Preparation and application of nitrogen-doped graphene-carbon nanohorn composite material

A nitrogen-doped graphene, carbon nanohorn technology, applied in hybrid capacitor electrodes, electrical components, battery electrodes, etc., can solve the problem of easy reagglomeration of graphene nanosheets, electrochemical performance, etc., achieve high yield, avoid two The effect of secondary agglomeration, high specific surface area

Inactive Publication Date: 2016-05-04
FUZHOU UNIV
View PDF4 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to provide the preparation and application of a nitrogen-doped graphene-carbon nanohorn composite material, which belongs to the technical field of preparation of graphene-based composite materials, overcomes and solves the problem of graphene nanohorn existing in the existing graphene preparation method. The composite material has the characteristics of good dispersion, low cost and excellent electrochemical performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation and application of nitrogen-doped graphene-carbon nanohorn composite material
  • Preparation and application of nitrogen-doped graphene-carbon nanohorn composite material
  • Preparation and application of nitrogen-doped graphene-carbon nanohorn composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Preparation of graphene oxide: Take 1.0g of expandable graphite and put it into a round bottom flask, then add 6.0g of potassium permanganate, then add 120mL of concentrated sulfuric acid and 14mL of concentrated phosphoric acid into the round bottom flask; Warm up the pot to 50°C, put the rotor into the flask, install the condenser on the flask, and put it into the oil bath for magnetic stirring for 24 hours; take it out from the oil bath; pour the reactants into a beaker with an appropriate amount of deionized water In an ice bath, add 30wt% hydrogen peroxide dropwise and stir until all the reactants turn golden yellow; after cooling to room temperature, wash with deionized water, filter and centrifuge repeatedly until the solution is neutral; pour the solution into an evaporating dish , put into a drying box for drying; after drying, grind to obtain graphene oxide, bottle it for later use;

[0041] (1) Dissolve 200 mg of graphene oxide powder in deionized water to pr...

Embodiment 2

[0045] The preparation of graphene oxide is the same as in Example 1.

[0046] (1) Dissolve 200mg of graphene oxide powder in deionized water to prepare a dispersion with a concentration of 5.58mg / mL, add 30mg of sodium lignosulfonate after ultrasonic dispersion for 30 minutes, and add 20g of melamine as a nitrogen dopant after ultrasonic dispersion for 30 minutes , and then add 5 mg of carbon nanohorns to obtain a mixture of graphene oxide-ligninsulfonic acid-melamine-carbon nanohorns; then add deionized water to 100mL, after ultrasonication for 1h, pour it into an evaporating dish, and dry it in an oven at 60°C. Obtain black solid powder, and then grind to obtain the precursor;

[0047] (2) Put the dried black precursor solid powder in (1) in a crucible, and carry out pyrolysis at 800°C under the protection of 100mL / min inert gas; heat up to 800°C at a heating rate of 3°C / min ℃, keep warm for 120min, and then cool with the furnace to obtain nitrogen-doped graphene-carbon na...

Embodiment 3

[0050] The preparation of graphene oxide is the same as in Example 1.

[0051] (1) Dissolve 200 mg of graphene oxide powder in deionized water to prepare a dispersion with a concentration of 5.58 mg / mL, add 20 mg of cellulose sodium after ultrasonic dispersion for 30 min, and add 20 g of urea as a nitrogen dopant after ultrasonic dispersion for 30 min. Add 5mg of carbon nanohorns to obtain a mixture of graphene oxide-cellulose sodium-urea-carbon nanohorns; then add deionized water to 100mL, after ultrasonication for 1h, pour it into an evaporating dish, and dry it in an oven at 60°C to obtain a black solid powder, and then grind to obtain the precursor;

[0052] (2) Put the dried black precursor solid powder in (1) in a crucible, and carry out pyrolysis at 700°C under the protection of 200mL / min inert gas; heat up to 700°C at a heating rate of 3°C / min ℃, keep warm for 120min, and then cool with the furnace to obtain nitrogen-doped graphene-carbon nanohorn composite material, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method and an application of a nitrogen-doped graphene-carbon nanohorn composite material, and belongs to the field of functional carbon materials. The preparation method of the nitrogen-doped graphene-carbon nanohorn composite material comprises the steps of ultrasonically dispersing graphene oxide to form a uniform solution in the presence of a biomass raw material, adding a nitrogen source substance and a carbon nanohorn, performing ultrasonic and uniform dispersion again to obtain a graphene oxide-biomass-nitrogen source substance-carbon nanohorn mixture solution, and drying the mixture to a constant weight, thereby obtaining a nitrogen precursor mixture; and performing normal-pressure high-temperature pyrolysis on the nitrogen precursor mixture to obtain the nitrogen-doped graphene-carbon nanohorn composite material. The prepared nitrogen-doped graphene-carbon nanohorn composite material can be used for electrode materials of lithium ion batteries and supercapacitors. The preparation method is simple; and the obtained composite material is loose in structure and good in nitrogen-doped graphene nanosheet dispersity. The method provides a new way for preparing a nitrogen-doped graphene based composite material.

Description

technical field [0001] The invention belongs to the technical field of preparation of graphene-based composite materials, and more specifically relates to the preparation and application of a nitrogen-doped graphene-carbon nanohorn composite material. Background technique [0002] Graphene has excellent electrical conductivity and high specific surface area, and is considered to be an ideal choice as an electrode material for superpolar electrical appliances. However, the existence of van der Waals force between sheets makes graphene sheets easy to reunite, which reduces the effective use of its specific surface area, and its surface lacks channels for electrolyte ions to move, which greatly limits its performance. Therefore, how to effectively solve the dispersion and surface modification of graphene has become a key scientific issue. In order to expand the application of graphene, it is often modified by doping or compounded with other materials to adjust the physical and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/583H01M4/62H01M4/36H01G11/32H01G11/36C01B31/02C01B31/04
CPCH01G11/32H01G11/36H01M4/362H01M4/583H01M4/625Y02E60/10Y02E60/13
Inventor 吕秋丰王文栋林晓强
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com