Rubber gasket material used for valves, and preparation method thereof

A rubber gasket and valve technology, applied in the field of rubber composite material processing, can solve problems such as low strength, unsatisfactory sealing effect, poor wear resistance, etc., achieve low cost, good sealing performance, and improve process performance.

Active Publication Date: 2014-03-19
蚌埠赛英电子科技发展有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance, and low strength, which are far from meeting the actual requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber gasket material used for valves, and preparation method thereof
  • Rubber gasket material used for valves, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The present invention will be described in detail below through specific examples.

[0010] A rubber gasket material for valves, made of the following raw materials in parts by weight (kg): nitrile rubber 80, EPDM rubber 12, zinc oxide 3, stearic acid 5, sulfur 2, 3, 3'- Disulfonyl hydrazide diphenyl sulfone 4, accelerator M0.5, accelerator TMTD1, aluminum hydroxide 10, zinc stearate 1, glycerol triglyceride 6, magnesium oxide 2, anti-scorch agent CTP1.2, N220 carbon black 15, N351 carbon black 30, modified attapulgite 10;

[0011] The modified attapulgite is made of the following raw materials in parts by weight (kg): attapulgite 20, clay 13, 1,6-hexamethylene diisocyanate 4, tripropylene glycol diacrylate 2, light calcium carbonate 2 , zinc oxide 1, wollastonite powder 3, magnesium hydroxide 10, chlorinated paraffin 1, diatomaceous earth 4, tributyl citrate 2, jade powder 8, pepper seed oil 1; the preparation method is to mix attapulgite, clay , diatomaceous earth m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rubber gasket material used for valves, and a preparation method thereof. The rubber gasket material comprises following raw materials, by weight, 80 to 90 parts of butadiene-acrylonitrile rubber, 12 to 15 parts of ethylene propylene diene monomer, 3 to 7 parts of zinc oxide, 5 to 8 parts of stearic acid, 2 to 5 parts of sulfur, 4 to 6 parts of DPSDSH, 0.5 to 1 part of promoter M, 1 to 2 parts of promoter TMTD, 10 to 12 parts of aluminium hydroxide, 1 to 2 parts of zinc stearate, 6 to 8 parts of glycerol trioleate, 2 to 4 parts of magnesium oxide, 1.2 to 1.4 parts of anti-scorching agent CTP, 15 to 18 parts of N220 carbon black, 30 to 35 parts of N351 carbon black, and 10 to 12 parts of modified attapulgite. According to the rubber gasket material, modified attapulgite is added, so that processing properties of the rubber gasket material are improved; and environmental friendly accessory ingredients are used, so that toxic and side effects are reduced, and pollution on the environment is reduced. Sealing performance of the rubber gasket material is excellent, formula is reasonable, technology is simple, cost is low, and the rubber gasket material possesses excellent aging resistance and corrosion resistance.

Description

technical field [0001] The invention relates to the field of processing rubber composite materials, in particular to a rubber gasket material for valves and a preparation method thereof. Background technique [0002] Gasket is a material used for sealing inside machinery, equipment, pipelines, etc. The gaskets currently used are mostly rubber gaskets, which are characterized by high temperature resistance, ozone resistance, natural aging resistance, vacuum resistance, fuel oil resistance, lubricating oil resistance, strong oxidant resistance, chemical resistance and good electrical insulation performance. Widely used in defense industry and civilian industry. However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance and low strength, which are far from meeting the actual requirements. Therefore researching and developing a kind of high-performance rubber gasket has become the task of top priority. Contents of the invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L23/16C08K13/06C08K9/00C08K9/02C08K3/34C08K5/103C08K3/26C08K3/22C08K5/11
Inventor 胡建强胡巍李丽
Owner 蚌埠赛英电子科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap