Modified sepiolite used for a polyethylene corrugated pipe material and a preparing method of the modified sepiolite

A corrugated pipe and sepiolite technology, which is applied in the field of modified sepiolite for polyethylene corrugated pipe materials and its preparation, can solve the problems of difficult sepiolite dispersion, easy layering, and much dust, and improve the dispersion performance , Improve mechanical strength, solve the effect of difficult dispersion

Inactive Publication Date: 2014-10-29
HEFEI HEAN MACHINERY MFG
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a modified sepiolite for polyethylene corrugated pipe material and its preparation method, which solves the problems of difficult sepiolite dispersion, easy delamination, and much dust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] A modified sepiolite for polyethylene corrugated pipe material, made of the following raw materials in weight (kg): sepiolite 95, nanometer zirconia 15, shell powder 22, perfluoroalkyl ethyl acrylate 6, Buty fatty acid 3, glucose pentaacetate 12, dammar resin 10, shellac 8, walnut shell powder 7, ozokerite 5, distearyl dimethyl ammonium chloride 1.5, polybutylene terephthalate 45. Ethylene-vinyl alcohol copolymer 30, polydibromophenylene ether 10, calcium hypophosphite 8, zinc laurate 2.5, additive 6;

[0011] The preparation method of described auxiliary agent is as follows: a, get the raw material of following weight (kg): tri-tert-butylphosphine tetrafluoroborate 4, aluminum triacetylacetonate 3, stearyl methacrylate 7, hexamethylenetetramine 3. Lingkite 10, dicyclopentadiene 6, zinc p-toluene sulfinate 2, waste glass powder 10, bamboo charcoal powder 10, mannide monooleate 2.5, tetramethyltetravinyl cyclotetra Siloxane 1.5, bisphenol s1, N-phenylmaleimide 2; b, mag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Modified sepiolite used for a polyethylene corrugated pipe material and a preparing method of the modified sepiolite are disclosed. The modified sepiolite is prepared from following raw materials by weight: 85-105 parts of sepiolite, 10-15 parts of nanometer zirconium dioxide, 18-26 parts of shell powder, 4-7 parts of perfluoro alkyl ethyl acrylate, 2-5 parts of tallow fatty acid, 9-16 parts of glucose pentaacetate, 10-15 parts of gum dammar, 6-12 parts of shellac, 5-10 parts of walnut shell powder, 4-8 parts of ozokerite, 1-2 parts of distearyl dimethyl ammonium chloride, 40-50 parts of polybutylene terephthalate, 25-35 parts of an ethylene-ethenol copolymer, 10-15 parts of polybrominated diphenyl ethers, 5-10 parts of calcium hypophosphite, 2-3 parts of zinc laurate and 5-7 parts of auxiliary agents. The modified sepiolite and the method can significantly improve the dispersing property of the sepiolite in a polyethylene base material, intensifying adhesion of sepiolite-polyethylene interfaces, effective overcome problems that are hard dispersion, easy layering, much dust, and the like of the sepiolite at present, and improve mechanical strength, wear resistance, fatigue resistance, elasticity, machinability, and other properties of the polyethylene material.

Description

technical field [0001] The invention relates to a modified sepiolite for polyethylene corrugated pipe material and a preparation method thereof, belonging to the technical field of inorganic fillers. Background technique [0002] Sepiolite is a kind of natural magnesium silicate containing water, porous, high specific area and fibrous structure. Because of its high aspect ratio, large specific surface area and good thermal stability, it is used as a A new inorganic semi-reinforcing filler has been widely used in the plastics industry. However, in the filling process of polyethylene materials, traditional sepiolite is often prone to uneven dispersion, layering, and excessive dust during production and construction, which limits its application in the field of polyethylene materials. To further improve its performance and broaden its application field, sepiolite must be modified. Contents of the invention [0003] The purpose of the present invention is to provide a modifi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L67/02C08L23/08C08K13/06C08K9/02C08K9/04C08K7/26
CPCC08L67/02C08K2201/011C08L23/06C08L2203/18C08L2205/035
Inventor 杨月琴杨晓伟郑海波武子静万丽丽沈先明牛保余海飞杨辉
Owner HEFEI HEAN MACHINERY MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products