Degreasing agent for stainless steel, carbon steel and petrochemical pipelines
A petrochemical and degreasing agent technology, applied in the field of chemical product preparation, can solve the problems of poor degreasing performance, physical harm to operators, poor high temperature performance, etc., and achieves green and environmentally friendly raw material sources, reduces physical harm, and has high degreasing efficiency. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0013] Example 1
[0014] Weigh 100g of sodium hydroxide, 40g of sodium gluconate, 20g of open powder, 30g of p-toluenesulfonic acid, and APG-081050g of alkyl glycoside. First dissolve sodium hydroxide in 760mL of water, then add sodium gluconate, open powder and P-toluenesulfonic acid is dissolved in sodium hydroxide solution, cooled to room temperature and packaged, and the product is ready. Dilute the degreaser product in Example 1 into 1000 mL of 10% aqueous solution, soak DN30 carbon steel or stainless steel elbows pickled with hydrochloric acid at room temperature for 30 minutes, take out the elbows, rinse with pure water, and then use oil-free dry air Blow dry, soak the dried elbow with 1000mL carbon tetrachloride for 10 minutes, and then determine the oil content of carbon tetrachloride to be 10mg / L, which is far better than the currently used degreasing agent (60g sodium hydroxide, 40g sodium carbonate, Base phenol polyoxyethylene ether OP-1020g, 880mL water compound, t...
Example Embodiment
[0015] Example 2
[0016] Weigh 150g of sodium hydroxide, 30g of powder, APG-081080g of alkyl glycoside, 70g of p-toluenesulfonic acid, and 80g of sodium gluconate. First dissolve sodium hydroxide in 590mL of water, then remove powder and p-benzyl. Sulfonic acid, APG-0810 and sodium gluconate are dissolved in sodium hydroxide solution, cooled to room temperature and packaged, ready to be a product. Dilute the degreaser product in Example 2 into 1000 mL of 10% aqueous solution, soak the DN30 carbon steel or stainless steel elbows pickled with hydrochloric acid at room temperature for 30 minutes, take out the elbows, rinse with pure water, and then use oil-free dry air Blow dry, soak the dried elbow with 1000mL carbon tetrachloride for 10 minutes, and then determine the oil content of carbon tetrachloride to be 8mg / L, which is far better than the oil content measured by the same method for the currently used degreasing agent.
Example Embodiment
[0017] Example 3
[0018] Weigh 100g of sodium hydroxide, APG-081050g of alkyl glycoside, 30g of powder, 65g of p-toluenesulfonic acid, 70g of sodium gluconate, first dissolve sodium hydroxide in 685mL water, and then add alkyl glycoside APG-0810, The powder, p-toluenesulfonic acid and sodium gluconate are dissolved in sodium hydroxide solution, cooled to room temperature and packaged, and the product is ready. Dilute the degreaser product in Example 3 into 1000 mL of 10% aqueous solution, soak DN30 carbon steel or stainless steel elbows pickled with hydrochloric acid at room temperature for 30 minutes, take out the elbows, rinse with pure water, and then use oil-free dry air Blow dry, soak the dried elbow with 1000mL carbon tetrachloride for 10 minutes, and then determine the oil content of carbon tetrachloride to be 15mg / L, which is far better than the oil content measured by the same method for the currently used degreasing agent.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap