A high-efficiency marine anti-corrosion coating

A marine anti-corrosion and coating technology, applied in anti-corrosion coatings, anti-fouling/underwater coatings, coatings, etc., can solve problems such as environmental and personal health threats, and achieve high fouling release, high hydrophobicity, and improved adhesion Effect

Active Publication Date: 2016-03-30
QINGDAO ADVANCED MARINE MATERIAL TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the ensuing problem is that the hulls of these large and small ships are all coated with anti-corrosion coatings and anti-fouling coatings that contain harmful substances such as various poisons and heavy metal compounds.
Coatings will release organic solvents during construction, use and curing, which pose a serious threat to the environment and human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-efficiency marine anti-corrosion coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A marine high-efficiency marine anti-corrosion coating, comprising the following raw materials in parts by weight: 25 parts of fluorinated acrylate, 18 parts of silicon rubber, 1.4 parts of zinc phosphate, 0.4 parts of calcium phosphate, 0.4 parts of zinc molybdate, 0.2 parts of calcium molybdate, three Aluminum polyphosphate 0.6 parts, TiO 2 6 parts, ZnO3 parts, CaCO 3 3 parts, SiO 2 9 parts, 0.1 part of chelating agent, 0.1 part of dispersant, 0.1 part of wetting agent.

Embodiment 2

[0014] A marine high-efficiency marine anti-corrosion coating, comprising the following raw materials in parts by weight: 40 parts of fluorinated acrylate, 33 parts of silicone rubber, 5 parts of zinc phosphate, 1 part of calcium phosphate, 1 part of zinc molybdate, 1 part of calcium molybdate, three Aluminum polyphosphate 2 parts, TiO 2 6 parts, ZnO3.6 parts, CaCO 3 6 parts, SiO 2 8.4 parts, 1 part of chelating agent, 1 part of dispersing agent, 1 part of wetting agent.

Embodiment 3

[0016] A marine high-efficiency marine anti-corrosion coating, comprising the following raw materials in parts by weight: 30 parts of fluorinated acrylate, 22 parts of silicone rubber, 5 parts of zinc phosphate, 1 part of calcium phosphate, 1 part of zinc molybdate, 1 part of calcium molybdate, three Aluminum polyphosphate 2 parts, TiO 2 4 parts, ZnO4 parts, CaCO 3 4 parts, SiO 2 6 parts, 0.4 parts of chelating agent, 0.4 parts of dispersing agent, 0.4 parts of wetting agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-efficiency ocean anticorrosive paint, which comprises the following active ingredients in parts by weight: 25-40 parts of fluorinated acrylate, 18-33 parts of silicone rubber, 3-10 parts of antirust pigment, 10-25 parts of filler, 0.1-1 part of chelating agent, 0.1-1 part of dispersing agent, and 0.1-1 part of wetting agent. According to the high-efficiency ocean anticorrosive paint, the silicone rubber and fluorinated acrylate materials have extremely low surface free energy, low friction coefficient, high hydrophobicity and high contamination releasing characteristic, so that the pollution and corrosion coefficients of steel can be lowered; the antirust pigment and filler are nanoscale particles, the nanoparticles and coatings form stronger hydrogen bonding, the compactness and ion permeability resistance of the coatings can be enhanced; through the nanoparticles, the rheological property of the paint can also be improved, and the adhesion force, hardness, finish degree and anti-aging properties of the coatings can be improved.

Description

technical field [0001] The invention relates to an anti-corrosion coating, in particular to a high-efficiency marine anti-corrosion coating, which belongs to the technical field of coatings. Background technique [0002] Seawater is the largest and highly corrosive natural electrolyte in nature. Seawater contains almost all chemical elements on the earth, and its composition is very complex. In addition, seawater also contains dissolved oxygen, marine life and decaying organic matter. These substances have caused great harm to metal components such as various marine transportation tools, oil production platforms, and marine equipment. With the development of coastal transportation, industrial production, and national defense construction in various countries, the threat of seawater and marine atmospheric corrosion has also become more and more serious. The more prominent, the more applicable and economical marine engineering protection method is to apply marine coatings tha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/02C09D4/06C09D5/16C09D5/08
Inventor 刘连河王强张茂伟
Owner QINGDAO ADVANCED MARINE MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products