Manufacturing process for silver zinc oxide copper oxide electrical contact and electrical contact product

A silver zinc oxide, manufacturing process technology, applied in the direction of contacts, circuits, electrical switches, etc., can solve the problems of unsatisfactory effect and service life, large surface contact resistance, low material utilization rate, etc., and achieve good arc extinguishing The effect of performance, low surface contact resistance, and high material utilization

Inactive Publication Date: 2014-12-10
张树堂
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many production links, long production cycle, low production efficiency, high production cost, and low material utilization rate (only 38% to 54%)
The reciprocating turnover of materials brings more impurity components to the contact base, pollutes the contact base, and seriously affects its performance
Unable to achieve the expected effect and service life
However, the silver zinc oxide contacts used in the current low-voltage electrical equipment generally have the disadvantages of high temperature and large surface contact resistance, and the safety is threatened by fusible welding.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1. According to the mass ratio of components: zinc: 5%; copper: 1.5%; yttrium: 0.03%; the balance is silver. The ingots are melted to form silver-zinc-copper alloy ingots.

[0032] 2. The silver-zinc-copper alloy ingot is heated and extruded into a wire, and then drawn to a wire with a diameter of φ1.5mm.

[0033] 3. On the cold heading machine, the wire material of 2 and the silver wire are cut into small sections with suitable lengths by the cold heading machine and made into a sheet contact product of φ3㎜×0.8㎜.

[0034] 4. Pour the contact product of 3 into an argon electric furnace in a vacuum state of 480°C for diffusion annealing for 60 minutes, and then cool down to 80°C with the furnace to take out the product.

[0035] 5. Put the product of 4 into an electric furnace with an oxygen flow pressure of 1.2 Mpa, firstly oxidize at 620°C for 6 hours, and then heat up to 700°C for 6 hours with the furnace. The finished electric contact is obtained after being cooled...

Embodiment 2

[0037] 1. According to the mass ratio of components: zinc: 7%; copper: 3%; yttrium: 0.05%; the balance is silver. The ingots are melted to form silver-zinc-copper alloy ingots.

[0038] 2. The silver-zinc-copper alloy ingot is heated and extruded into a wire, and then drawn to a wire with a diameter of φ2.5mm.

[0039] 3. On the cold heading machine, the wire material of 2 and the silver wire are cut into small sections with suitable lengths by the cold heading machine and made into a sheet contact product of φ5㎜×1.3㎜.

[0040] 4. Pour the contact product of 3 into an argon electric furnace for 90 minutes in a vacuum state of 500°C for diffusion annealing, and then cool down to 80°C with the furnace to take out the product.

[0041] 5. Put the product of 4 into an electric furnace with an oxygen flow pressure of 1.2 Mpa, firstly oxidize at 630°C for 18 hours, and then heat up to 710°C for 16 hours with the furnace. The finished electric contact is obtained after being cooled...

Embodiment 3

[0043] 1. According to the mass ratio of components: zinc: 8%; copper: 4%; cerium: 0.02%; the balance is silver. The ingots are melted to form silver-zinc-copper alloy ingots.

[0044] 2. The silver-zinc-copper alloy ingot is heated and extruded into a wire, and then drawn to a wire with a diameter of φ3mm.

[0045] 3. On the cold heading machine, the wire material of 2 and the silver wire are cut into small sections with suitable lengths by the cold heading machine and made into a sheet contact product of φ6㎜×1.5㎜.

[0046] 4. Pour the contact product of 3 into an argon electric furnace for 90 minutes in a vacuum state of 520°C for diffusion annealing, and then cool down to 80°C with the furnace to take out the product.

[0047] 5. Put the product of 4 into an electric furnace with an oxygen flow pressure of 1.2 Mpa, firstly oxidize at 630°C for 22 hours, and then heat up to 720°C for 20 hours with the furnace. The finished electric contact is obtained after being cooled to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing process for a silver zinc oxide copper oxide electrical contact and an electrical contact product. In the manufacturing process, the electrical contact product is manufactured through smelting, ingot casting, hot extrusion, drawing into ally wires, forming of required specification of sheet through cold heading, then diffusion annealing and oxidation treatment. The electrical contact product produced by adopting the preparation method is characterized in that the electrical contact product is low in surface contact resistance, good in electrical property and arc extinguishing performance, high in welding resistance and good in combination property. The processing method is simple, the material utilization rate is high, the detrimental impurity is few, the production cost is low, and the production cycle is low. The economic benefit and social benefit are particularly obvious.

Description

technical field [0001] The invention belongs to the technical field of electric contact manufacturing, and specifically refers to a manufacturing process and a product of a silver-zinc-oxide-copper-oxide electric contact. Background technique [0002] In low-voltage electrical equipment, the electrical contacts, which are the core components of electrical appliances, carry the heavy task of connecting and breaking currents. It is an important guarantee to ensure the safe operation of equipment and the safety of people's lives and property. [0003] At present, the production process of electrical contacts is nothing more than two major types of production: powder metallurgy and alloy internal oxidation. Most of the contact manufacturers continue to use the alloy internal oxidation method to produce electrical contact products. The production link of the method is realized by processes such as smelting, ingot casting, surface treatment, hot-rolled welding cladding, cold-rol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01H11/04H01H1/023C22F1/14B23P15/00
Inventor 张树堂郑晓杰唐艳华
Owner 张树堂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap