Black weather-stress-cracking-resistant polyethylene cable sheath material and preparation method thereof

A technology of environmental cracking resistance and cable sheathing material, applied in the direction of insulating cables, cables, circuits, etc., can solve the problems of easy deformation, limited application range, easy cracking, etc., and achieve the effect of excellent resistance to environmental stress cracking

Active Publication Date: 2014-01-15
安徽天民电气科技有限公司
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing polyethylene sheath material is easily deformed when subjected to external force or molding process during use, and it is easy to crack when exposed to liquid solvent and its vapor state, which limits its application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Black weather-stress-cracking-resistant polyethylene cable sheath material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A black environmental cracking-resistant polyethylene cable sheath compound, made of the following raw materials by weight (kg): linear low-density polyethylene 60, high-density polyethylene 20, EVA resin 20, diisononyl phthalate 15 , propylene glycol sebacate polyester 10, epoxy linseed oil 7, antimony trioxide 15, zinc stannate 8, nano zeolite powder 6, straw ash 4, composite filler 5, nano dolomite 10, channel black 25, Dibutyltin Dilaurate 2, Calcium Stearate 1, Zinc Stearate 2, Oxidized Polyethylene Wax 4, Antioxidant DLTP1, Antioxidant 10102;

[0013] The preparation method of the composite filler is as follows: a. Take the following raw materials by weight (kg): attapulgite 8, sepiolite 6, potassium feldspar 6, bis(dioctyloxypyrophosphate)ethylene titanate Ester 1.5, titanium dioxide 4, nano-carbon 5, nano-alumina 3, paraffin oil 6, polyisobutylene 4, ferrocene 2, zinc methacrylate 1.5, p-tert-octylphenol formaldehyde resin 7; b, attapulgite , sepiolite and pota...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a black weather-stress-cracking-resistant polyethylene cable sheath material and a preparation method thereof. The black weather-stress-cracking-resistant polyethylene cable sheath material is prepared from the following raw materials in parts by weight: 55-75 parts of linear low-density polyethylene , 20-30 parts of high-density polyethylene, 15-20 parts of EVA resin, 10-15 parts of diisononyl phthalate, 8-12 parts of propanediol sebacate polyester, 5-10 parts of epoxidized linseed oil, 10-15 parts of antimony trioxide, 5-10 parts of zinc stannate, 5-10 parts of ,nanometer zeolite powder, 3-5 parts of straw ash, 4-6 parts of a composite filling material, 8-12 parts of nanometer dolomite, 20-30 parts of channel black, 2-3 parts of dibutyltin dilaurate, 1-2 parts of calcium stearate, 1-2 parts of zine stearate, 3-5 parts of oxidized polyethylene wax, 0.5-1 part of antioxidant DLTP and 1-2 parts of antioxidant 1010. The cable material of the invention has excellent performances comprising environment stress cracking resistance, high temperature resistance, oil resistance, cold resistance, acid-base resistance, weathering aging resistance, wear resistance and the like, has good running in a working environment of -40 DEG C to 95 DEG C without deformation and cracking, and is safe, reliable and durable in use.

Description

technical field [0001] The invention relates to a black environmental cracking-resistant polyethylene cable sheath material and a preparation method thereof, belonging to the technical field of cable materials. Background technique [0002] Black polyethylene cable material is made of low-density polyethylene resin, carbon black and other additives, melted and kneaded, and granulated. As a cable sheath material, it not only has excellent dielectric properties, but also has excellent physical and mechanical properties. It is suitable for sheath materials of communication, control, signal and electric cables, and can be laid overhead, buried or underground. However, the existing polyethylene sheath material is easily deformed when subjected to external force or molding process during use, and is easy to crack when contacted with liquid solvent and its vapor state, which limits its application range. Contents of the invention [0003] The object of the present invention is t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08K13/06C08K5/12C08K5/11C08K5/1515C08K3/22C08K3/04C08K3/34C08K3/26H01B3/44
CPCC08K2003/2241C08L23/0815C08K2201/014C08L2203/202C08L2205/035C08L2207/062H01B3/441H01B7/18H01B7/28C08L23/06C08L23/0853C08L67/02C08K13/06C08K5/12C08K5/11C08K5/1515C08K3/2279C08K3/04C08K3/346
Inventor 曹悦煕
Owner 安徽天民电气科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap