A kind of anti-crack thermal insulation mortar and preparation method thereof

A technology for thermal insulation mortar and raw materials, applied in the field of building materials, can solve problems such as affecting the use and different performance and quality of mortar, and achieve the effects of improving compression resistance, outstanding thermal insulation and energy saving effect, and excellent crack resistance performance.

Active Publication Date: 2015-12-30
长治市中宝建材股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the performance and quality of mortar are different, which affects the use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A crack-resistant thermal insulation mortar, made of the following raw materials in parts by weight: aluminum sulfate 5, alum 3, charcoal 16, perlite 240, pitch rock 23, obsidian 36, coal slime 35, fly ash 40, urea 3.5 , Potassium dihydrogen phosphate 4, cement 190, sepiolite wool 45, sand 110, appropriate amount of water, additive 23;

[0016] The auxiliary agent is made of the following raw materials in parts by weight (kg): polyisobutylene 1.1, stainless steel fiber 6.5, acetylene carbon black 2.5, lead isooctanoate 0.5, dipentaerythritol hexaacrylate 4.5, methyl methacrylate 2.5, amino resin 1. Organic bentonite 1.2, tartaric acid 0.7, magnesium borate whiskers 1.5, fumed aluminum oxide 1.5, epoxy acrylate 3.5, polytetrafluoroethylene micropowder 2.5, peppermint oil 0.4, sodium dodecylbenzene sulfonate 0.2, over Ammonium sulfate 0.1, potassium persulfate 0.1, water 16; the preparation method is: water, sodium dodecylbenzene sulfonate, dipentaerythritol hexaacrylate,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses anti-cracking thermal insulation mortar. The anti-cracking thermal insulation mortar is prepared from the following raw materials in parts by weight: 4-6 parts of aluminum sulfate, 2-4 parts of alum, 14-17 parts of wood charcoal, 230-250 parts of perlite, 20-25 parts of pitchstone, 34-38 parts of obsidian, 30-40 parts of coal slime, 30-50 parts of coal ash, 3-4 parts of urea, 3-5 parts of monopotassium phosphate, 180-200 parts of cement, 40-50 parts of sepiolite fabric, 100-120 parts of sand, a proper amount of water and 20-25 parts of auxiliaries. The mortar has the advantages of good adhesiveness, water-retaining property and thermal-insulation and heat-insulation performance, outstanding thermal-insulation energy-saving effects, and further has excellent anti-cracking performance by use of the sepiolite fabric, is suitable for masonry and plastering construction of a wall material. By use of the auxiliaries adopted by the anti-cracking thermal insulation mortar, the compressive strength and the breaking strength of the mortar are improved, and the peaceability, the flow sagging resistance, the thixotropy and the settling resistance of the mortar are improved.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a crack-resistant thermal insulation mortar and a preparation method thereof. Background technique [0002] Mortar is a common material for construction and is an essential material in construction. According to performance, mortar can be divided into many types, such as combined mortar, caulking mortar, thermal insulation mortar, etc.; [0003] At present, the performance and quality of mortar are different, which affects the use. Specifically, the factors that affect the performance of mortar include the workability, fluidity, water retention of freshly mixed mortar, and the strength of hardened mortar. New mortars need to be researched to have excellent construction and processability, sag resistance, thixotropy, anti-settling properties, storage stability, improved pumpability and shear thinning, and new materials need to be found , in order to improve its per...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00
Inventor 朱兴堂朱亮亮陈军彦
Owner 长治市中宝建材股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap