop stirring after the reaction system is cooled to room temperature, add 10g polyoxypropylene glyceryl ether, 30g polydimethylsiloxane and 60g dichlorodimethylhydantoin; then, Then carry out ultrafine grinding for 5 minutes to obtain a stearic acid aqueous dispersion with a solid content of 20%.

[0044] 2. Preparation of water-based lubricant based on nano-tungsten disulfide

[0045] Step 1, add 60g of water to the reaction kettle, slowly add 5.2g of polyethylene glycol 6000 powder at a stirring speed of 2000r / min, and mechanically stir for 45 minutes and the polyethylene glycol 6000 is completely dissolved in water; during the stirring ...

Embodiment 3

[0048] 1. Prepare a stearic acid aqueous dispersion with a solid content of 10%

[0049] First, add 45kg of water and 5kg of stearic acid granules into the reaction kettle, and heat until the stearic acid is completely melted; Vinyl ether, 50g urea, stop stirring after the reaction system is cooled to room temperature, add 30g emulsified silicone oil and 40g methyl p-hydroxybenzoate; then, carry out ultrafine grinding for 3min, and obtain stearic acid aqueous solution with a solid content of 10%. Dispersions.

[0050] 2. Preparation of water-based lubricant based on nano-tungsten disulfide

[0051] Step 1, add 51g of water into the reaction kettle, slowly add 3.3g of sodium alginate powder at a stirring speed of 3000r / min, after mechanical stirring for 2 hours, the sodium alginate is completely dissolved in water; during the stirring process, add 0.03g of polyoxygen Propylene Glyceryl Ether, the obtained content is 6% sodium alginate solution;

[0052] Step 2, in the sodium...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based lubricant based on nanometer tungsten disulfide, which comprises the following components and contents, by weight, 1% to 15% of nanometer tungsten disulfide, 1% to 10% of solid lubricant, 0.2% to 3% of antirust agent, 10% to 40% of aqueous stearic acid, 10% to 20% of waterborne zinc stearate, 0.4% to 4% of emulsifying stabilizer, 0.01% to 0.05% of defoaming agent, and 8% to 77% of water. The constituent content of the components sums up to 100%. The preparing method of the water-based lubricant and a usage method thereof are disclosed. The water-based lubricant based on the nanometer tungsten disulfide has the advantages of being good in the lubrication effect of the water-based lubricant, large in elongation coefficient, environment-friendly and unpolluted, and wide in applying scope. In addition, the preparing method of the water-based lubricant and the use method and process steps thereof are simple and fast so as to improve the production efficiency and benefit the environmental protection.

Description

technical field [0001] The invention belongs to the technical field of lubricant preparation, in particular to a water-based lubricant based on nanometer tungsten disulfide and a preparation method thereof. Background technique [0002] In the process of metal plastic forming, the resistance of tissue tangential movement is generated between the contact surfaces when the metal to be processed and the mold move relative to each other, that is, the external friction force. The existence of external friction will increase the force and energy required for processing, so the metal surface must be lubricated. If the lubrication of the metal surface does not meet the requirements, it will aggravate the wear of the mold, and the phenomenon of adhesion and abrasion on the surface of the workpiece will occur. Therefore, lubrication and plastic forming are closely related, and the development of lubrication technology can promote the development of metal cold plastic forming. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M173/00C10M111/02C10M111/06
Inventor 杜德光葛巧谊李明张文龙
Owner HENAN HUIER NANO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com