Rubber layer material of drill hoses

A technology for drilling rubber hose and rubber layer is applied in the field of rubber layer material for drilling rubber hose, which can solve the problems of deliquescence rubber medium dispersion performance, unbright color of products, insufficient color development of pigments, etc., and achieves increased stability and superior aging resistance. , the effect of good strength

Inactive Publication Date: 2015-06-24
青岛新动力文化传媒有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, the rubber material of the drilling hose has the following problems: the storage stability is poor, the color of the product is not bright, and the pigment will not only deliquesce after being eroded by water. What's more serious is that the dispersion performance in the rubber medium is poor, which leads to insufficient color development of the pigment in the product. The main reason for this is the selection of liquid paraffin, which can easily absorb moisture in the air.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A rubber layer material for drilling rubber hose is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0018] 50 parts of natural rubber latex, 10 parts of cross-linked starch, 0.3 parts of accelerator TMTD, 3 parts of sulfur, 0.6 parts of calcium stearate, 1 part of zinc oxide, 1 part of anti-aging agent, silicon oxide, calcium carbonate and silicon carbide according to 3 parts of nanomaterials with a weight ratio of 2:1:1, 3 parts of white carbon black, 0.4 parts of titanium dioxide, 0.2 parts of octadecyl imidazoline, 2 parts of clay, naphthenic oil and engine oil according to the composition of 2:1 0.4 parts of wetting agent, 0.2 parts of azo condensation pigment or phthalocyanine pigment.

Embodiment 2

[0020] A rubber layer material for drilling rubber hose is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0021] 55 parts of natural rubber latex, 11 parts of cross-linked starch, 0.4 parts of accelerator TMTD, 4 parts of sulfur, 0.7 parts of calcium stearate, 1.5 parts of zinc oxide, 1.5 parts of anti-aging agent, silicon oxide, calcium carbonate and silicon carbide according to 3.5 parts of nanomaterials, 4 parts of white carbon black, 0.5 parts of titanium dioxide, 0.2 parts of octadecyl imidazoline, 3 parts of clay, naphthenic oil and engine oil in a weight ratio of 2:1:1 0.5 parts of wetting agent, 0.3 parts of azo condensation pigment or phthalocyanine pigment.

Embodiment 3

[0023] A rubber layer material for drilling rubber hose is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0024] 60 parts of natural rubber latex, 12 parts of cross-linked starch, 0.5 parts of accelerator TMTD, 5 parts of sulfur, 0.8 parts of calcium stearate, 2 parts of zinc oxide, 2 parts of anti-aging agent, silicon oxide, calcium carbonate and silicon carbide by weight 4 parts of nanomaterials with a ratio of 2:1:1, 5 parts of white carbon black, 0.6 parts of titanium dioxide, 0.3 parts of octadecyl imidazoline, 4 parts of clay, naphthenic oil and engine oil according to the composition of 2:1 0.6 parts of wetting agent, 0.4 parts of azo condensation pigment or phthalocyanine pigment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber layer material of drill hoses. The rubber layer material is characterized in comprising following ingredients, by weight, 50 to 60 parts of natural rubber latex, 10 to 12 parts of crosslinked starch, 0.3 to 0.5 part of promoter TMTD, 3 to 5 parts of sulphur, 0.6 to 0.8 part of calcium stearate, 1 to 2 parts of zinc oxide, 1 to 2 parts of an anti-aging agent, 3 to 4 parts of a nano material, 3 to 5 parts of white carbon black, 0.4 to 0.6 part of titanium dioxide, 0.2 to 0.3 part of octadecyl imidazoline, 2 to 4 parts of argil, 0.4 to 0.6 part of a wetting agent, and 0.2 to 0.4 part of an organic pigment. Stability of the rubber layer material is improved; the rubber layer material possesses relatively excellent strength, extensibility, organic solvent corrosion resistance, and aging resistance, and is long in service life, and wide in application range.

Description

technical field [0001] The invention belongs to the technical field of rubber materials, and in particular relates to a rubber layer material of a drilling rubber hose. Background technique [0002] The chemical properties of natural rubber Natural rubber is unsaturated rubber, which is easy to undergo vulcanization reaction (structural reaction) with vulcanizing agent, oxidation and cracking reaction between bromine and oxygen, ozone, chlorination reaction with halogen, and occurs under the action of catalyst and acid chemical reaction etc. However, since natural rubber is a polymer compound, it has the reaction characteristics of olefinic organic compounds, such as slow reaction speed, incomplete and uneven reaction, and the phenomenon of coexistence of various chemical reactions (such as oxidative cracking reaction and structuring reaction) )Wait. [0003] Natural rubber has excellent comprehensive physical and mechanical properties Natural rubber has good elasticity at...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08L3/00C08K13/02C08K3/06C08K5/098C08K3/22C08K3/36C08K3/34
CPCC08K2003/2241C08L7/02C08K2201/011C08K2201/014C08L2201/08C08L2203/18C08L2205/025C08L2205/035
Inventor 宋修训
Owner 青岛新动力文化传媒有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products