BOPP (biaxially-oriented polypropylene) insulating release film

A technology of release film and film layer, applied in the field of release film, can solve the problems of affecting the range of use, poor weather resistance, aging, etc., and achieve the effect of improving the range of use, good compatibility, and good insulation

Inactive Publication Date: 2016-03-30
TAICANG CUSTOM NEW MATERIALS CO LTD
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although BOPP has many advantages, due to the properties of its material PP itself, the weather resistance of BOPP film is poor, and it is more likely to age under the action of external environme

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A kind of BOPP insulating release film, comprises film layer, and described film layer comprises following component by weight ratio:

[0051] BOPP: 120 copies;

[0052] Boron nitride: 6 parts;

[0053] Epoxy resin 6101: 5 parts;

[0054] Phenolic resin 2124: 5 parts;

[0055] Melamine: 1 part;

[0056] Furfuryl alcohol furfural resin: 5 parts;

[0057] Polyacrylamide: 1.2 parts;

[0058] Polyamide 66: 4 parts;

[0059] Nano alumina: 1.2 parts;

[0060] Mica powder: 2 parts;

[0061] Talcum powder: 1.2 parts;

[0062] Polyvinyl alcohol tert-butyraldehyde: 2 parts;

[0063] FEP: 5 copies;

[0064] PBT: 8 parts;

[0065] PET: 10 parts;

[0066] Polyethylene glycol monomethyl ether: 15 parts;

[0067] PTFE: 8 parts;

[0068] Polymethyl methacrylate: 8 parts;

[0069] Polyphenylene sulfide: 4 parts;

[0070] Organic montmorillonite: 4 parts;

[0071] Paraffin: 6 parts;

[0072] Polyether ether ketone fiber: 2 parts;

[0073] Nano silicon dioxide: 3 parts;...

Embodiment 2

[0082] A kind of BOPP insulating release film, comprises film layer, and described film layer comprises following component by weight ratio:

[0083] BOPP: 130 copies;

[0084] Boron nitride: 7 parts;

[0085] Epoxy resin 6101: 6 parts;

[0086] Phenolic resin 2124: 6 parts;

[0087] Melamine: 1.5 parts;

[0088] Furfuryl alcohol furfural resin: 6 parts;

[0089] Polyacrylamide: 1.4 parts;

[0090] Polyamide 66: 5 parts;

[0091] Nano alumina: 1.4 parts;

[0092] Mica powder: 3 parts;

[0093] Talcum powder: 1.3 parts;

[0094] Polyvinyl alcohol tert-butyraldehyde: 3 parts;

[0095] FEP: 6 copies;

[0096] PBT: 9 parts;

[0097] PET: 11 parts;

[0098] Polyethylene glycol monomethyl ether: 18 parts;

[0099] PTFE: 9 parts;

[0100] Polymethyl methacrylate: 9 parts;

[0101] Polyphenylene sulfide: 5 parts;

[0102] Organic montmorillonite: 5 parts;

[0103] Paraffin: 7 parts;

[0104] Polyether ether ketone fiber: 3 parts;

[0105] Nano silicon dioxide: 4 parts...

Embodiment 3

[0114] A kind of BOPP insulating release film, comprises film layer, and described film layer comprises following component by weight ratio:

[0115] BOPP: 140 copies;

[0116] Boron nitride: 8 parts;

[0117] Epoxy resin 6101: 7 parts;

[0118] Phenolic resin 2124: 7 parts;

[0119] Melamine: 2 parts;

[0120] Furfuryl alcohol furfural resin: 7 parts;

[0121] Polyacrylamide: 1.6 parts;

[0122] Polyamide 66: 6 parts;

[0123] Nano alumina: 1.6 parts;

[0124] Mica powder: 4 parts;

[0125] Talcum powder: 1.4 parts;

[0126] Polyvinyl alcohol tert-butyraldehyde: 4 parts;

[0127] FEP: 7 copies;

[0128] PBT: 10 copies;

[0129] PET: 12 copies;

[0130] Polyethylene glycol monomethyl ether: 20 parts;

[0131] PTFE: 10 parts;

[0132] Polymethyl methacrylate: 10 parts;

[0133] Polyphenylene sulfide: 6 parts;

[0134] Organic montmorillonite: 6 parts;

[0135] Paraffin: 8 parts;

[0136] PEEK fiber: 4 parts;

[0137] Nano silicon dioxide: 5 parts;

[0138] A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a BOPP (biaxially-oriented polypropylene) insulating release film. The BOPP insulating release film comprises BOPP, boron nitride, epoxy resin 6101, phenol-formaldehyde resin 2124, melamine, furfural furfuryl alcohol resin, polyacrylamide, polyamide 66, nano-alumina, mica, talc, poly(vinyl butyral), FEP (fluorinated ethylene propylene), PBT (polybutylece terephthalate), PET (polyethylene terephthalate), methoxypolyethylene glycols, PTFE (polytetrafluoroethylene), polymethylmethacrylate, polyphenylene sulfide, organic montmorillonite, paraffin, polyetheretherketone fiber, nano-silica, an antioxidant 1010, a light stabilizer 622, nano-TiO2, PP-g-MAH (maleic anhydride grafted polypropylene), an antifoaming agent, a thickener and a coupling agent. The BOPP insulating release film has excellent insulation, water resistance, corrosion resistance, temperature resistance, weather resistance, adhesiveness as well as heat dissipation and energy storage functions.

Description

technical field [0001] The invention relates to a release film, in particular to a BOPP insulating release film. Background technique [0002] Release film, also known as peeling film, isolation film, separation film, barrier film, release film, film, plastic film, hole masking film, silicone oil film, silicone oil paper, anti-adhesive film, slip film, Tianna paper, release film Paper, silliconfilm, release film, release. Usually, in order to increase the release force of the plastic film, the plastic film will be treated with plasma, or coated with fluorine, or coated with silicon (silicone) release agent on the surface of the film material, such as PET, PE, OPP, etc. ;It can show extremely light and stable release force for various organic pressure-sensitive adhesives (such as hot-melt adhesives, acrylic adhesives and rubber-based pressure-sensitive adhesives). [0003] Because the release film has the advantages of isolation, filling, protection, and easy peeling, it is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L63/00C08L77/06C08L67/02C08L33/12C08L61/16C08K13/06C08K9/04C08K3/34C08K3/22C08K3/36C08K5/3492
CPCC08L23/12C08K2201/011C08L2201/08C08L2203/16C08L2205/02C08L2205/025C08L2205/035C08L2205/16
Inventor 李瑞清
Owner TAICANG CUSTOM NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap