Anti-ultraviolet and anti-aging powder coating added with nano titanium dioxide

A technology of nano-titanium dioxide and powder coatings, applied in powder coatings, anti-corrosion coatings, polyester coatings, etc., can solve problems such as easy delamination of metal coatings, poor impact resistance of ceramics, and poor mechanical and thermal properties of polymer coatings. Achieve the effects of improving weather resistance and hydrophobicity, improving hydrophobicity and oil repellency, and good anti-aging effect

Inactive Publication Date: 2016-04-06
TONGLING SIDE TECH
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the pump valve is a casting or forging, its surface is rough. At present, there are still some defects in the functional powder coating technology for valve surface treatment in the existing technology, which leads to defects such as shrinkage cavities, pinholes and severe orange peel in the coating, which in turn leads to The application of pump valves in special fields such as food, biology, pharmaceuticals, chemicals, aerospace and electronics is limited
Moreover, most of the pump valves will be used in high water content, high sand content, strong corrosion medium environment and other factors, which will aggravate the corrosion of the pump valve and make it easier to scale on the pump valve, resulting in short service life of the pump valve and short inspection cycle. , The problem of heavy workload brings inconvenience to the use. The general surface strengthening process mainly includes metal coating, ceramic coating and other coatings. Although the wear is slowed down to a certain extent and the corrosion resistance is improved, they all exist. Disadvantages: the metal coating is easy to delaminate and cause shedding; ceramics have poor impact resistance and are prone to cracking; some polymer coatings have poor mechanical and thermal properties, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] An ultraviolet aging resistant powder coating with nano titanium dioxide, made of the following parts by weight (kg) of raw materials: hydroxy polyester resin 52, fluorocarbon resin 7, triglycidyl isocyanurate 4, nano aluminum oxide 13 , Perfluorooctyl triethoxy silane 0.8, 75wt% ethanol solution 25, silane coupling agent kh5600.5, rutile nano titanium dioxide 15, aluminate coupling agent F10.2, matting micropowder wax 3. Amorphous silica 0.8, carboxymethyl cellulose 1.5, low-melting glass powder 4, deionized water in an appropriate amount.

[0013] Said powder coating with nano-titanium dioxide anti-ultraviolet aging is prepared by the following specific steps:

[0014] (1) Put nano-aluminum oxide into a 75wt% ethanol solution, stir and disperse evenly, then add perfluorooctyltriethoxysilane, heat and reflux for 2 hours, add silane coupling agent kh560 after cooling, Continue to stir and react for 2 hours, and finally distill under reduced pressure to remove the solvent in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-ultraviolet and anti-aging powder coating added with nano titanium dioxide. The powder coating is prepared from the following raw materials: 52-54 parts of hydroxy polyester resin, 7-8 parts of fluorocarbon resin, 4-5 parts of triglycidyl isocyanurate, 13-15 parts of nano-aluminum oxide, 0.8-0.9 part of perfluorooctyl triethoxysilane, 25-30 parts of an ethanol solution with the concentration of 75wt%, 0.5-0.6 part of a silane coupling agent kh560, 15-17 parts of rutile type nano titanium dioxide, 0.2-0.25 part of an aluminum coupling agent F1, 3-4 parts of extinction micronized wax, 0.8-1 part of amorphous silica, 1.5-2 parts of carboxymethyl cellulose, 4-5 parts of low-melting glass powder and a proper amount of deionized water. In the preparation of the powder coating, the aluminate coupling agent-modified rutile type nano titanium dioxide is additionally added, so that the weatherability and the hydrophobicity are improved; the powder coating is used for corrosion protection of an outside pump valve, and has an excellent anti-aging effect.

Description

Technical field [0001] The invention relates to the technical field of coatings, in particular to a powder coating with nanometer titanium dioxide added to resist ultraviolet aging. Background technique [0002] In recent years, the application of powder coatings has surpassed water-based coatings and high-solid coatings in the coatings industry, and has become one of the most widely used coatings in the industry. The powder coating process solves the problems of flammability, explosion and environmental pollution in the traditional paint coating process, and its coating has superior performance, the raw materials can be recycled and reused, and the coating process is simple. It can be widely used in the coating of pumps and valve shells. Because the pump valve is a casting or forging, its surface is rough. The existing functional powder coating technology for valve surface treatment still has certain defects, causing the coating to appear shrinkage, pinholes and serious orange ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D127/12C09D7/12C09D5/03C09D5/08C09C1/36C09C1/40C09C3/12C09C3/08
CPCC08K2201/011C08L2205/035C09D5/03C09D5/08C09D7/62C09D167/00C08L27/12C08K13/06C08K9/06C08K9/04C08K2003/2227C08K2003/2237C08K3/36
Inventor 孔华英
Owner TONGLING SIDE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products