A titanium-niobium-zirconium-based hydroxyapatite and composite material technology, applied in medical science, prostheses, etc., can solve the problems of low compressive strength, easy peeling off of the coating, long-term biological stability, poor elastic modulus, etc., and achieve extreme Effects of high density, short sintering time, and low elastic modulus

Active Publication Date: 2017-09-26
KUNMING UNIV OF SCI & TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to solve the problems existing in the existing titanium and titanium alloy-based hydroxyapatite composite materials, such as the coating is easy to fall off and the long-term biological stability is poor, and the elastic modulus of the composite material prepared by mixing titanium alloy / ceramic is high, Low compressive strength, etc., provides a preparation method of titanium-niobium-zirconium-based hydroxyapatite biocomposite material, the obtained biocomposite material has the advantages of uniform composition and structure, low elastic modulus, good biological activity, etc., and can be used as artificial Bone tissue repair or replacement material application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of titanium-niobium-zirconium-based hydroxyapatite biocomposite material
  • A kind of preparation method of titanium-niobium-zirconium-based hydroxyapatite biocomposite material
  • A kind of preparation method of titanium-niobium-zirconium-based hydroxyapatite biocomposite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) According to the mass percentage (wt%) of Ti 65%, Nb 30%, and Zr 5%, respectively weigh Ti, Nb, and Zr metal powders with a purity of 99.5%, 99.95%, and 99% and a particle size of 45 μm ;Put the powder into a ball mill jar for mechanical alloying. During the ball milling process, the ball milling medium is stainless steel balls, the ball-to-material ratio is 3:1, sealed with alcohol and then vacuumed to 30Pa, and then ball milled for 7 hours, the obtained metal mixed powder is still placed in alcohol for later use.

[0023] (2) According to 15% of the mass of the mixed metal powder obtained in step (1), weigh the hydroxyapatite powder with a purity of 97% and a particle size of 100nm, add it to the mixed metal powder for ball milling, seal it with alcohol and pump it. Vacuum at 20Pa, mix for 1.5h, and then dry in a vacuum oven at 40°C to obtain mixed powder.

[0024] (3) Put the mixed powder obtained in step (2) into a graphite mold, then put it into a spark plasma...

Embodiment 2

[0027] (1) According to the mass percentage (wt%) of T60%, Nb 34%, and Zr 6%, respectively weigh Ti, Nb, and Zr metal powders with a purity of 99.5%, 99.95%, and 99%, and a particle size of 25 μm; The powder is put into a ball mill jar for mechanical alloying. During the ball milling process, the ball milling medium is stainless steel balls, the ball-to-material ratio is 3:1, sealed with alcohol and then vacuumed to 30Pa, and then ball milled for 8 hours, the obtained metal mixed powder is still placed in alcohol for later use.

[0028] (2) According to 20% of the mass of the mixed metal powder obtained in step (1), weigh hydroxyapatite powder with a purity of 97% and a particle size of 10 μm, add it to the mixed metal powder for ball milling, seal it with alcohol and pump it Vacuum at 25 Pa, mix for 2 h, and then dry in a vacuum oven at 40°C to obtain a mixed powder.

[0029] (3) Put the mixed powder obtained in step (2) into a graphite mold, then put it into a spark plasma ...

Embodiment 3

[0032] (1) According to the mass percentage (wt%) of Ti 67%, Nb 29%, and Zr 4%, respectively weigh Ti, Nb, and Zr metal powders with a purity of 99.5%, 99.95%, and 99%, and a particle size of 30 μm ;Put the powder into a ball mill jar for mechanical alloying. During the ball milling process, the ball milling medium is stainless steel balls, the ball-to-material ratio is 4:1, sealed with alcohol and then vacuumed to 25Pa, and then ball milled for 6 hours, the obtained metal mixed powder is still placed in alcohol for later use.

[0033] (2) According to 10% of the mass of the mixed metal powder obtained in step (1), weigh hydroxyapatite powder with a purity of 97% and a particle size of 20nm, add it to the mixed metal powder for ball milling, seal it with alcohol and pump it Vacuum at 30Pa, mix for 1 h, and then dry in a vacuum oven at 40°C to obtain a mixed powder.

[0034] (3) Put the mixed powder obtained in step (2) into a graphite mold, then put it into a spark plasma sin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a titanium-niobium-zirconium-based hydroxyapatite biocomposite material, which belongs to the field of biomaterial preparation. The composite material prepared by the invention adopts the titanium-niobium-zirconium alloy as a matrix, and the hydroxyapatite is bioceramics; the mass of the hydroxyapatite is 10-25% of that of the titanium alloy. Its preparation process is as follows: put hydroxyapatite and titanium alloy powder into a ball mill jar, seal it with alcohol and evacuate to 20-30Pa, and dry it in a vacuum drying oven after ball milling for 6-8 hours; put the dried powder into Graphite molds are formed by cold pressing, and finally spark plasma sintering is used. During the sintering process, the sintering temperature is controlled at 1100°C~1200°C, and the temperature is first heated to 1000°C at a heating rate of 100°C / min, and then heated to 25~50°C / min. The sintering temperature is kept warm, the holding time is 6-10min, and the pressure is 50-60MPa; the biocomposite material prepared by the present invention has an elastic modulus of 25.4-45GPa, and has both excellent mechanical properties and biocompatibility; the method of the present invention is simple in process , Low preparation cost.

Description

technical field [0001] The invention relates to a method for preparing a titanium-niobium-zirconium-based hydroxyapatite biocomposite material, in particular to a method for preparing a titanium alloy-based hydroxyapatite biocomposite material by using spark plasma sintering technology, which belongs to the technical field of biomedical material preparation . Background technique [0002] Titanium niobium zirconium biomedical titanium alloys such as Ti-34Nb-6Zr, Ti-30Nb-5Zr-5Ta, Ti-29Nb-4.6Zr-13Ta, etc. have low elastic modulus, high specific strength, good wear resistance and corrosion resistance and biological Compatibility and other advantages, it is one of the most promising new materials for human body replacement and repair. However, biomedical titanium alloy is an inert material with no biological activity on the surface and lack of active repair function. After implanted in the human body, the surface of the titanium alloy and the body tissue are simply interlocked ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/42A61L27/50C22C1/05
Inventor 张玉勤何正员何远怀蒋业华周荣
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com