Kudzuvine root porous particles and application thereof to cigarettes

A technology of porous particles and kudzu root, which is applied in the application, tobacco, and e-liquid filter elements, etc., can solve the problems of limited harm reduction and coke reduction, unfavorable cigarette composite filter rods, unstable physical properties, etc., and achieves strong operability and standardization , good application prospects, and the effect of improving the effective contact area

Active Publication Date: 2014-04-02
HONGYUN HONGHE TOBACCO (GRP) CO LTD
View PDF5 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cigarette material researchers have developed some filter rod granular materials by using natural plant materials. Some effects have been achieved in cigarette flavoring and harm reduction, but there are still the following disadvantages: (1) The plant material is directly crushed into particles, the shape of the particles is uneven, and the physical properties are unstable. When the granules are easily broken, a large amount of dust is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Take 1 kg of fresh kudzu root, wash and cut it into pieces, dry it at 50°C until the water content is 6%, then crush the raw material into 100-mesh powder, put the prepared kudzu root powder in a Midi Glatt fluidized bed for granulation, and fluidize Bed fluidization pressure is 0.15Bar, air flow temperature is 70°C and dried for 10 minutes; then 8 parts of gelatin, 2 parts of sodium carboxymethyl starch, and distilled water are used to prepare a binder solution with a concentration of 10% and use the top spray method For spraying, the fluidizing pressure is 0.2Bar, the air temperature is 70°C, the spray pressure is 0.15Bar, the spray rate is 10g / min, and the amount of adhesive solution is 380g; after the adhesive is applied, set the fluidizing air pressure to 0.15Bar 1. Dry for 10 minutes at an air temperature of 70° C., adjust the moisture content to 5%, and pass through a 60-mesh sieve to obtain kudzu root porous particles for cigarette filter rods.

Embodiment 2

[0029] Take 0.8 kg of fresh kudzu root, wash and cut into pieces, dry at 60°C until the water content is 5%, then crush the raw material into 120-mesh powder, put the prepared kudzu root powder in a Midi Glatt fluidized bed for granulation, flow The fluidized bed fluidized pressure is 0.12 Bar, and the air temperature is 70 ° C. Dry for 8 minutes; then weigh 5 parts of gelatin and 5 parts of polyvinylpyrrolidone according to parts by weight, and prepare a binder solution with a concentration of 8% with distilled water It is sprayed by top spraying, the fluidization pressure is 0.15Bar, the air temperature is 60℃, the spray pressure is 0.12Bar, the spray rate is 9g / min, and the amount of adhesive solution is 240g; after the adhesive is applied, set the fluidization The air pressure is 0.12 Bar, the air temperature is 70 DEG C and dried for 8 minutes, the moisture content is adjusted to 6%, and the kudzu root porous particles for cigarette filter sticks are obtained by passing th...

Embodiment 3

[0031] Take 0.5kg of fresh kudzu root, wash and cut into pieces, dry at 50°C until the water content is 6%, then pulverize the raw material into 120-mesh powder, put the prepared kudzu root powder in a Midi Glatt fluidized bed for granulation, first The fluidized bed fluidization pressure is 0.12Bar, and the air temperature is 60 °C and dried for 5 minutes; then weigh 1 part of gelatin, 1 part of polyvinylpyrrolidone, and 1 part of sodium carboxymethyl starch in parts by weight, and prepare it with distilled water The adhesive solution with a concentration of 6% is sprayed by top spraying, the fluidization pressure is 0.12 Bar, the air temperature is 80 ° C, the spray pressure is 0.08 Bar, the spray rate is 8 g / min, and the amount of adhesive solution is 180 g; After the agent is applied, set the fluidization pressure to 0.12 Bar and the air temperature to 60°C and dry for 5 minutes, adjust the moisture content to 7%, and pass through a 20-mesh sieve to obtain the kudzu root po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses kudzuvine root porous particles and application thereof to cigarettes. The kudzuvine root porous particles of 20-60 meshes are prepared by taking kudzuvine root powder of which the water content is 5-6 percent and the particle diameter is 100-160 meshes as raw materials and taking one or more of gelatin, polyvinylpyrrolidone and sodium carboxymethyl starch as bonding agents with a fluidized bed top spray process. The particles are rough in surfaces and are large in specific surface areas, the effective contact area between a particle material and cigarette smoke is increased remarkably, and hydrocyanic acid and crotonaldehyde in cigarette smoke can be adsorbed selectively; the irritation of the cigarette smoke is effectively lowered, and remaining taste is improved; meanwhile, the effect of improving the sweet taste of smoke is enhanced. The kudzuvine root porous particles and the application thereof to the cigarettes have the advantages of simple production process, high operability, high standardability, ready availability of raw materials, low cost, convenience in the realization of industrial production and good application prospect.

Description

technical field [0001] The invention belongs to the technical field of cigarette materials, and in particular relates to porous particles of kudzu root that can improve the smoking quality of cigarettes. At the same time, the invention also relates to the application of the porous particle in cigarette processing. Background technique [0002] Pueraria lobata, the tuber of the leguminous plant Pueraria mirifica, is a kind of commonly eaten vegetable in some provinces and regions in southern China. It tastes sweet and cool, and is often used for soup and medicine. The main components in kudzu root are kudzu root starch, kudzu root fiber and kudzu root flavonoids, and the content of isoflavones with anti-cancer and anti-cancer effects such as puerarin and soybean isoflavones is also considerable. Many researchers have analyzed the chemical components of Pueraria lobata, and obtained that the total isoflavone content in Pueraria lobata root is 7.80%, the total amino acid conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A24D3/14
Inventor 王明锋朱保昆廖头根陶鹰王坚刘亚
Owner HONGYUN HONGHE TOBACCO (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap