Fluorine-modified water-borne alkyd resin and preparation method thereof

A water-based alkyd resin and fluorine-modified technology, applied in the field of fluorine-modified water-based alkyd resin and the preparation of modified water-based alkyd resin, can solve the problem that the surface of the substrate coating is easily polluted and the coating surface is unevenly dispersed , large surface tension and other problems, to achieve the effect of no environmental pollution, low dielectric constant and excellent performance

Inactive Publication Date: 2016-06-15
UNION FOSHAN CHEM +1
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the surface treatment agent that acts on the surface of plastic, wood, metal, etc. for antifouling and waterproof treatment, due to the uneven dispersion of the coating surface after application and the excess

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A fluorine-modified water-based alkyd resin, the preparation process of which is as follows:

[0023] a. In a four-port reactor equipped with a thermometer, condenser, water separator, and agitator, add 10 parts of refined linseed oil, 3 parts of glycerin, 2 parts of petroleum anhydride, 3 parts of phthalic anhydride, and three 2 parts of methylol propane, 3 parts of xylene, 2.5 parts of benzoic acid, 8 parts of epoxy resin, heating up to a certain temperature to dissolve the material, continuing to stir and heat up until reflux occurs, and continuing the heat preservation reaction for a period of time;

[0024] b. Sampling and testing the acid value of the reactant until it is close to the theoretical value; cool down, add 10 parts of perfluorohexyl ethyl acrylate, 5 parts of hydroxypropyl acrylate, and 4 parts of methacrylic acid, and carry out polymerization reaction at a certain temperature ;

[0025] c. After the polymerization reaction is completed, turn on the v...

Embodiment 2

[0027] A fluorine-modified water-based alkyd resin, the preparation process of which is as follows:

[0028] a. In a four-port reactor equipped with a thermometer, condenser, water separator, and agitator, 12 parts of refined linseed oil, 2.5 parts of glycerin, 2.5 parts of petroleum anhydride, 3.5 parts of phthalic anhydride, three 1.5 parts of methylolpropane, 3.5 parts of xylene, 3 parts of benzoic acid, and 6 parts of epoxy resin, heated to a certain temperature to dissolve the materials, continued stirring and heating until reflux occurred, and continued to keep warm for a period of time;

[0029] b. Take a sample to detect the acid value of the reactant until it is close to the theoretical value; cool down, add 7 parts of hexafluorobutyl methacrylate, 2.5 parts of hydroxypropyl acrylate, 4.5 parts of methacrylic acid, and 2 parts of butyl methacrylate , to control the polymerization reaction at a certain temperature;

[0030] c. After the polymerization reaction is comp...

Embodiment 3

[0032] A fluorine-modified water-based alkyd resin, the preparation process of which is as follows:

[0033] a. In a four-port reactor equipped with a thermometer, condenser, water separator, and agitator, 10 parts of refined castor oil, 2.0 parts of glycerin, 2.5 parts of petroleum anhydride, 2.5 parts of phthalic anhydride, benzene 3.2 parts of formic acid, 2 parts of trimethylolpropane, 2.8 parts of benzoic acid, 2.0 parts of xylene, 6.5 parts of epoxy resin, heat up to a certain temperature to dissolve the materials, continue to stir and heat up until reflux occurs, and continue to keep warm for a period of time time;

[0034] b. Take a sample to detect the acid value of the reactant until it is close to the theoretical value; cool down, add 6.6 parts of octafluoropentyl acrylate, 1.4 parts of isobutyl methacrylate, 3.2 parts of methacrylic acid, and 2.6 parts of tert-butyl acrylate, Carry out the polymerization reaction under the control certain temperature;

[0035] c....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a fluorine-modified water-based alkyd resin and a preparation method thereof. Its components are composed of vegetable oil fatty acids, organic acid anhydrides, polyols, epoxy resins, fluorine monomers, acrylic monomers and deionized water; The fluorine-modified water-based alkyd resin prepared by the invention can be formulated into one-component water-based coatings, two-component water-based coatings, and normal-temperature curing coatings. The fluorine-modified water-based alkyd resin prepared by the present invention has good adhesion, stain resistance, water resistance, alkali resistance, durability, hydrophobicity, low dielectric constant and other properties, and is widely used in marine fields, wood Coatings, anti-fouling and water-repellent coatings, which can also be used in radome materials, have enormous application potential.

Description

technical field [0001] The invention relates to a preparation method of a modified water-based alkyd resin, in particular to a fluorine-modified water-based alkyd resin with uniform structure, low cost, extremely low surface tension, and good hydrophobic and antifouling functions, belonging to synthetic resins Technical field: The present invention combines the characteristics of easy-to-obtain alkyd resin raw materials, low cost and small fluorine atomic radius, and the prepared fluorine-modified water-based alkyd resin can be used for substrates such as wood, metal, and plastic. Background technique [0002] At present, the surface treatment agent that acts on the surface of plastic, wood, metal, etc. for antifouling and waterproof treatment, due to the uneven dispersion of the coating surface after application and the excessive surface tension, this makes the surface of the substrate coating extremely easy to be polluted and difficult to Clean, and thus low surface energy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F283/01C08F220/24C08F220/22C09D151/08
CPCC08F283/01C08F2500/26C09D151/08C08F220/24C08F220/22
Inventor 张武许钧强康伦国姚东生
Owner UNION FOSHAN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap