Catalyst for preparing p-xylene through benzene and methanol alkylation and preparation method of catalyst

A technology for para-xylene and fluidized bed catalyst, which is applied in physical/chemical process catalysts, molecular sieve catalysts, chemical instruments and methods, etc., can solve the problems of complicated catalyst preparation steps, low xylene selectivity, and low benzene conversion rate. , to achieve the effects of high stability, lower production costs, and higher yield per pass

Active Publication Date: 2016-01-06
陕西煤化工技术工程中心有限公司
View PDF12 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The problem to be solved by the present invention is that in the past literature, benzene and methyl alcohol alkylation catalyst benzene conversion rate is low, p-xylene selectivity in xylene isomers is low, The catalyst preparation steps are cumbersome and the problem of poor stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for preparing p-xylene through benzene and methanol alkylation and preparation method of catalyst
  • Catalyst for preparing p-xylene through benzene and methanol alkylation and preparation method of catalyst
  • Catalyst for preparing p-xylene through benzene and methanol alkylation and preparation method of catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 3Kg hydrogen ZSM-5 (SiO 2 / Al 2 o 3 =25, particle size 1-4μm) molecular sieve, 4Kg kaolin, 2Kg silica sol, add appropriate amount of water, stir evenly, spray dry and shape, roast at 600℃ for 3h, record as raw powder A.

[0032] Take 0.9Kg tetraethyl orthosilicate to make ethanol solution, impregnate in raw powder A, and dry to get raw powder A-I; make 0.1KgMgO (precursor is magnesium nitrate hexahydrate) into aqueous solution, dip in the roasted raw powder A-I, the original powder A-II is obtained after drying. The catalyst BTPX-01 was obtained after the raw powder A-II was roasted.

Embodiment 2

[0034] 3.5Kg hydrogen ZSM-5 (SiO 2 / Al 2 o 3 =150, particle size 20-500nm) molecular sieve, 1.5Kg pseudoboehmite, 0.5Kg alumina sol, 2Kg kaolin, add appropriate amount of water, stir evenly, spray dry and shape, roast at 600°C for 3h, record as raw powder B.

[0035] Take 2Kg tetraethyl orthosilicate to prepare ethanol solution, impregnate in raw powder B, and dry to obtain raw powder B-I; make 0.5KgCaO (precursor is calcium nitrate tetrahydrate) into an aqueous solution, impregnate in raw powder B-I, after drying Obtain the original powder B-II. The catalyst BTPX-02 was obtained after the raw powder B-II was roasted.

Embodiment 3

[0037] 1.5Kg sodium ZSM-5 (SiO 2 / Al 2 o 3 =25, particle size 1-4μm) molecular sieve, 3Kg pseudo-boehmite, 3Kg silica, 1.5Kg aluminum sol, add appropriate amount of water, stir evenly, spray dry and shape, roast at 600°C for 3h, record as raw powder C.

[0038]Make 0.01KgMgO (the precursor is magnesium chloride) into an aqueous solution, impregnate it in Kg raw powder C, and dry it to obtain raw powder C-I; take 0.99Kg tetrabutyl orthosilicate to make an ethanol solution, and dip it in the roasted raw powder C-I, After drying, the original powder C-II was obtained. The catalyst BTPX-03 was obtained after the raw powder C-II was calcined.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a fluidized bed catalyst for preparing p-xylene through benzene and methanol alkylation in a high selectivity way and a preparation method of the fluidized bed catalyst. The fluidized bed catalyst is prepared from an active ingredient, a substrate material, a bonding agent and modified ingredients, wherein the active ingredient is a sodium type or hydrogen type ZSM-5 molecular sieve; the modified ingredients are a silicone alkyl compound and alkaline earth metal. The active ingredient, the substrate material and the bonding agent are mixed and sprayed for formation; then, the modified ingredients are used for modification to prepare the fluidized bed catalyst; or the active ingredient is modified by the modified ingredients at first, and is then mixed with the substrate material and the bonding agent for spraying to prepare the fluidized bed catalyst. The fluidized bed catalyst is used for benzene and methanol alkylation reaction; the single-pass conversion rate of the benzene reaches a value higher than 55 percent; the isomerization process is not needed; the obtained major product is the p-xylene; the selectivity of the p-xylene in the isomer is as high as more than 95 percent; the partial middle product is methylbenzene.

Description

technical field [0001] The invention relates to a fluidized bed catalyst for preparing p-xylene with high selectivity in the alkylation of benzene and methanol and a preparation method thereof, belonging to the technical field of catalysts. Background technique [0002] Paraxylene is an extremely important bulk chemical raw material, mainly used in the production of terephthalic acid (PTA) and dimethyl terephthalate (DMT). Due to the rapid development of my country's polyester industry, the consumption of PTA and DMT has increased, resulting in a rapid increase in the consumption of p-xylene. In contrast, the expansion speed of aromatics is lower than the demand growth, and the self-sufficiency rate of p-xylene is only about 60%. It is estimated that the demand for p-xylene will be as high as 20.7 million tons in 2015. [0003] In industry, p-xylene is generally produced by the separation of aromatics from petroleum cracking products, disproportionation of toluene or transa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J29/40C07C2/86C07C15/08
CPCY02P20/52
Inventor 张世刚辛玉兵汪彩彩张军民刘建斌陈亚妮张变玲张小虎
Owner 陕西煤化工技术工程中心有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap