Polyvinyl chloride Grade-A flame-retardant fireproof silencing wear-resistant wood-plastic floor material

A technology for polyvinyl chloride and wood-plastic flooring, which is applied in the field of interior decoration materials, can solve problems such as the inability to achieve fire resistance, and achieve the effects of good dimensional stability, low price, and good compression creep resistance.

Inactive Publication Date: 2015-05-06
SHENDUN FIREPROOF TECH
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] It can be seen that once the above-mentioned wood-plastic floor encounters a fire, its fireproof ability cannot reach the A-level fireproof standard of GB 50222-95 "National Standard of the People's Republic of China on Fire Protection Design of Building Interior Decoration"

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The preparation of embodiment 1 flame-retardant polyether

[0050] An arc generator is set in a 2-meter-high, cylindrical airtight reaction vessel, and a microwave generator is set at a height of 1.5m on the wall of the reactor. Before the reaction starts, the container is filled with nitrogen and carbon dioxide (volume ratio 100:1.5) after vacuuming, so that the pressure in the container is 75MPa.

[0051] The catalyst is a mixture of 0.6 parts by mass of methanol, 0.5 parts by mass of silicone oil, 0.3 parts by mass of sodium silicate, and 0.1 parts by mass of sodium bicarbonate.

[0052] Rare earth fluoride (purchased from Yixing Xinweilicheng Rare Earth Co., Ltd., 2000 mesh) with mass parts of 1, 0.5, 1.5, and 1.5, butylene oxide, catalyst, and polytetrafluoroethylene at a temperature of 560 ° C and a pressure It is obtained after 3 hours of reaction under the reaction conditions of 75MPa, voltage of 15,000 volts, and microwave frequency of 100GHz.

Embodiment 2

[0053] Preparation of embodiment 2 flame retardant polyether

[0054] Equipment and pressure control are the same as in Example 1.

[0055] The catalyst is a mixture of 0.7 parts by mass of methanol, 0.6 parts by mass of silicone oil, 0.5 parts by mass of sodium silicate, and 0.2 parts by mass of sodium bicarbonate.

[0056] Rare earth fluoride (purchased from Yixing Xinweilicheng Rare Earth Co., Ltd., 2000 mesh) with mass parts of 1, 0.5, 2.0, and 1.5, butylene oxide, catalyst, and polytetrafluoroethylene at a temperature of 550 ° C and a pressure It is obtained after 3 hours of reaction under the reaction conditions of 75MPa, voltage of 15,000 volts, and microwave frequency of 100GHz.

Embodiment 3

[0057] The preparation of embodiment 3 flame-retardant polyether

[0058] Equipment and pressure control are the same as in Example 1.

[0059] Catalyst is with embodiment 2. The mass parts are respectively 1, 0.5, 2.0, 1.5 lanthanum fluoride (purchased from Yixing Xinweilicheng Rare Earth Co., Ltd.), butylene oxide, catalyst, and polytetrafluoroethylene at a temperature of 550 ° C and a pressure of 75 MPa. Under the reaction conditions of a voltage of 15,000 volts and a microwave frequency of 100 GHz, it was obtained after 3 hours of reaction.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
oxygen indexaaaaaaaaaa
oxygen indexaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a polyvinyl chloride Grade-A flame-retardant fireproof silencing wear-resistant wood-plastic floor material which is prepared from the following raw materials in parts by weight: 60-80 parts of polyvinyl chloride, 3-5 parts of melamine, 30-40 parts of wood meal, 1.1-2.2 parts of molybdenum trioxide, 8-11 parts of tetrabromobisphenol A, 0.5-1.0 part of ferrocene, 13-27 parts of hexabromocyclododecane, 2-5 parts of plasticizer, 10-22 parts of zinc borate, 2-5 parts of cosolvent, 20-40 parts of hydroxide, 0.6-1.8 parts of color master batch, 10-15 parts of flame-retardant polyether, 30-60 parts of calcium carbonate, 5-10 parts of sodium carbonate, 5-9 parts of ammonium polyphosphate, 10-20 parts of hollow glass microsphere and 5-9 parts of high-pressure polyethylene. The polyvinyl chloride Grade-A flame-retardant fireproof silencing wear-resistant wood-plastic floor material satisfies Grade A in Chinese National Standard Code for Fire Prevention in Design of Interior Decoration of Building GB5022-95.

Description

technical field [0001] The invention relates to the field of interior decoration materials, in particular to a class A polyvinyl chloride flame-retardant, fire-proof, sound-absorbing and wear-resistant wood-plastic floor material. Background technique [0002] Wood-plastic flooring is a new type of environmentally friendly wood-plastic composite material product. The wood powder produced during the production of medium and high-density fiberboards is added to recycled plastics to make wood-plastic composite materials through granulation equipment, and then extruded into production groups. Made into wood-plastic flooring. The main material of wood-plastic outdoor flooring is polyvinyl chloride and wood powder or bamboo powder. After adding additives, mixing at high speed, granulating, and then using an extruder to extrude the pellets into molding materials, this type of floor can be used for garden landscape , villas and other outdoor platforms. The national standard for wo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08L71/02C08L23/06C08K13/04C08K7/28C08K3/22C08K5/136C08K3/38C08K3/26C08K3/32
CPCC08L27/06C08G65/323C08K2201/014C08L2201/02C08L2205/035C08L97/02C08L71/02C08L23/06C08K13/04C08K7/28C08K2003/2255C08K5/136C08K3/38C08K2003/265C08K2003/262C08K2003/323C08K5/12C08K5/34922C08K2003/2227C08K2003/2224C08K5/1515
Inventor 杨京学任海龙宫连仲杨继彬宫怀叡
Owner SHENDUN FIREPROOF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com