Tooth-spherical alumina carrier, tooth-spherical hydrotreating catalyst and preparation methods thereof

A spherical alumina, hydrotreating technology, used in physical/chemical process catalysts, chemical instruments and methods, treatment of hydrocarbon oil, etc. The effect of reducing the amount of ingredients added, optimizing the pore size distribution, and saving production costs

Active Publication Date: 2013-09-11
SHENYANG SANJUKAITE CATALYST
View PDF6 Cites 47 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the study found that the addition of peptizers, pore expanders, and forming aids will also have negative effects, mainly reflected in: the addition of peptizers with too large a proportion will seriously reduce the pore volume and specific surface area of ​​the carrier; Diffusion additives such as cellulose, CO

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tooth-spherical alumina carrier, tooth-spherical hydrotreating catalyst and preparation methods thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The preparation method of the toothed spherical alumina carrier described in this embodiment comprises the following steps:

[0035] (1) Weigh 100g of macroporous aluminum hydroxide with a pore diameter of 15-20nm produced by the carbonization method, 1.3g of the lubricant scallop powder, 3g of the dispersant ethyl cellulose, and 4g of the pore-enlarging agent sodium polyacrylate, and mix them by stirring After mixing the above-mentioned various components by machine for 20 minutes, add nitric acid solution 4g of peptizer mass concentration 60wt%, anionic surfactant dodecyl phosphate monoester 5g and deionized water 15g, then adopt kneader to mix 20 Minutes to make a soft block plastic body;

[0036] (2) Put the soft block-shaped plastic body prepared in step (1) into the chute of the extruder, extrude through the toothed spherical orifice plate, and then cut into pellets with a cutter, and keep it at room temperature for 40 minutes. , dried at 120°C for 3 hours, and c...

Embodiment 2

[0038] The preparation method of the toothed spherical alumina carrier described in this embodiment comprises the following steps:

[0039] (1) Weigh 100g of macroporous aluminum hydroxide with a pore diameter of 5-12nm produced by the carbonization method, 1.3g of a mixture of squash powder and stearic acid at a mass ratio of 1:1 as a lubricant, and ethyl cellulose as a dispersant 1.5 g of a mixture of cellulose and hydroxyethyl cellulose in a mass ratio of 1:1, and a pore-enlarging agent is a mixture of polyvinyl alcohol, sodium polyacrylate, starch derivatives and carbon black in a mass ratio of 1:1:1:1 1.5g, and use a stirring mixer to mix the above-mentioned various components for 40 minutes, add peptizers to be nitric acid solution (mass concentration is 60wt%), citric acid solution (mass concentration is 90wt%), acetic acid solution (mass concentration 30wt%) and tartaric acid solution (mass concentration 30wt%) with a mass ratio of 1:1:1:1 mixed acid solution consistin...

Embodiment 3

[0042] The preparation method of the toothed spherical alumina carrier described in this embodiment comprises the following steps:

[0043] (1) Weigh a total of 100g of the mixture of macroporous aluminum hydroxide produced by carbonization method and small-pore aluminum hydroxide produced by nitric acid method with a mass ratio of 1:1, 2g of lubricant kale powder, and dispersant ethyl cellulose 0.2g and 0.3g of pore-enlarging agent carboxymethyl starch, and after using a stirring mixer to mix the above-mentioned various components for 60 minutes, add 0.5g of acetic acid solution with a mass concentration of peptizer of 30wt%, and anionic surfactant butyloctyl Dithioester 0.2g and deionized water 14g, then adopt kneader to mix for 60 minutes, make soft lump plastic body;

[0044] (2) Put the soft block-shaped plastic body prepared in step (1) into the chute of the extruder, extrude through the toothed spherical orifice plate, and then cut into pellets with a cutter, and keep i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apertureaaaaaaaaaa
Apertureaaaaaaaaaa
Login to view more

Abstract

The invention relates to a tooth-spherical alumina carrier, a tooth-spherical hydrotreating catalyst and preparation methods thereof. The tooth-spherical alumina carrier comprises the following components in parts by weight: 0.5-4 parts of a peptizing agent, 0.2-2 parts of a lubricant, 0.2-3 parts of a dispersant, 0.3-4 parts of a pore-enlarging agent, and 100 parts of aluminum hydroxide. Because various additives such as the peptizing agent, the pore-enlarging agent, the dispersant, the anionic surfactant and the like in the tooth-spherical alumina carrier disclosed by the invention are greatly reduced, the cost of the tooth-spherical alumina carrier is saved, and the tooth-spherical alumina carrier also has the advantages of large specific surface area, high mechanical strength, and the like.

Description

technical field [0001] The invention relates to a toothed spherical alumina carrier, a toothed spherical hydrogenation catalyst and a preparation method thereof, belonging to the technical field of hydrogenation catalysts. Background technique [0002] With the development of the national economy, people's demand for energy is increasing. Petroleum is one of the important energy sources. Due to its non-renewability, petroleum resources, especially light oil resources, are decreasing day by day. With the reduction of light oil resources, the proportion of heavy oil in the world's oil production is increasing, and the content of residual oil in heavy oil is as high as 60%. Therefore, the lightening of heavy oil is very important in the current refining industry. One of the important jobs. Hydrotreating of heavy oil is one of the important means of lightening heavy oil. The so-called hydrotreating of heavy oil refers to the process of hydrodesulfurization of heavy oil in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J21/04B01J27/188B01J27/185B01J35/08C10G49/04
Inventor 闫闯赵素云李景斌
Owner SHENYANG SANJUKAITE CATALYST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap